Viscoelastic principles

Important viscoelastic principles include the time-temperature superposition principle and its resultant WLF equation. These can be applied to understand the relationship between literature values of the glass transition temperature and actual needs. Thus, by using the growing amount of science now available in the field of damping, one can select that polymeric material which will damp most effectively. 

Details of both continuous shear and dynamic oscillatory testing of pharmaceutical semisolids, including gels, have been addressed in reviews, where the fundamental viscoelastic principles are further developed along with a discussion of data analyses and interpretations. 

Since the Gross frequency relaxation spectrum can be computed from r , i.e., from the loss modulus, G = T co, the agreement between the computed and measured G values provides good means of verifying both the computational and experimental procedures. It has been found that Eqs 7.83 and 7.84 are useful to evaluate the rheological performance of systems that obey the linear viscoelastic principles. 

In principle, the relaxation spectrum H(r) describes the distribution of relaxation times which characterizes a sample. If such a distribution function can be determined from one type of deformation experiment, it can be used to evaluate the modulus or compliance in experiments involving other modes of deformation. In this sense it embodies the key features of the viscoelastic response of a spectrum. Methods for finding a function H(r) which is compatible with experimental results are discussed in Ferry s Viscoelastic Properties of Polymers. In Sec. 3.12 we shall see how a molecular model for viscoelasticity can be used as a source of information concerning the relaxation spectrum. 

Micro-mechanical processes that control the adhesion and fracture of elastomeric polymers occur at two different size scales. On the size scale of the chain the failure is by breakage of Van der Waals attraction, chain pull-out or by chain scission. The viscoelastic deformation in which most of the energy is dissipated occurs at a larger size scale but is controlled by the processes that occur on the scale of a chain. The situation is, in principle, very similar to that of glassy polymers except that crack growth rate and temperature dependence of the micromechanical processes are very important. 

The simplest theoretical model proposed to predict the strain response to a complex stress history is the Boltzmann Superposition Principle. Basically this principle proposes that for a linear viscoelastic material, the strain response to a complex loading history is simply the algebraic sum of the strains due to each step in load. Implied in this principle is the idea that the behaviour of a plastic is a function of its entire loading history. There are two situations to consider. 

It is apparent therefore that the Superposition Principle is a convenient method of analysing complex stress systems. However, it should not be forgotten that the principle is based on the assumption of linear viscoelasticity which is quite inapplicable at the higher stress levels and the accuracy of the predictions will reflect the accuracy with which the equation for modulus (equation (2.33)) fits the experimental creep data for the material. In Examples (2.13) and (2.14) a simple equation for modulus was selected in order to illustrate the method of solution. More accurate predictions could have been made if the modulus equation for the combined Maxwell/Kelvin model or the Standard Linear Solid had been used. 

This second group of tests is designed to measure the mechanical response of a substance to applied vibrational loads or strains. Both temperature and frequency can be varied, and thus contribute to the information that these tests can provide. There are a number of such tests, of which the major ones are probably the torsion pendulum and dynamic mechanical thermal analysis (DMTA). The underlying principles of these dynamic tests have been covered earlier. Such tests are used as relatively rapid methods of characterisation and evaluation of viscoelastic polymers, including the measurement of T, the study of the curing characteristics of thermosets, and the study of polymer blends and their compatibility. They can be used in essentially non-destructive modes and, unlike the majority of measurements made in non-dynamic tests, they yield data on continuous properties of polymeric materials, rather than discontinuous ones, as are any of the types of strength which are measured routinely. 

Since we are interested in this chapter in analyzing the T- and P-dependences of polymer viscoelasticity, our emphasis is on dielectric relaxation results. We focus on the means to extrapolate data measured at low strain rates and ambient pressures to higher rates and pressures. The usual practice is to invoke the time-temperature superposition principle with a similar approach for extrapolation to elevated pressures [22]. The limitations of conventional t-T superpositioning will be discussed. A newly developed thermodynamic scaling procedure, based on consideration of the intermolecular repulsive potential, is presented. Applications and limitations of this scaling procedure are described. 

There are two superposition principles that are important in the theory of Viscoelasticity. The first of these is the Boltzmann superposition principle, which describes the response of a material to different loading histories (22). The second is the time-temperature superposition principle or WLF (Williams, Landel, and Ferry) equation, which describes the effect of temperature on the time scale of the response. 

There are many types of deformation and forces that can be applied to material. One of the foundations of viscoelastic theory is the Boltzmann Superposition Principle. This principle is based on the assumption that the effects of a series of applied stresses acting on a sample results in a strain which is related to the sum of the stresses. The same argument applies to the application of a strain. For example we could apply an instantaneous stress to a body and maintain that stress constant. For a viscoelastic material the strain will increase with time. The ratio of the strain to the stress defines the compliance of the body ... 

An important and sometimes overlooked feature of all linear viscoelastic liquids that follow a Maxwell response is that they exhibit anti-thixo-tropic behaviour. That is if a constant shear rate is applied to a material that behaves as a Maxwell model the viscosity increases with time up to a constant value. We have seen in the previous examples that as the shear rate is applied the stress progressively increases to a maximum value. The approach we should adopt is to use the Boltzmann Superposition Principle. Initially we apply a continuous shear rate until a steady state... 

Because of equipment limitations in measuring stress and strain in polymers, the time-temperature superposition principle is used to develop the viscoelastic response curve for real polymers. For example, the time-dependent stress relaxation modulus as a function of time and temperature for a PMMA resin is shown in... 

Fig. 3.14. The data is for a very broad range of times and temperatures. The superposition principle is based on the observation that time (rate of change of strain, or strain rate) is inversely proportional to the temperature effect in most polymers. That is, an equivalent viscoelastic response occurs at a high temperature and normal measurement times and at a lower temperature and longer times. The individual responses can be shifted using the WLF equation to produce a modulus-time master curve at a specified temperature, as shown in Fig. 3.15. The WLF equation is as shown by Eq. 3.31 for shifting the viscosity. The method works for semicrystalline polymers. It works for amorphous polymers at temperatures (T) greater than Tg + 100 °C. Shifting the stress relaxation modulus using the shift factor a, works in a similar manner.

Dynamic mechanical experiments yield both the elastic modulus of the material and its mechanical damping, or energy dissipation, characteristics. These properties can be determined as a function of frequency (time) and temperature. Application of the time-temperature equivalence principle [1-3] yields master curves like those in Fig. 23.2. The five regions described in the curve are typical of polymer viscoelastic behavior. 

---