Potentiodynamic polarization method

Cyclic potentiodynamic polarization method. Electrochemical studies of pitting corrosion usually indicate that pitting occurs only within or above a critical potential or potential range. Therefore the susceptibility of passive metals to pitting corrosion is often investigated by electrochemical methods such as potentiodynamic or potentiostatic... 

Potentiostatic methods. Once the breakdown potential is determined by cyclic potentiodynamic polarization methods, polarizing individual samples at potentials above and below this value will indicate the validity of the chosen scan rate and give some kinetic data on the initiation and propagation of pits at different levels. Another possibility is to initiate pits above the pitting or breakdown potential and then shift to lower values above or below the protection potential. It is assumed that at imposed values below the protection potential, one should observe current decrease until complete repassivation. 

Cyclic Potentiodynamic Polarization Methods to Determine Em aaiAEp, ... 

Complications with Cyclic Potentiodynamic Polarization Methods... 

Although the cyclic method is a reasonable method for screening variations in alloy composition and environments, the cycHc potentiodynamic polarization method has been found to have a number of shortcomings [80-85. One major problem concerns the effect of the potential scan rate. The values of both and pro, are a strong function of... 

The basic electrochemical method for evaluating the susceptibihty of metals to pitting and crevice corrosion is covered by ASTM G 61 [30]. An anodic polarization curve is measured by a cyclic potentiodynamic polarization method using a specific scanning rate, from which breakdown potential and protection potential can be determined. See Fig. 11. 

Potentiodynamic polarization method was ap>plied to a wide range of potential changes to characterize the current-potential relationship j = f(E) in corrosion systems under investigation. The corrosion current density jcor and potential Ecor of tested metallic materials were further determined based on extrapolation of tangents to the curves of the cathodic and anodic polarization zones. 

All obtained results of imjjedance measurements confirm the significant impact of the material structure and the additions of nickel alloy on the resistance to corrosion and are consistent with the results obtained by potentiodynamic polarization method. 

Polarization probe.s. Polarization methods other than LPR are also of use in process control and corrosion analysis, but only a few systems are offered commercially. These systems use such polarization techniques as galvanodynamic or potentiodynamic, potentiostatic or galvanostatic, potentiostaircase or galvanostaircase, or cyclic polarization methods. Some systems involving these techniques are, in fact, used regularly in processing plants. These methods are used in situ or... 

Evidence of localized corrosion can be obtained from polarization methods such as potentiodynamic polarization, EIS, and electrochemical noise measurements, which are particularly well suited to providing data on localized corrosion. When evidence of localized attack is obtained, the engineer needs to perform a careful analysis of the conditions that may lead to such attack. Correlation with process conditions can provide additional data about the susceptibility of the equipment to locaHzed attack and can potentially help prevent failures due to pitting or crevice corrosion. Since pitting may have a delayed initiation phase, careful consideration of the cause of the localized attack is critical. Laboratory testing and involvement of an... 

It is preferable to carry out laboratory corrosion tests and to validate the data with service tests for the selection of materials. It is needless to note that the chosen test method be reliable and cost effective. Some of the test methods in use in industry are service tests, field tests, laboratory tests, and rapid electrochemical methods such as potentiodynamic polarization, linear polarization, electrochemical impedance and electrochemical noise. 

The methods of measuring corrosion rates in the course of testing corrosion inhibitors are conventional weight loss, electrochemical techniques such as linear polarization resistance, potentiodynamic polarization, AC impedance, and electrochemical potential or current noise. 

The test method ASTM F7464 covers the determination of the resistance to either pitting or crevice corrosion of passive metals and alloys from which surgical implants are produced. The resistance of surgical implants to localized corrosion is carried out in dilute sodium chloride solution under specific conditions of potentiodynamic test method. Typical transient decay curves under potentiostatic polarization should monitor susceptibility to localized corrosion. Alloys are ranked in terms of the critical potential for pitting, the higher (more noble) this potential, the more resistant is to passive film breakdown and to localized corrosion. (Sprowls)14... 

ASTM G59-97. (2009) Standard Test Method for Conducting Potentiodynamic Polarization Resistance Measurements, American Society for Testing Materials. 

---