Rotary kiln calciner

Refined calcined alumina is commonly used in combination with high purity limestone [1317-65-3] to produce high purity calcium aluminate cement (CAC). The manufacture, properties, and appHcations of CAC from bauxite limestone, as weU as high purity CAC, has been described (104). High purity CAC sinters readily in gas-fired rotary kiln calcinations at 1600 —1700 K. CAC reactions are considered practically complete when content of free CaO is less than 0.15% andloss on ignition is less than 0.5% at 1373 K. 

AVM is a continuous rotary-kiln calciner/induction-heated melter process [B6, C3]. The... 

Rotary-kiln/continuous melter (AVM) (France-Cogema, Marcoule) Borosilicate glass Monolithic cylinder Furnace-heated metallic or ceramic crucible Rotary-kiln calcine Thermal... 

Green coke has a carbon content of around 92%. To produce carbon products, the green coke, which contains up to 15% volatiles, is calcined, reducing the volatile content to around 0.1%. Calcination takes place in rotary hearth or in rotary kiln calciners at temperatures from 1250 to 1450 °C the volatile components are used as fuel. 

The following elements are essential in any computer model of rotary kiln calcination ... 

Calcination. Calcination involves a low (<1000° C) temperature soHd-state chemical reaction of the raw materials to form the desired final composition and stmcture such as perovskite for BaTiO and PZT. It can be carried out by placing the mixed powders in cmcibles in a batch or continuous kiln. A rotary kiln also can be used for this purpose to process continuously. A sufficiendy uniform temperature has to be provided for the mixed oxides, because the thermal conductivity of powdered materials is always low. 

Fig. 5. Schematic of the Kennedy van Saun (KVS) patented low pressure drop (LPD) preheater/rotary kiln lime calcining system available in sites...

Rotary kilns and, to a lesser extent, Fluo-SoHds kilns are used to calcine a wet precipitated calcium carbonate filter cake in the kraft or sulfate paper-pulp process (15). Lime is regenerated for use as a causticization reagent in recovering caustic soda for pulp digestion. Losses in lime recovery are replaced by purchased lime (see Paper Pulp). 

Portland Cement Manufacture. The second greatest use of limestone is as raw material in the manufacture of Pordand cement (10). The average limestone factor per ton of Pordand cement is 1.0—1.1 t of pulverized limestone. The limestone, calcined to lime in the cement rotary kiln, combines with siUca and alumina to form tricalcium siUcate and tricalcium aluminate and other lesser cementing compounds (see Cement). Most cement companies operate captive limestone quarries. 

VoIa.tiIes. Manganese may contain some chemically bonded water or carbon dioxide both of which can be removed by calcining or sintering. The Mexican Molango ore (Table 4) is an example of a low grade ore that is upgraded by calcination in a rotary kiln. 

Calcination of the washed cake of the hydrated gel of Ti02 is carried out in rotary kilns similar to those used for producing cement (qv). The kilns are directiy heated with gas or oil. An excess of air in the kilns is required to prevent the possible reduction of Ti02 to its lower oxides. The presence of such oxides, even in small quantities, gives the final product a bluish gray shade. 

Strontium Hexaferrite. Strontium hexaferrite [12023-91 -5] SrO-6 Fe2 03, is made by combining powdered ferric oxide, Fe203, and strontium carbonate, SrCO, and calcining the mixture at ca 1000°C in a rotary kiln (9). The material is cmshed, mixed with a binder, and pressed or extmded into... 

Attrition Loss. The tendency of a support body to be reduced to powder is termed susceptibiHty to attrition, and the measurement of such susceptibiHty is termed attrition loss. Attrition can occur when support bodies mb against one another and abrade the surface, such as during calcination in a rotary kiln or sizing on moving screens. 

Calcined diatomite is produced from natural diatomite, which is then subjected to high temperature calcination in a rotary kiln at about 980°C. The calcined material is then again milled and classified to remove coarse agglomerates as well as extreme fines. 

Black a.sh. Barium sulfide (BaS) is produced by calcining a mixture of barite (BaSOj and carbon at a temperature of 1350 K in continuous rotary kilns. 

Spodumcnc. A mixture of quartz, feldspar, and spodumene is being calcined in rotary kilns at 1475 K to produce lithium aluminum silicate. 

Sulphate process. The ilmenite is reacted with sulphuric acid giving titanium sulphate and ferric oxide. After separation of ferric oxide, addition of alkali allows precipitation of hydrous titanium dioxide. The washed precipitate is calcined in a rotary kiln to render titanium dioxide. The nucleation and calcination conditions determine the crystalline structure of titanium dioxide (e.g. rutile or anatase). 

At the alumina plant, the bauxite ore is further crushed to the correct particle size for efficient extraction of the alumina through digestion by hot sodium hydroxide liquor. After removal of "red mud" (the insoluble part of the bauxite) and fine solids from the process liquor, aluminum trihydrate crystals are precipitated and calcined in rotary kilns or fluidized bed calciners to produce alumina (AljOj). Some alumina processes include a liquor purification step. 

---