Properties abrasion resistance

As the cis 1,4 content decreases, and 1,2 vinyl content increases, the low temperature properties, abrasion resistance and resilience become inferior. 

ASTM D1630 Standard test method for rubber property-abrasion resistance (footwear abrader)... 

D 1630 Test Method for Rubber Property - Abrasion Resistance (NBS Abrader)... 

Abrasion resistance D 1630 Rubber property—abrasion resistance (NBS Abrader) 9.01... 

Outstanding properties abrasion resistance, resistance to oils and greases, rebound resilience, load-bearing capacity, damping properties ... 

Outstanding properties abrasion resistance, chemical resistance, low friction coefficient, self-lubricating ... 

Urethane modified Chemical and corrosion resistance, weather resistance, good mechanical properties, abrasion resistance... 

Spandex fibers are available as fine as 1.1 tex (10 den), and the finest extmded latex thread available is about 16 tex (140 den). The availabihty of spandex fibers in such fine sizes and their unique properties compared to mbber, eg, dyeabiUty, high modulus, abrasion resistance, and whiteness, has allowed extensive penetration into hosiery and sportswear markets. 

In the sheeting market, the low density polyethylenes are less important than the high density resins. The high density resins have excellent chemical resistance, stress-crack resistance, durabiUty, and low temperature properties which make them ideal for pond liners, waste treatment faciUties, and landfills. In thicker section, HMW-HDPE sheet makes good containers, trays, tmck-bed liners, disposable items, and concrete molds. The good durabiUty, abrasion resistance, and light weight are critical elements for its selection. 

Cellular mbber has been used extensively as shoe soles, where its combination of cushioning abiUty and wear resistance, coupled with desirable economics, has led to very wide acceptance. In this case the cushioning properties are of minor importance compared with the abrasion resistance and cost. Other significant cushioning appHcations for cellular mbbers and latex foam mbbers are as carpet underlay and as cushion padding ia athletic equipment. 

Catalysis is usually accompHshed through the use of tertiary amines such as triethylenediamine. Other catalysts such as 2,4,6-/m(/V,/V-dimethylaminomethyl)phenol are used in the presence of high levels of cmde MDI to promote trimerization of the isocyanate and thus form isocyanurate ring stmctures. These groups are more thermally stable than the urethane stmcture and hence are desirable for improved flammabiUty resistance (236). Some urethane content is desirable for improved physical properties such as abrasion resistance. 

Some amorphous copoly(ether—sulfone) fkms have been prepared (117) with Ts around 130°C with no loss in weight up to 400°C in ak or N2. Other backbones iavestigated in this class of polymers are copoly(ether—amides) (118) and copoly(ether—ketones) (119). These polymers show good mechanical properties, flow characteristics, and abrasion resistance. 

The fabric may also be given one or more of a number of other finishing treatments, either ia tandem with web formation and bonding or off-line as a separate operation, as a means of enhancing fabric performance or aesthetic properties. Performance properties iaclude functional characteristics such as moisture transport, absorbency, or repeUency flame retardancy electrical conductivity or static propensity abrasion resistance and frictional behavior. Aesthetic properties iaclude appearance, surface texture, and smell. 

---