Glass modulus

Dehye temperature 474 electrical conductivity 392 electron configuration 14, 516 electronegativity 36 glasses, modulus of elasticity 301 heat capacity at room temperature 474... 

When 00 holds in constant, for instance, the glass modulus, or the rubbery modulus exhibiting linear viscoelasticity. 

In Figure 5.23 the finite element model predictions based on with constraint and unconstrained boundary conditions for the modulus of a glass/epoxy resin composite for various filler volume fractions are shown. 

In Figure 5.24 the predicted direct stress distributions for a glass-filled epoxy resin under unconstrained conditions for both pha.ses are shown. The material parameters used in this calculation are elasticity modulus and Poisson s ratio of (3.01 GPa, 0.35) for the epoxy matrix and (76.0 GPa, 0.21) for glass spheres, respectively. According to this result the position of maximum stress concentration is almost directly above the pole of the spherical particle. Therefore for a... 

Material properties can be further classified into fundamental properties and derived properties. Fundamental properties are a direct consequence of the molecular structure, such as van der Waals volume, cohesive energy, and heat capacity. Derived properties are not readily identified with a certain aspect of molecular structure. Glass transition temperature, density, solubility, and bulk modulus would be considered derived properties. The way in which fundamental properties are obtained from a simulation is often readily apparent. The way in which derived properties are computed is often an empirically determined combination of fundamental properties. Such empirical methods can give more erratic results, reliable for one class of compounds but not for another. 

At very short times the modulus is on the order of 10" ° N m comparable to ordinary window glass at room temperature. In fact, the mechanical behavior displayed in this region is called the glassy state, regardless of the chemical composition of the specimen. Inorganic and polymeric glasses... 

Improved Hot—Wet Properties. Acryhc fibers tend to lose modulus under hot—wet conditions. Knits and woven fabrics tend to lose their bulk and shape in dyeing and, to a more limited extent, in washing and drying cycles as well as in high humidity weather. Moisture lowers the glass-transition temperature T of acrylonitrile copolymers and, therefore, crimp is lost when the yam is exposed to conditions requited for dyeing and laundering. 

Elasticity. Glasses, like other britde materials, deform elastically until they break in direct proportion to the appHed stress. The Young s modulus E is the constant of proportionaUty between the appHed stress and the resulting strain. It is about 70 GPa (10 psi) [(0.07 MPa stress per )Tm/m strain = (0.07 MPa-m) / Tm)] for a typical glass. 

The glass-ceramic phase assemblage, ie, the types of crystals and the proportion of crystals to glass, is responsible for many of the physical and chemical properties, such as thermal and electrical characteristics, chemical durabiUty, elastic modulus, and hardness. In many cases these properties are additive for example, a phase assemblage comprising high and low expansion crystals has a bulk thermal expansion proportional to the amounts of each of these crystals. 

The TPX experimental product of Mitsubishi Petrochemical Ind. (221) is an amorphous, transparent polyolefin with very low water absorption (0.01%) and a glass-transition temperature comparable to that of BPA-PC (ca 150°C). Birefringence (<20 nm/mm), flexural modulus, and elongation at break are on the same level as PMMA (221). The vacuum time, the time in minutes to reach a pressure of 0.13 mPa (10 torr), is similarly short like that of cychc polyolefins. Typical values of TPX are fisted in Table 11. A commercial application of TPX is not known as of this writing. 

Fig. 26. Qualitative compatison of substrate materials for optical disks (187) An = birefringence IS = impact strength BM = bending modulus HDT = heat distortion temperature Met = metallizability WA = water absorption Proc = processibility. The materials are bisphenol A—polycarbonate (BPA-PC), copolymer (20 80) of BPA-PC and trimethylcyclohexane—polycarbonate (TMC-PC), poly(methyl methacrylate) (PMMA), uv-curable cross-linked polymer (uv-DM), cycHc polyolefins (CPO), and, for comparison, glass.

The effect of temperature on properties can be seen in Figure 2, which shows the effect on modulus of increasing temperature of unmodified and glass-reinforced nylon-6,6. Impact strength, however, shows a steady increase with temperature as it does with moisture. 

Fig. 2. Effect of temperature on the shear modulus of dry nylon-6,6 (—) and nylon-6,6 plus 30% glass fiber (-). To covert MPa to psi, multiply by 145.

Polycarbonates are an unusual and extremely useful class of polymers. The vast majority of polycarbonates are based on bisphenol A [80-05-7] (BPA) and sold under the trade names Lexan (GE), Makrolon (Bayer), CaUbre (Dow), and Panlite (Idemitsu). BPA polycarbonates [25037-45-0] having glass-transition temperatures in the range of 145—155°C, are widely regarded for optical clarity and exceptional impact resistance and ductiUty at room temperature and below. Other properties, such as modulus, dielectric strength, or tensile strength are comparable to other amorphous thermoplastics at similar temperatures below their respective glass-transition temperatures, T. Whereas below their Ts most amorphous polymers are stiff and britde, polycarbonates retain their ductiUty. 

---