Copolymers radical polymerization

Polymeric vinylidene chloride generally produced by free radical polymerization of CH2 = CCl2. Homopolymers and copolymers are used. A thermoplastic used in moulding, coatings and fibres. The polymers have high thermal stability and low permeability to gases, and are self extinguishing. 

The elastomer produced in greatest amount is styrene-butadiene rubber (SBR) Annually just under 10 lb of SBR IS produced in the United States and al most all of it IS used in automobile tires As its name suggests SBR is prepared from styrene and 1 3 buta diene It is an example of a copolymer a polymer as sembled from two or more different monomers Free radical polymerization of a mixture of styrene and 1 3 butadiene gives SBR... 

Remember from Sec. 1.3 that graft copolymers have polymeric side chains which differ in the nature of the repeat unit from the backbone. These can be prepared by introducing a prepolymerized sample of the backbone polymer into a reactive mixture—i.e., one containing a source of free radicals—of the side-chain monomer. As an example, consider introducing polybutadiene into a reactive mixture of styrene ... 

We begin our discussion of copolymers by considering the free-radical polymerization of a mixture of two monomers. Mi and M2. This is already a narrow view of the entire field of copolymers, since more than two repeat units can be present in copolymers and, in addition, mechanisms other than free-radical chain growth can be responsible for copolymer formation. The essential features of the problem are introduced by this simpler special case, so we shall restrict our attention to this system. 

Butenediol does not undergo free-radical polymerization. A copolymer with vinyl acetate can be prepared with a low proportion of butenediol (110). 

Emulsion Adhesives. The most widely used emulsion-based adhesive is that based upon poly(vinyl acetate)—poly(vinyl alcohol) copolymers formed by free-radical polymerization in an emulsion system. Poly(vinyl alcohol) is typically formed by hydrolysis of the poly(vinyl acetate). The properties of the emulsion are derived from the polymer employed in the polymerization as weU as from the system used to emulsify the polymer in water. The emulsion is stabilized by a combination of a surfactant plus a coUoid protection system. The protective coUoids are similar to those used paint (qv) to stabilize latex. For poly(vinyl acetate), the protective coUoids are isolated from natural gums and ceUulosic resins (carboxymethylceUulose or hydroxyethjdceUulose). The hydroHzed polymer may also be used. The physical properties of the poly(vinyl acetate) polymer can be modified by changing the co-monomer used in the polymerization. Any material which is free-radically active and participates in an emulsion polymerization can be employed. Plasticizers (qv), tackifiers, viscosity modifiers, solvents (added to coalesce the emulsion particles), fillers, humectants, and other materials are often added to the adhesive to meet specifications for the intended appHcation. Because the presence of foam in the bond line could decrease performance of the adhesion joint, agents that control the amount of air entrapped in an adhesive bond must be added. Biocides are also necessary many of the materials that are used to stabilize poly(vinyl acetate) emulsions are natural products. Poly(vinyl acetate) adhesives known as "white glue" or "carpenter s glue" are available under a number of different trade names. AppHcations are found mosdy in the area of adhesion to paper and wood (see Vinyl polymers). 

Polymerization of methacrylates is also possible via what is known as group-transfer polymerization. Although only limited commercial use has been made of this technique, it does provide a route to block copolymers that is not available from ordinary free-radical polymerizations. In a prototypical group-transfer polymerization the fluoride-ion-catalyzed reaction of a methacrylate (or acrylate) in the presence of a silyl ketene acetal gives a high molecular weight polymer (45—50). 

Copolymers of VDC can also be prepared by methods other than conventional free-radical polymerization. Copolymers have been formed by irradiation and with various organometaHic and coordination complex catalysts (28,44,50—53). Graft copolymers have also been described (54—58). 

The nmr spectmm of PVAc iu carbon tetrachloride solution at 110°C shows absorptions at 4.86 5 (pentad) of the methine proton 1.78 5 (triad) of the methylene group and 1.98 5, 1.96 5, and 1.94 5, which are the resonances of the acetate methyls iu isotactic, heterotactic, and syndiotactic triads, respectively. Poly(vinyl acetate) produced by normal free-radical polymerization is completely atactic and noncrystalline. The nmr spectra of ethylene vinyl acetate copolymers have also been obtained (33). The ir spectra of the copolymers of vinyl acetate differ from that of the homopolymer depending on the identity of the comonomers and their proportion. 

