Iron nickel

Another system very similar to the cobalt-iron alloy system is FeNi. FeNi alloys were deposited from a sulfate electrolyte containing a sum of 1 mol dm metal salt. 0.5 mol dm H3BO4 were added and subsequently the pH was adjusted to pH = 2.0. The electrolyte was made with deoxidized water. No additives were used. The deposition was carried out under potentiostatic control on copper substrates. The composition was approximately independent on the potential between 1.1 and The results are presented 

The following selectivity constants were detennined = 15.5 and gNipe= 0.10 

The scattering of the data in this third example is larger than in the previous examples. 

---

It is alloyed with iron, nickel and other metals to make Alnico, an alloy of unusual magnetic strength with many important uses. Stellite alloys, containing cobalt, chromium, and tungsten, are used for high-speed, heavy-duty, high temperature cutting tools, and for dies. 

A large number of organometallic compounds are based on transition metals Examples include organic derivatives of iron nickel chromium platinum and rhodium Many important industrial processes are catalyzed by transition metals or their complexes Before we look at these processes a few words about the structures of transition metal complexes are m order... 

Density is a particularly important characteristic of alloys used in rotating machinery, because centrifugal stresses increase with density. Densities of the various metals in Table 1 range from 6.1 to 19.3 g/cm. Those of iron, nickel, and cobalt-base superaHoys fall in the range 7-8.5 g/cm. Those alloys which contain the heavier elements, ie, molybdenum, tantalum, or tungsten, have correspondingly high densities. 

Table 9. Composition of Iron—Nickel-Base Alloys, wt %...

Tables 10 and 11 list typical compositions of cast and wrought cobalt-base alloys, respectively. Stress—mpture properties of two wrought cobalt alloys, Haynes 188 and L-605, are compared to those of iron—nickel alloys ia Figure 10 (49). The cobalt alloys generally are inferior ia strength to the strongest cast nickel-base superaHoys. Tensile strengths at low and iatermediate temperatures are particularly deficient for the cobalt alloys.

Fig. 14. Effects of iron (—), nickel (-), and copper (...) contaminant levels on the saltwater corrosion performance of magnesium AZ91 alloy containing...

Metals less noble than copper, such as iron, nickel, and lead, dissolve from the anode. The lead precipitates as lead sulfate in the slimes. Other impurities such as arsenic, antimony, and bismuth remain partiy as insoluble compounds in the slimes and partiy as soluble complexes in the electrolyte. Precious metals, such as gold and silver, remain as metals in the anode slimes. The bulk of the slimes consist of particles of copper falling from the anode, and insoluble sulfides, selenides, or teUurides. These slimes are processed further for the recovery of the various constituents. Metals less noble than copper do not deposit but accumulate in solution. This requires periodic purification of the electrolyte to remove nickel sulfate, arsenic, and other impurities. 

Pyrometa.llurgica.1 Processes. Nickel oxide ores are processed by pyrometaHurgical or hydrometaHurgical methods. In the former, oxide ores are smelted with a sulfiding material, eg, gypsum, to produce an iron—nickel matte that can be treated similarly to the matte obtained from sulfide ores. The iron—nickel matte may be processed in a converter to eliminate iron. The nickel matte then can be cast into anodes and refined electrolyticaHy. 

Nickel—Iron. A large amount of nickel is used in alloy and stainless steels and in cast irons. Nickel is added to ferritic alloy steels to increase the hardenabihty and to modify ferrite and cementite properties and morphologies, and thus to improve the strength, toughness, and ductihty of the steel. In austenitic stainless steels, the nickel content is 7—35 wt %. Its primary roles are to stabilize the ductile austenite stmcture and to provide, in conjunction with chromium, good corrosion resistance. Nickel is added to cast irons to improve strength and toughness. 

The electro deposition of tungsten aUoys of iron, nickel, and cobalt is commercially feasible but has remained largely experimental. The properties of these aUoys should, however, be of sufficient interest for engineering appHcations. 

An important item in this array of matenals is the class known as maraging steels. This group of high nickel martensitic steels contain so Htde carbon that they are often referred to as carbon-free iron—nickel martensites (54). Carbon-free iron—nickel martensite with certain alloying elements is relatively soft and ductile and becomes hard, strong, and tough when subjected to an aging treatment at around 480°C. 

The first iron—nickel martensitic alloys contained ca 0.01% carbon, 20 or 25% nickel, and 1.5—2.5% aluminum and titanium. Later an 18% nickel steel containing cobalt, molybdenum, and titanium was developed, and still more recentiy a senes of 12% nickel steels containing chromium and molybdenum came on the market. 

Solvent for Electrolytic Reactions. Dimethyl sulfoxide has been widely used as a solvent for polarographic studies and a more negative cathode potential can be used in it than in water. In DMSO, cations can be successfully reduced to metals that react with water. Thus, the following metals have been electrodeposited from their salts in DMSO cerium, actinides, iron, nickel, cobalt, and manganese as amorphous deposits zinc, cadmium, tin, and bismuth as crystalline deposits and chromium, silver, lead, copper, and titanium (96—103). Generally, no metal less noble than zinc can be deposited from DMSO. 

Ozonation can be enhanced by the addition of ultraviolet (uv) radiation. This combination can be effective in degrading chlorinated organic compounds and pesticides. In addition, metal ions such as iron, nickel, chromium, and titanium [7440-32-6] can act as catalysts, as can ultrasonic mixing. 

Generally, most asphalts are 79—88 wt % C, 7—13 wt % H, trace-8 wt % S, 2—8 wt % O, and trace-3 wt % N (Table 7). Trace metals such as iron, nickel, vanadium, calcium, titanium, magnesium, sodium, cobalt, copper, tin, and 2inc, occur in cmde oils. Vanadium and nickel are bound in organic complexes and, by virtue of the concentration (distillation) process by which asphalt is manufactured, are also found in asphalt. 

Carbides of the Iron Group Metals. The carbides of iron, nickel, cobalt, and manganese have lower melting points, lower hardness, and different stmctures than the hard metallic materials. Nonetheless, these carbides, particularly iron carbide and the double carbides with other transition metals, are of great technical importance as hardening components of alloy steels and cast iron. 

I. G. Wright, Oxidation of Iron-, Nickel-, and Cobalt-Base Alloys, MCIC Report 72-07, BatteUe-Columbus Laboratories, BatteUe Memorial Institute, 1972. 

---