Thermal properties dynamic mechanical analysis

Thermal analysis iavolves techniques ia which a physical property of a material is measured agaiast temperature at the same time the material is exposed to a coatroUed temperature program. A wide range of thermal analysis techniques have been developed siace the commercial development of automated thermal equipment as Hsted ia Table 1. Of these the best known and most often used for polymers are thermogravimetry (tg), differential thermal analysis (dta), differential scanning calorimetry (dsc), and dynamic mechanical analysis (dma). 

Thermal Properties. Spider dragline silk was thermally stable to about 230°C based on thermal gravimetric analysis (tga) (33). Two thermal transitions were observed by dynamic mechanical analysis (dma), one at —75° C, presumed to represent localized mobiUty in the noncrystalline regions of the silk fiber, and the other at 210°C, indicative of a partial melt or a glass transition. Data from thermal studies on B. mori silkworm cocoon silk indicate a glass-transition temperature, T, of 175°C and stability to around 250°C (37). The T for wild silkworm cocoon silks were slightly higher, from 160 to 210°C. 

Thermal and thermomechanical analyses44 are very important for determining die upper and lower usage temperature of polymeric materials as well as showing how they behave between diose temperature extremes. An especially useful thermal technique for polyurethanes is dynamic mechanical analysis (DMA).45 Uiis is used to study dynamic viscoelastic properties and measures die ability to... 

An associated technique which links thermal properties with mechanical ones is dynamic mechanical analysis (DMA). In this, a bar of the sample is typically fixed into a frame by clamping at both ends. It is then oscillated by means of a ceramic shaft applied at the centre. The resonant frequency and the mechanical damping exhibited by the sample are sensitive measurements of the mechanical properties of a polymer which can be made over a wide range of temperatures. The effects of compositional changes and methods of preparation can be directly assessed. DMA is assuming a position of major importance in the study of the physico-chemical properties of polymers and composites. 

Dynamic mechanical analysis (DMA) or dynamic mechanical thermal analysis (DMTA) provides a method for determining elastic and loss moduli of polymers as a function of temperature, frequency or time, or both [1-13]. Viscoelasticity describes the time-dependent mechanical properties of polymers, which in limiting cases can behave as either elastic solids or viscous liquids (Fig. 23.2). Knowledge of the viscoelastic behavior of polymers and its relation to molecular structure is essential in the understanding of both processing and end-use properties. 

Thermal analysis is a group of techniques in which a physical property of a substance is measured as a function of temperature when the sample is subjected to a controlled temperature program. Single techniques, such as thermogravimetry (TG), differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), dielectric thermal analysis, etc., provide important information on the thermal behaviour of materials. However, for polymer characterisation, for instance in case of degradation, further analysis is required, particularly because all of the techniques listed above mainly describe materials only from a physical point of view. A hyphenated thermal analyser is a powerful tool to yield the much-needed additional chemical information. In this paper we will concentrate on simultaneous thermogravimetric techniques. 

In addition, Seferis and Wedgewood have pointed out the many pitfalls that should be avoided when using dynamic mechanical analysis (DMA) to determine thermal properties in epoxy systems [134]. However, Sanz, et al. have investigated Tg of epoxy systems via DMA for a myriad of epoxy compositions and compiled large amounts of reasonable data using this technique [ 135]. Zukas has done the same using torsional braid analysis (TBA) on many epoxy systems and produced similar conclusions to Sanz [129]. 

The main experimental methodology used is to directly characterize the tensile properties of CNTs/polymer composites by conventional pull tests (e.g. with Instron tensile testers). Similarly, dynamic mechanical analysis (DMA) and thermal mechanical analysis (TMA) were also applied to investigate the tensile strength and tensile modulus. With these tensile tests, the ultimate tensile strength, tensile modulus and elongation to break of composites can be determined from the tensile strain-stress curve. 

Glass transition temperature, Tg, and storage modulus, E , were measured to explore how the pigment dispersion affects the material (i.e. cross-link density) and mechanical properties. Both Tg and E were determined from dynamic mechanical analysis method using a dynamic mechanical thermal analyzer (DMTA, TA Instruments RSA III) equipped with transient testing capability. A minimum of 3 to 4 specimens were analyzed from each sample. The estimated uncertainties of data are one-standard deviation. 

The analytical techniques used to study changes in physical properties with temperature are called thermal analysis techniques. They include thermogravimetric analysis (TGA), differential thermal analysis (DTA), differential scanning calorimetry (DSC), thermometric titration (TT), and direct injection enthalpimetry, dynamic mechanical analysis (DMA), and thermomechanical analysis (TMA). Thermal analysis techniques are used in... 

Thermal analysis has been used extensively to characterize resin composites, which have been under development for several decades. Conventional DSC is an excellent method for investigating polymerization of the composites [53-57]. The glass-transition temperature, which is highly relevant for the mechanical properties of the composites, can be readily foimd by dynamic mechanical analysis (DMA) [58-61], as shown in Figure 22, and by thermomechanical analysis (TMA) [62,63], where there is a discontinuity in the slopes of the plot of length change as a function of temperature below and above Tg. 

Plastics - Thermomechanical analysis (TMA) - Determination of linear thermal expansion coefficient and glass transition temperature Plastics - Thermomechanical analysis (TMA) - Determination of softening temperature Plastics - Determination of dynamic mechanical properties -General principles Plastics - Dynamic mechanical analysis - Determination of glass transition temperature Plastics - Dynamic mechanical analysis - Calibration... 

Thermal analysis is well suited for characterizing and identifying plastics, as their properties are temperature dependent. It involves methods in which the substance is subjected to a controlled temperature program and the changes in the physical and chemical properties are measured as a function of temperature or time. The ambient atmosphere also influences the properties of plastic. Thermal analysis comprises traditional techniques differential scanning calorimetry (DSC), differential thermal analysis, thermogravimetric analysis, thermomechanical analysis, and more recent methods pressure differential scanning calorimetry, dynamic mechanical analysis, and differential photocalorimetry. 

---