In contrast to ionic chain polymerizations, free radical polymerizations offer a facile route to copolymers ([9] p. 459). The ability of monomers to undergo copolymerization is described by the reactivity ratios, which have been tabulated for many monomer systems for a tabulation of reactivity ratios, see Section 11/154 in Brandrup and Immergut [14]. These tabulations must be used with care, however, as reactivity ratios are not always calculated in an optimum manner [15]. Systems in which one reactivity ratio is much greater than one (1) and the other is much less than one indicate poor copolymerization. Such systems form a mixture of homopolymers rather than a copolymer. Uncontrolled phase separation may take place, and mechanical properties can suffer. An important ramification of the ease of forming copolymers will be discussed in Section 3.1. 

Mixtures of monomers can be used to balance properties. This is possible due to the ease of copolymer formation via free-radical polymerization. The glass transition temperature of acrylic copolymers can be predicted from the weight fraction of the component monomers and the glass transition temperatures of the respective homopolymers [20]. Eq. 3 (commonly known as the Fox equation) is reported ... 

A novel cross-linked polystyrene-divinylbenzene copolymer has been produced from suspension polymerization with toluene as a diluent, having an average particle size of 2 to 50 /rm, with an exclusive molecular weight for the polystyrene standard from about 500 to 20,000 in gel-permeation chromatography. A process for preparing the PS-DVB copolymer by suspension polymerization in the presence of at least one free-radical polymerization initiator, such as 2,2 -azo-bis (2,4-dimethylvaleronitrile) with a half-life of about 2 to 60 min at 70°C, has been disclosed (78). 

The block copolymer produced by Bamford s metal carbonyl/halide-terminated polymers photoinitiating systems are, therefore, more versatile than those based on anionic polymerization, since a wide range of monomers may be incorporated into the block. Although the mean block length is controllable through the parameters that normally determine the mean kinetic chain length in a free radical polymerization, the molecular weight distributions are, of course, much broader than with ionic polymerization and the polymers are, therefore, less well defined,... 

The structure-property relationship of graft copolymers based on an elastomeric backbone poly(ethyl acry-late)-g-polystyrene was studied by Peiffer and Rabeony [321. The copolymer was prepared by the free radical polymerization technique and, it was found that the improvement in properties depends upon factors such as the number of grafts/chain, graft molecular weight, etc. It was shown that mutually grafted copolymers produce a variety of compatibilized ternary component blends. 

Corner, T. Free Radical Polymerization — The Synthesis of Graft Copolymers. Vol. 62, pp. 95— 142. 

It has been shown by Schulz and Kern2 J that the radical polymerization of acrolein can take the course of the 1,2-mechanism as well as that of the 1,4- or 3,4-mechanism leading to formylethylene, oxy-2-propenylene, or oxy-2-propenylidene units, respectively. This behaviour of acrolein and its derivatives seems to be also retained to a certain extent, in the radical copolymerization of 4 with AN causing a decrease fo the content of aldehyde groups in the copolymers. 

The C-S bond of the sulfide end groups can be relatively weak and susceptible to thermal and photo- or radical-induced homolysis. This means that certain disulfides [for example 7-9] may act as iniferters in living radical polymerization and they can be used as precursors to block copolymers (Sections 7.5.1 and 9.3.2). 

Many block and graft copolymer syntheses involve radical polymerization at some stage of the overall preparation. This section deals with direct syntheses of... 

Further examples of micellar stabilization when micelles are composed of block copolymers formed by living radical polymerization are mentioned in Section 9.9.2. 

Chung and coworkers have reported on the use of stable borinale or boroxyl radicals (e.g. 114) to mediate radical polymerization." Methacrylates (MMA) and acrylates (trifluoroelhyl acrylate) have been polymerized at ambient temperature to yield polymers with relatively narrow molecular weight distributions.231233 The method has been used to prepare block copolymers and polyolefin graft copolymers.2 4 37... 

---