Since the m,m -DABP polyimide is known to be an outstanding adhesive, lap shear strength tests employing titanium-titanium adherends and metal ion filled polyimides were conducted. Tests were performed at room temperature, 250°C and 275°C employing either DMAC or DMAC/Diglyme as the solvent. At room temperature regardless of the metal ion employed adhesive strength is de-... 

This chapter will cover acrylic chemistry, the various types of acrylic adhesives that have come into existence over the years, advantages and limitations of these systems, properties of adhesives, lap shear strength, what makes these systems unique among other types of adhesives, and examples of performance. 

The primary motivation for preparing metal ion modified polyimide films has been to obtain materials having mechanical, electrical, optical, adhesive and surface chemical properties different from nonmodified polyimide films. For example, the tensile modulus of metal ion modified polyimide films was increased (both at room temperature and 200°C) an elongation was reduced compared with the nonmodified polyimide. Although certain polyimides are known to be excellent adhesives, lap shear strength (between titanium adherends) at elevated temperature (275 C) was increased grther by incorporation of tris(acetylacetonato)aluminum(III). In another example, highly... 

Adhesive lap shear strengths of the ATS-modified LARC-13/titanium bonds tested at ambient and elevated temperatures are presented in Table 5. As was found in previous studies (Table 1), toughness has been achieved at a sacrifice to the elevated temperature strengths of the adhesives containing individual elastomers ATSj q to... 

Effect of adherend material on adhesive lap-shear strength ... 

Polyimides of 6FDA and aUphatic diamines with good low temperature processkig and low moisture swelling are known to be useful as hot-melt adhesives (109). Aluminum strips bonded by this polymer (177°C/172 kPa (25 psi) for 15 min) exhibited a lap-shear strength of 53 MPa (7690 psi) at room temperature and 35 MPa (5090 psi) at 100°C. The heat- and moisture-resistant 6F-containing Pis useful ki electronic devices are prepared from... 

Primer (source) Adhesive Tensile lap shear strength (psi) ... 

Flexibilized epoxy resins are important structural adhesives [69]. Liquid functionally terminated nitrile rubbers are excellent flexibilizing agents for epoxy resins. This liquid nitrile rubber can be reacted into the epoxy matrix if it contains carboxylated terminated functionalities or by adding an amine terminated rubber. The main effects produced by addition of liquid nitrile rubber in epoxy formulations is the increase in T-peel strength and in low-temperature lap shear strength, without reducing the elevated temperature lap shear. 

St. Clair et. al. investigated a series of maleimide and nadimide terminated polyimides and developed LARC-13 [8,9]. Changing the terminal group from maleimide to nadimide, the value of the lap shear strength of a titanium lap shear joint increased from 7 to 19 MPa [9]. They also added an elastomeric component to the adhesive formulation. The introduction of 15 wt% of a rubbery component, ATBN (amine terminated butadiene nitrile polymer) and ADMS (aniline terminated polydimethyl siloxane) enhanced the adhesive properties as follows 19 MPa to 25 MPa (ATBN) titanium T-peel strength 0.2 kN/m to 1.4... 

In other studies [115], the bond strengths of joints made from steel substrates coated with a variety of oils and waxes ( 6 mg/cm ) and Joined with acrylic adhesive were investigated. Lap-shear strengths up to 15 MPa were obtained with room temperature curing. Very little degradation was seen after 1000 h of... 

Lap shear strengths for EB-cured acrylic adhesives on graphite composites... 

Adhesive Curing dose (kGy) Man. specs. Lap shear strength (MPa) ... 

There has been very little work done on the development of EB-curable epoxy adhesives. When undertaking this development work the authors had two objectives. The first objective was to develop a series of adhesives for bonding aluminum-to-aluminum (Al-Al) and composite-to-composite (C-C) with lap shear strengths of 30 MPa or greater at room temperature. The second objective was that the... 

We have also looked at the lap shear strength of selected EB-ciirable epoxy adhesives. Because the adhesives being developed were being used for both aluminum-to-aluminum and composite-to-composite applications the lap shear strengths for both adherends was measured. Aluminum adherends were T2024 phosphoric acid anodized according to ASTM 3933. The composite adherends... 

Lap shear strengths (MPa) of selected EB-cured epoxy adhesives at various temperatures... 

Effects on lap shear strength of EB-cured epoxy adhesives from different surface preparations on aluminum and composite adherends... 

Patel et al. [70] in a recent publication have explored the adhesive action of the mbber-siUca hybrid nanocomposites on different substrates. The rubber-silica hybrid nanocomposites are synthesized through in situ silica formation from TEOS in strong acidic pH within acryhc copolymer (EA-BA) and terpolymer (EA-BA-AA) matrices. The transparent nanocomposites have been apphed in between the aluminum (Al), wood (W), and biaxially oriented polypropylene (PP) sheets separately and have been tested for peel strength, lap shear strength, and static holding power of the adhesive joints. 

ISO 1926 1979 Cellular plastics - Determination of tensile properties of rigid materials ISO 4587 2003 Adhesives - Determination of tensile lap-shear strength of rigid-to-rigid... 

Corrosion Testing. Salt spray testing (ASTM-B-117-52,54) was used to determine durability of adhesive bond in corrosive environment. Lap shear samples were exposed to salt spray for 14 days and then immediately tested for lap shear strength. 

---