Dynamic scanning calorimetry

Other characterization methods that are of value are dynamic scanning calorimetry (DSC) and thermal gravimetric analysis (TGA). A sample DSC is shown in the middle of Figure 15.2. Most cure reactions are exothermic, and the heat generated by cure can cause excessive heat to build up in the polymer if control is not exercised. DSC measures the generation of heat as a function of time and temperature. This can be used to predict the temperature at which the laminate will begin to cure (the onset of the peak in Fig. 15.2) and the temperature or time at which cure will be complete, further improving the selection of cure cycles to try. 

Tg values can be determined via either calorimetric, dynamic scanning calorimetry (DSC) or mechanical dynamic mechanical analysis (DMA) measurements. However, since three dimensional highly crosslinked systems have relatively small amounts of molecular motion, the DSC method is not particularly sensitive for Tg determination [131,132]. Fry and Lind have reported that DSC is misleading, as reactive groups are often sufficiently entrapped in the vitrified structure to give spurious results [133]. 

Extrapolated values at 0% moisture content High molecular weight glutenins DSC Dynamic scanning calorimetry DMTA Dynamic mechanical thermal analysis ... 

C Tm s ranging from 165-205 C as determined by dynamic scanning calorimetry (Table 3). The polymers readily crystallized from the melt, and crystallization transitions, Tc, were readily observed at a temperature 30-40 C below Tm as the... 

No. 15, 2000, p.5949-55 UNDERSTANDEVG VITRIFICATION DURING CURE OF EPOXY RESINS USING DYNAMIC SCANNING CALORIMETRY AND RHEOLOGICAL TECHNIQUES Lange J Altmann N Kelly C T Halley P J Queensland,University... 

The crystal stmcture of glycerides may be unambiguously determined by x-ray diffraction of powdered samples. However, the dynamic crystallization may also be readily studied by differential scanning calorimetry (dsc). Crystallization, remelting, and recrystallization to a more stable form may be observed when Hquid fat is solidified at a carefully controlled rate ia the iastmment. Enthalpy values and melting poiats for the various crystal forms are shown ia Table 3 (52). 

Other PDMS—sihca-based hybrids have been reported (16,17) and related to the ceramer hybrids (10—12,17). Using differential scanning calorimetry, dynamic mechanical analysis, and saxs, the microstmcture of these PDMS hybrids was determined to be microphase-separated, in that the polysiUcate domains (of ca 3 nm in diameter) behave as network cross-link junctions dispersed within the PDMS oligomer-rich phase. The distance between these... 

Glass-transition temperatures are commonly determined by differential scanning calorimetry or dynamic mechanical analysis. Many reported values have been measured by dilatometric methods however, methods based on the torsional pendulum, strain gauge, and refractivity also give results which are ia good agreement. Vicat temperature and britde poiat yield only approximate transition temperature values but are useful because of the simplicity of measurement. The reported T values for a large number of polymers may be found ia References 5, 6, 12, and 13. 

Thermal analysis iavolves techniques ia which a physical property of a material is measured agaiast temperature at the same time the material is exposed to a coatroUed temperature program. A wide range of thermal analysis techniques have been developed siace the commercial development of automated thermal equipment as Hsted ia Table 1. Of these the best known and most often used for polymers are thermogravimetry (tg), differential thermal analysis (dta), differential scanning calorimetry (dsc), and dynamic mechanical analysis (dma). 

The thermal glass-transition temperatures of poly(vinyl acetal)s can be determined by dynamic mechanical analysis, differential scanning calorimetry, and nmr techniques (31). The thermal glass-transition temperature of poly(vinyl acetal) resins prepared from aliphatic aldehydes can be estimated from empirical relationships such as equation 1 where OH and OAc are the weight percent of vinyl alcohol and vinyl acetate units and C is the number of carbons in the chain derived from the aldehyde. The symbols with subscripts are the corresponding values for a standard (s) resin with known parameters (32). The formula accurately predicts that resin T increases as vinyl alcohol content increases, and decreases as vinyl acetate content and aldehyde carbon chain length increases. 

A number of analytical techniques such as FTIR spectroscopy,65-66 13C NMR,67,68 solid-state 13 C NMR,69 GPC or size exclusion chromatography (SEC),67-72 HPLC,73 mass spectrometric analysis,74 differential scanning calorimetry (DSC),67 75 76 and dynamic mechanical analysis (DMA)77 78 have been utilized to characterize resole syntheses and crosslinking reactions. Packed-column supercritical fluid chromatography with a negative-ion atmospheric pressure chemical ionization mass spectrometric detector has also been used to separate and characterize resoles resins.79 This section provides some examples of how these techniques are used in practical applications. 

Dynamic DSC, 409. See also Differential scanning calorimetry (DSC) Dynamic mechanical analysis (DMA), 138, 163, 241-242, 407, 409... 

A3 AIBN c Cp DLS DLVO DSC EO GMA HS-DSC KPS LCST Osmotic third virial coefficient 2,2 -Azobis(isobutyronitrile) Polymer concentration Partial heat capacity Dynamic light scattering Derjaguin-Landau-Verwey-Overbeek Differential scanning calorimetry Ethylene oxide Glycidylmethacrylate High-sensitivity differential scanning calorimetry Potassium persulphate Lower critical solution temperature... 

Teoh, H.M., Schmidt, SJ., Day, G.A., and Faller, J.F. 2001. Investigation of commeal components using dynamic vapor sorption and differential scanning calorimetry. J. Food Sci. 66, 434-440. Tromp, R.H., Parker, R., and Ring, S.G. 1997. Water diffusion in glasses of carbohydrates. Carbo-hydr. Res. 303, 199-205. 

Dynamic mechanical anlaysis (DMA) measurements were done on a Rheometrics RDS-7700 rheometer in torsional rectangular geometry mode using 60 x 12 x 3 mm samples at 0.05% strain and 1 Hz. Differential scanning calorimetry (DSC), thermomechanical analysis (TMA), and thermogravimetric analysis (TGA) were performed on a Perkin-Elmer 7000 thermal analysis system. 

Bisphthalonitrile monomers were cured neat, with nucleophilic and redox co-reactants, or in combination with a reactive diluent. Dynamic mechanical measurements on the resulting polymers from -150 to +300°C turn up several differences attributable to differences in network structure. Rheovibron results were supplemented with solvent extraction, differential scanning calorimetry (DSC), vapor pressure osmometry, and infrared spectroscopy to characterize the state of cure. 

---