Thin-film composite mixed-matrix membranes

3 Thin-Film Composite Mixed-Matrix Membranes 

Thin-film composite mixed-matrix membranes can be made by a coating method or by a dual-layer co-extrusion technology, as discussed in Section 11.5.2.2. 

Jia and coworkers prepared thin-film composite zeolite-filled silicone rubber membranes by a dip-coating method [82]. The membranes have a thin silicalite-1/ silicone rubber mixed-matrix selective layer on top of a porous polyetherimide support. 

Only a slight improvement in separation was obtained with the membrane having a mixed-matrix layer thickness of more than 18 mm. 

Geong and coworkers reported a new concept for the formation of zeolite/ polymer mixed-matrix reverse osmosis (RO) membranes by interfacial polymerization of mixed-matrix thin films in situ on porous polysulfone (PSF) supports [83]. The mixed-matrix films comprise NaA zeoHte nanoparticles dispersed within 50-200 nm polyamide films. It was found that the surface of the mixed-matrix films was smoother, more hydrophilic and more negatively charged than the surface of the neat polyamide RO membranes. These NaA/polyamide mixed-matrix membranes were tested for a water desalination application. It was demonstrated that the pure water permeability of the mixed-matrix membranes at the highest nanoparticle loadings was nearly doubled over that of the polyamide membranes with equivalent solute rejections. The authors also proved that the micropores of the NaA zeolites played an active role in water permeation and solute rejection. 

---

The geometries for asymmetric mixed-matrix membranes include flat sheets, hollow fibers and thin-fihn composites. The flat sheet asymmetric mixed-matrix membranes are formed into spirally wound modules and the hollow fiber asymmetric mixed-matrix membranes are formed into hollow fiber modules. The thin-film composite mixed-matrix membranes can be fabricated into either spirally wound or hollow fiber modules. The thin-film composite geometry of mixed-matrix membranes enables selection of different membrane materials for the support layer and low-cost production of asymmetric mixed-matrix membranes utilizing a relatively high-cost zeolite/polymer separating layer on the support layer. 

The new concept of using mixed-matrix membranes with commercially attractive thin-film composite geometry for desalination of water has been demonstrated by Jeong and coworkers [83]. 

Cross-section structure. An anisotropic membrane (also called asymmetric ) has a thin porous or nonporous selective barrier, supported mechanically by a much thicker porous substructure. This type of morphology reduces the effective thickness of the selective barrier, and the permeate flux can be enhanced without changes in selectivity. Isotropic ( symmetric ) membrane cross-sections can be found for self-supported nonporous membranes (mainly ion-exchange) and macroporous microfiltration (MF) membranes (also often used in membrane contactors [1]). The only example for an established isotropic porous membrane for molecular separations is the case of track-etched polymer films with pore diameters down to about 10 run. All the above-mentioned membranes can in principle be made from one material. In contrast to such an integrally anisotropic membrane (homogeneous with respect to composition), a thin-film composite (TFC) membrane consists of different materials for the thin selective barrier layer and the support structure. In composite membranes in general, a combination of two (or more) materials with different characteristics is used with the aim to achieve synergetic properties. Other examples besides thin-film are pore-filled or pore surface-coated composite membranes or mixed-matrix membranes [3]. 

S., Khadivi, M. A., and Rostami, E. 2013. Novel thin film composite membrane fabricated by mixed matrix nanoclay/ chitosan on PVDF microfiltration support Preparation, characterization and performance in dye removal. J. Membr. Sci. 436 97-108. 

---