Low expansion surface regions can be obtained by removal of alkali from the surface region of alkali-alkaline earth-silicate glasses. Exposure to SO2 vapor, which is often carried out to improve chemical durability, leaches alkali ions from the surface, producing a silica-rich near-surface region. The reduction in alkali concentration reduces the thermal expansion coefficient and produces a compressive layer after cooling the glass. 

The network-forming structure of silicate glasses, such as alkali or alkaline-earth silicate glasses, is composed of (SiO ) tetrahedra (Kreidl 1983). Because of the tetravalence of silicon, (SiO ) tetrahedra can link together on four corners by means of oxygen ions to form a fiilly three-dimensional network. In alkali or alkaline-earth silicate glasses, the alkali and alkaline-earth ions break Si-O-Si bonds, loosening the (SiO ) tetrahedra network. 

Direct information on structural regions dominated by different Q" species in Alkaline/alkaline earth silicate glasses have been obtained from linear and multilinear regressions. The statistical models achieved an accuracy in prediction of about 2 ppm for the Si 5iso [87], 10 ppm for the Na 5iso [91], of 2°-4 for the mean value of the Si-O-Si bond angle distribution, 2°-4° [87], and of less than 10 ppm for the chemical shift anisotropy Si Acs of the species [91]. 

Alkali-Alkaline-Earth Silicate Glasses (Soda-Lime Glasses). This is the oldest glass type, which is produced in large batches for windows and containers (see Sect. 3.4.3). Such glasses contain about 71% Si02,... 

Structure of Alkali-Alkaline Earth-Silicate Glass... 

As a further consequence microstructured glass components caimot be used at T exceeding T j. Micron-sized holes and channels, sharp edges or walls will deform by viscous flowing of the glass. Microstructured alkali alkaline earth silicate glasses can be safely used up to temperatures of about 350° C (see also Fig. 1.27, it shows the temperatures of the annealing point... 

The thermal expansion coefEcient a of alkali alkaline earth silicate glasses varies from 7 to 10 x 10 K depending on the actual chemical composition of the glass and is many times greater than for silica (quartz) glass. 

Besides the chemical composition the size of the cooled glass devices also depends on the cooling rate in the transformation range (Fig. 1.31). Therefore the cooling rate plays also a part if a joining between an alkali alkaline earth silicate glass with another material exhibits inner stresses. 

The specific electrical resistivity of alkali alkaline earth silicate glasses at room temperature is still high enough (ranging from 10 ° to 10 " H cm) for them to be electrical insulators. However, with increasing temperature the electrical resistivity decreases. A material is classified as insulator if the specific electrical resistivity exceeds 10 Q cm, which is only given for alkali alkaline earth silicate glasses if the temperature does not exceed about 150°C. This temperature is the maximum service temperature for alkali alkaline earth... 

Unfortunately the addition of large amounts of alkali oxides to silica leads to a reduction of the chemical durability of the resulting glass. Although commercial alkali alkaline earth silicate glasses are used as bottles and other containers for liquids, these glasses are compared with silica glass rather susceptible to dissolution in water and chemical reactions with acids and alkaline lyes. 

All these remarks are very important for appljdng alkali alkaline earth silicate glasses in microdevices. Nevertheless, absolutely regarded in comparison with other materials, also these glasses are chemically resistant. 

---