Steels surface treatment

Almeida, E., Diamantino, T.C, Figueiredo M.O., Sa C. (1998). Oxidizing alternative species to chromium VI in zinc - galvanized steel surface treatment. Part I-A morphological and chemical study. Surface and Coating Technology, Vol. 106, pp. 8-17. ISSN 0257-8972... 

Le Bozec, M L Her, C. Compere, A. Laouenan, D. Costa and P. Marcus, Influence of stainless steel surface treatment on the oxygen reduction reaction in seawater, Corros. Sci. 43 765-786 (2001). 

The AET was used at standard tests of numerous structural materials, above all steels and cast iron, prepared are ceramic samples. Part of tested samples had qjecial sur ce layer treatments by laser, plasma nitridation and similar. Effect of special surface treatment the authors published already earlier [5,6]. In this contribution are summed up typical courses of basic dependencies, measured by the AET at contact loading. 

Sa.lts Salting out metal chlorides from aqueous solutions by the common ion effect upon addition of HCl is utilized in many practical apphcations. Typical data for ferrous chloride [13478-10-9] FeCl2, potassium chloride [7447-40-7] KCl, and NaCl are shown in Table 9. The properties of the FeCl2-HCL-H2 0 system are important to the steel-pickling industry (see Metal SURFACE TREATMENTS Steel). Other metal chlorides that are salted out by the addition of hydrogen chloride to aqueous solutions include those of magnesium, strontium, and barium. 

Alkaline permanganate pretreatment of steel for the removal of heat scale and smut prior to acid pickling results in faster descaling and reduced metal attack (see Metal surface treatments Metal treatments). Stainless steel alloys can also be cleaned by alkaline permanganate followed by pickling in nonoxidi2ing acids (260). 

P/M steels can be heat treated in the same manner as cast or wrought steels. They may be austenitized, quenched, and tempered. Surface hardening includes pack or gas carburization or nitriding, ie, heating in a nitrogen-containing atmosphere. Because of the greater amount of exposed surface area in the form of porosity, a protective atmosphere is needed (see Metal surface treatments). 

Nickel Phosphate. Tri nickel orthophosphate [14396-43-17, Ni2(P0 2 7H20, exists as apple-green plates which decompose upon heating. It is prepared by the reaction of nickel carbonate and hot dilute phosphoric acid. Nickel phosphate is an additive to control the crystal size of ziac phosphate ia coaversioa coatiags which are appHed to steel prior to its being paiated (see Metal surface treatments). 

Metal Treatment. After rolling, the oxide scale on sheet steel is removed by acid treatment (pickling) (see Metal surface treatments). Phosphoric acid, a good pickling agent, leaves the steel coated with a thin film of iron phosphates. This process improves mst resistance but presents a problem if the steel is to be electroplated. 

An iatermediate treatment that adds both carbon and nitrogen to steel surfaces can be obtained by exposiag the parts to a bath of molten cyanide at just above the critical temperature of the core for about one hour followed by direct quenching. The hardened area is about 0.25-mm deep. 

Although there is considerable evidence that chemical surface treatments improve the substrate bondability of stainless steels, there is no general agreement on which is the best. One etchant commonly used with stainless steels is an HNO3-HF mixture [128-131] others are chromic acid and ferric chloride/hydrochloric... 

Fig. 30. Phosphoric acid etched A.314 steel surface showing extensive etching along martensite boundaries. This alloy contains the same constituents as A606, but has been given a different heat treatment 54. ...

Filiform corrosion is characterised by the formation of a network of threadlike filaments of corrosion products on the surface of a metal coated with a transparent lacquer or a paint him, as a result of exposure to a humid atmosphere. This phenomenon first attracted attention because of its formation on lacquered steel, and for this reason it is sometimes referred to as underfilm corrosion, but although it is most readily observed under a transparent lacquer it can also occur under an opaque paint film or on a bare metal surface. Filiform corrosion has been observed on steel, zinc, magnesium and aluminium coated with lacquers and paints, and with aluminium foil coated with paper. Surface treatment of the metal by phosphating or chromating lessens the tendency for filiform corrosion to occur, but it is not completely... 

---