Response viscoelastic

In principle, the relaxation spectrum H(r) describes the distribution of relaxation times which characterizes a sample. If such a distribution function can be determined from one type of deformation experiment, it can be used to evaluate the modulus or compliance in experiments involving other modes of deformation. In this sense it embodies the key features of the viscoelastic response of a spectrum. Methods for finding a function H(r) which is compatible with experimental results are discussed in Ferry s Viscoelastic Properties of Polymers. In Sec. 3.12 we shall see how a molecular model for viscoelasticity can be used as a source of information concerning the relaxation spectrum. 

The relaxation and creep experiments that were described in the preceding sections are known as transient experiments. They begin, run their course, and end. A different experimental approach, called a dynamic experiment, involves stresses and strains that vary periodically. Our concern will be with sinusoidal oscillations of frequency v in cycles per second (Hz) or co in radians per second. Remember that there are 2ir radians in a full cycle, so co = 2nv. The reciprocal of CO gives the period of the oscillation and defines the time scale of the experiment. In connection with the relaxation and creep experiments, we observed that the maximum viscoelastic effect was observed when the time scale of the experiment is close to r. At a fixed temperature and for a specific sample, r or the spectrum of r values is fixed. If it does not correspond to the time scale of a transient experiment, we will lose a considerable amount of information about the viscoelastic response of the system. In a dynamic experiment it may... 

The response of this model to creep, relaxation and recovery situations is the sum of the effects described for the previous two models and is illustrated in Fig. 2.39. It can be seen that although the exponential responses predicted in these models are not a true representation of the complex viscoelastic response of polymeric materials, the overall picture is, for many purposes, an acceptable approximation to the actual behaviour. As more and more elements are added to the model then the simulation becomes better but the mathematics become complex. 

The typical viscoelastic response, as shown in Fig. 2.18, is the propagation of a shock due to the compression, followed by a relaxation to an equilibrium state. The relaxation response is a significant part of the total response. Relaxation times are typically in the 0.1 /is regime. At pressures over about 2 GPa, PMMA shows a change in relaxation time which may be indicative of mechanical failure. Anderson has recently extended this work to other polymers and found similar strong viscoelastic behavior [92A01]. 

The ramp of pressure to about 3 GPa observed in shock-loaded fused quartz has been used very effectively in acceleration-pulse loading studies of viscoelastic responses of polymers by Schuler and co-workers. The loading rates obtained at various thicknesses of fused quartz have been accurately characterized and data are summarized in Fig. 3.6. At higher peak pressures there are no precise standard materials to produce ramp loadings, but materials such as the ceramic pyroceram have been effectively employed. (See the description of the piezoelectric polymer in Chap. 5.)... 

Adsorption of rubber over the nanosilica particles alters the viscoelastic responses. Analysis of dynamic mechanical properties therefore provides a direct clue of the mbber-silica interaction. Figure 3.22 shows the variation in storage modulus (log scale) and tan 8 against temperature for ACM-silica, ENR-silica, and in situ acrylic copolymer and terpolymer-silica hybrid nanocomposites. 

Better cross-linking with the latter also improves post Tg viscoelastic responses of the rubber vulcanizates. Similar effect has also been observed with polychloroprene as investigated by Sahoo and Bhowmick [41]. Figure 4.8 represents the comparative tensile stress-strain behavior of polychloroprene rubber (CR) vulcanizates, highlighting superiority of the nanosized ZnO over conventional rubber grade ZnO [41]. 

Sui, C., McKenna, G.B., and Puskas, J.E. Nonlinear viscoelastic response of dendritic (arborescent) polyisobutylenes in single- and reversing double-step shearing flows, J. Rheol, 51, 1143, 2007. 

At sufficiently low strain, most polymer materials exhibit a linear viscoelastic response and, once the appropriate strain amplitude has been determined through a preliminary strain sweep test, valid frequency sweep tests can be performed. Filled mbber compounds however hardly exhibit a linear viscoelastic response when submitted to harmonic strains and the current practice consists in testing such materials at the lowest permitted strain for satisfactory reproducibility an approach that obviously provides apparent material properties, at best. From a fundamental point of view, for instance in terms of material sciences, such measurements have a limited meaning because theoretical relationships that relate material structure to properties have so far been established only in the linear viscoelastic domain. Nevertheless, experience proves that apparent test results can be well reproducible and related to a number of other viscoelastic effects, including certain processing phenomena. 

Here m is the usual small-strain tensile stress-relaxation modulus as described and observed in linear viscoelastic response [i.e., the same E(l) as that discussed up to this point in the chapter). The nonlinearity function describes the shape of the isochronal stress-strain curve. It is a simple function of A, which, however, depends on the type of deformation. Thus for uniaxial extension,... 

---