Solution Polymers. Acryflc solution polymers are usually characterized by their composition, solids content, viscosity, molecular weight, glass-transition temperature, and solvent. The compositions of acryflc polymers are most readily determined by physicochemical methods such as spectroscopy, pyrolytic gas—liquid chromatography, and refractive index measurements (97,158). The solids content of acryflc polymers is determined by dilution followed by solvent evaporation to constant weight. Viscosities are most conveniently determined with a Brookfield viscometer, molecular weight by intrinsic viscosity (158), and glass-transition temperature by calorimetry. 

In methacrylic ester polymers, the glass-transition temperature, is influenced primarily by the nature of the alcohol group as can be seen in Table 1. Below the the polymers are hard, brittle, and glass-like above the they are relatively soft, flexible, and mbbery. At even higher temperatures, depending on molecular weight, they flow and are tacky. Table 1 also contains typical values for the density, solubiHty parameter, and refractive index for various methacrylic homopolymers. 

T and are the glass-transition temperatures in K of the homopolymers and are the weight fractions of the comonomers (49). Because the glass-transition temperature is directly related to many other material properties, changes in T by copolymerization cause changes in other properties too. Polymer properties that depend on the glass-transition temperature include physical state, rate of thermal expansion, thermal properties, torsional modulus, refractive index, dissipation factor, brittle impact resistance, flow and heat distortion properties, and minimum film-forming temperature of polymer latex... 

Thermal Properties. Thermal properties include heat-deflection temperature (HDT), specific heat, continuous use temperature, thermal conductivity, coefficient of thermal expansion, and flammability ratings. Heat-deflection temperature is a measure of the minimum temperature that results in a specified deformation of a plastic beam under loads of 1.82 or 0.46 N/mm (264 or 67 psi, respectively). Eor an unreinforced plastic, this is typically ca 20°C below the glass-transition temperature, T, at which the molecular mobility is altered. Sometimes confused with HDT is the UL Thermal Index, which Underwriters Laboratories estabflshed as a safe continuous operation temperature for apparatus made of plastics (37). Typically, UL temperature indexes are significantly lower than HDTs. Specific heat and thermal conductivity relate to insulating properties. The coefficient of thermal expansion is an important component of mold shrinkage and must be considered when designing composite stmctures. 

Poly(vinyl acetate) is too soft and shows excessive cold flow for use in moulded plastics. This is no doubt associated with the fact that the glass transition temperature of 28°C is little above the usual ambient temperatures and in fact in many places at various times the glass temperature may be the lower. It has a density of 1.19 g/cm and a refractive index of 1.47. Commercial polymers are atactic and, since they do not crystallise, transparent (if free from emulsifier). They are successfully used in emulsion paints, as adhesives for textiles, paper and wood, as a sizing material and as a permanent starch . A number of grades are supplied by manufacturers which differ in molecular weight and in the nature of comonomers (e.g. vinyl maleate) which are commonly used (see Section 14.4.4)... 

This statement can be proved very easily by considering four different types of general POP properties and their variability as a function of the side substituents on the polymer skeleton, i.e. glass transition temperature (Tg), morphology, solvent solubility and limiting oxygen index (LOI). The values of these parameters are reported in Tables 5-8. 

Table 10 Glass transition temperatures and limiting oxygen index values for selected aryloxyphosphazenes copolymers [284,584,585] ...

The transition between crystalline and amorphous polymers is characterized by the so-called glass transition temperature, Tg. This important quantity is defined as the temperature above which the polymer chains have acquired sufficient thermal energy for rotational or torsional oscillations to occur about the majority of bonds in the chain. Below 7"g, the polymer chain has a more or less fixed conformation. On heating through the temperature Tg, there is an abrupt change of the coefficient of thermal expansion (or), compressibility, specific heat, diffusion coefficient, solubility of gases, refractive index, and many other properties including the chemical reactivity. 

Films containing about 10% CIRh(PPh3)3 in PMMA were prepared and subjected to oxygen index, TGA, and DSC measurements. The oxygen index, bottom ignition (1 1), increases from about 14 for pure PMMA to about 20 for the rhodium compound in PMMA. TGA analysis indicates that about 25% of the sample is non-volatile at 600°C and the glass transition temperature increases by about 15°C by DSC. 

Table 1 Glass transition temperature (7 gi), melting temperature (V m) and melt flow index (MFI) of polymers...

PS has a high index of refraction (1.592) and hence has excellent transparency to visible light. PS is a brittle polymer with a glass transition temperature rgof 100 C, a heat deflection temperature of 90 C, and a solubility parameter of 9.1 H. 

Amorphous polymers characteristically possess excellent optical properties. Unlike all the other commercially available fluoropolymers, which are semicrystalline, Teflon AF is quite clear and has optical transmission greater than 90% throughout most of the UV, visible, and near-IR spectrum. A spectrum of a 2.77-mm-thick slab of AF-1600 is shown in Figure 2.5. Note the absence of any absorption peak. Thin films of Teflon AF have UV transmission greater Ilian 95% at 200 mm and are unaffected by radiation from UV lasers. The refractive indexes of Teflon AF copolymers are shown in Figure 2.6 and decrease with increasing FDD content. These are the lowest refractive indexes of any polymer family. It should be noted that the abscissa could also be labeled as glass transition temperature, Tg, since Tg is a function of the FDD content of the AF copolymer. Abbe numbers are low 92 and 113 for AF-1600 and AF-2400. 

Glass transition temperature is one of the most important parameters used to determine the application scope of a polymeric material. Properties of PVDF such as modulus, thermal expansion coefficient, dielectric constant and loss, heat capacity, refractive index, and hardness change drastically helow and above the glass transition temperature. A compatible polymer blend has properties intermediate between those of its constituents. The change of glass transition temperature has been a widely used method to study the compatibility of polymer blends. Normally, the glass transition temperatme of a compatible polymer blend can be predicted by the Gordon-Taylor relation ... 

Fluorine content (%) Decomp. temperature (°C) Glass transition temperature (°C) Dielectric constant (E) Average refractive index (H) In-plane/out-of- plane birefringence (Ani)... 

The combination of high transparency, high glass transition temperature, and refractive index, together with an excellent process-ability, makes COCs attractive as an alternative for materials like poly(carbonate) and PMMA in the field of optical components and high capacity DVDs and compact disks (57,58). 

The glass transition temperatures of the plasticized polycarbonates have been determined by measuring the refractive index of properly compounded films as a function of temperature. The glass transition temperatures are those temperatures... 

---