Alternative technology for modifying a poly(aLkylene terephthalate) by incorporation of a phosphinate stmcture has been developed by Enichem. Phosphinate units of the stmcture —P(CgH5) (0)CH20— are introduced into a polyester such as PET or PBT by transesterification with an oligomer comprised of the aforementioned units (136). 

Decafluorobiphenyl [434-90-2] C F C F (mol wt, 334.1 mp, 68°C bp, 206°C), can be prepared by I Jllmann coupling of bromo- [344-04-7] chloro- [344-07-0] or iodopentafluorobenzene [827-15-6] with copper. This product shows good thermal stabiHty decafluorobiphenyl was recovered unchanged after 1 h below 575°C (270). Decafluorobiphenyl-based derivatives exhibit greater oxidative stabiHty than similar hydrocarbon compounds (271). Therm ally stable poly(fluorinated aryl ether) oligomers prepared from decafluorobiphenyl and bisphenols show low dielectric constant and moisture absorption which are attractive for electronic appHcations (272). 

The biodegradation of poly(alkylene glycols) is hindered by their lack of water solubiUty, and only the low oligomers of poly(propylene glycol) are biodegradable with any certainty (179—181), as are those of poly(tetramethylene glycol) (182). A similar xo-oxidation mechanism to that reported for poly(ethylene glycol) has been proposed. 

The phase behavior of several polybibenzoates with oxyalkylene spacers has been reported [11,14,15,20-27]. These spacers include the dimer of trimethylene glycol and different ethylene oxide oligomers. The most noticeable characteristic of these polybibenzoates with ether groups in the spacer is the considerable decrease of the rate of the mesophase-crystal transformation. Thus, Fig. 8 shows the DSC curves corresponding to a sample of poly[oxybis(trimethylene)p,p -bibenzoate], PDTMB, with a structure similar to that of P7MB but with the... 

This article, while not being intended to provide a full account of poly(arylene)s, emphasises the synthetic aspects. The synthesis of conjugated oligomers and polymers is, however, always part of an interdisciplinaiy approach with their active physical function being a key concern. In that sense the research being reviewed above concentrates on physical properties rather than playing with exotic chemical structures. 

By Naylor and Gilliam62, d (pT)6 was condensed in the presence of Poly A with carbodiimide to give d-(pT)12 with a yield of 5%. In the experiment of Shabarova and Prokofiev67, d-(pA)2 preactivated in the form of an amino add amidate was condensed on Poly U to give products with a yield of 10%. Uesugi and Ts o68 studied the condensation of (2 MeIp)6 or (2 MeIp)s in the presence of a Poly C template. The relative overall yield of the oligomer products was 43 to 71%. 

Hie most representative member of this class of polyesters is the low-molar-mass (M 1000-3000) hydroxy-terminated aliphatic poly(2,2/-oxydiethylene adipate) obtained by esterification between adipic acid and diethylene glycol. This oligomer is used as a macromonomer in the synthesis of polyurethane elastomers and flexible foams by reaction with diisocyanates (see Chapter 5). Hydroxy-terminated poly(f -caprolactonc) and copolyesters of various diols or polyols and diacids, such as o-phthalic acid or hydroxy acids, broaden the range of properties and applications of polyester polyols. 

The reported molar masses of polyesters obtained by enzymatic catalysis are relatively low, generally below 8000, except for polymers recovered by precipitation.336 This procedure results in the elimination of a soluble fraction consisting of low-molar-mass linear and cyclic oligomers.336 An Mw as high as 46,400 has thus been reported for a poly(tetramethylene decanedioate) obtained... 

Poly (ary lene ether sulfone)s and poly(arylene ether ketone) have been employed to prepare block and graft copolymers. Generally, the block copolymers can be prepared by reacting functional-group-terminated oligomers with other functional oligomers and monomers. 

Preparation of polyfethylene oxide) (PEO) and poly(arylene ether) based hydrophilic-hydrophobic block copolymer is of special interest because PEO has been proven to be particularly reliable and versatile for the surface modification of biomaterials. The first poly(ediylene oxide)-/ /oc/c-polysulfonc (PEO-fc-PSF) copolymers were reported by Aksenov et al.217 They employed diisocyanate chemistry to link hydroxy-terminated sulfone oligomers and polyfethylene... 

Hedrick et al. reported imide aryl ether ketone segmented block copolymers.228 The block copolymers were prepared via a two-step process. Both a bisphenol-A-based amorphous block and a semicrystalline block were prepared from a soluble and amorphous ketimine precursor. The blocks of poly(arylene ether ether ketone) oligomers with Mn range of 6000-12,000 g/mol were coreacted with 4,4,-oxydianiline (ODA) and pyromellitic dianhydride (PMDA) diethyl ester diacyl chloride in NMP in the presence of A - me thy 1 morphi 1 i nc. Clear films with high moduli by solution casting and followed by curing were obtained. Multiphase morphologies were observed in both cases. 

---