Copolymerization, glass transition polymers

Most Kaminsky catalysts contain only one type of active center. They produce ethylene—a-olefin copolymers with uniform compositional distributions and quite narrow MWDs which, at their limit, can be characterized by M.Jratios of about 2.0 and MFR of about 15. These features of the catalysts determine their first appHcations in the specialty resin area, to be used in the synthesis of either uniformly branched VLDPE resins or completely amorphous PE plastomers. Kaminsky catalysts have been gradually replacing Ziegler catalysts in the manufacture of certain commodity LLDPE products. They also faciUtate the copolymerization of ethylene with cycHc dienes such as cyclopentene and norhornene (33,34). These copolymers are compositionaHy uniform and can be used as LLDPE resins with special properties. Ethylene—norhornene copolymers are resistant to chemicals and heat, have high glass transitions, and very high transparency which makes them suitable for polymer optical fibers (34). 

The glass-transition temperature in amorphous polymers is also sensitive to copolymerization. Generally, T of a random copolymer falls between the glass-transition temperatures of the respective homopolymers. For example, T for solution-polymerized polybutadiene is —that for solution-polymerized polystyrene is -HlOO°C. A commercial solution random copolymer of butadiene and styrene (Firestone s Stereon) shows an intermediate T of —(48). The glass-transition temperature of the random copolymer can sometimes be related simply as follows ... 

T and are the glass-transition temperatures in K of the homopolymers and are the weight fractions of the comonomers (49). Because the glass-transition temperature is directly related to many other material properties, changes in T by copolymerization cause changes in other properties too. Polymer properties that depend on the glass-transition temperature include physical state, rate of thermal expansion, thermal properties, torsional modulus, refractive index, dissipation factor, brittle impact resistance, flow and heat distortion properties, and minimum film-forming temperature of polymer latex... 

This combination of monomers is unique in that the two are very different chemically, and in thek character in a polymer. Polybutadiene homopolymer has a low glass-transition temperature, remaining mbbery as low as —85° C, and is a very nonpolar substance with Htde resistance to hydrocarbon fluids such as oil or gasoline. Polyacrylonitrile, on the other hand, has a glass temperature of about 110°C, and is very polar and resistant to hydrocarbon fluids (see Acrylonitrile polymers). As a result, copolymerization of the two monomers at different ratios provides a wide choice of combinations of properties. In addition to providing the mbbery nature to the copolymer, butadiene also provides residual unsaturation, both in the main chain in the case of 1,4, or in a side chain in the case of 1,2 polymerization. This residual unsaturation is useful as a cure site for vulcanization by sulfur or by peroxides, but is also a weak point for chemical attack, such as oxidation, especially at elevated temperatures. As a result, all commercial NBR products contain small amounts ( 0.5-2.5%) of antioxidant to protect the polymer during its manufacture, storage, and use. 

Plasticizers and Copolymerization also shift the glass transition responses of the amorphous phase of crystalline polymers. In addition, the degree of Crystallinity and melting point are lowered. The resulting effects on the... 

Copolymerization. Introducing a comonomer (one of the compounds comprising the monomer) with known glass transition temperature, Tgl, into a polymer with known Tg 2 to form a copolymer (a polymer comprised of two or more monomers) can affect the glass transition temperature. If the two homopolymers (polymer... 

Besides by motions of chain parts or side groups (see 3.4), a secondary transition can also result from the presence of a second polymer, which has been added in a small quantity by blending, or which has, as tails , be copolymerized with the main polymer. Such a second polymer then has its glass transition at Tsec. Both cases occur when the impact strength of a polymer has been improved, either by blending with some rubber, or by copolymerization. A similar situation is found with block copolymers. In 3.5 these cases are dealt with in more detail. 

---