Silver neodecanoate

Electrical and Electronic Applications. Silver neodecanoate [62804-19-7] has been used in the preparation of a capacitor-end termination composition (110), lead and stannous neodecanoate have been used in circuit-board fabrication (111), and stannous neodecanoate has been used to form patterned semiconductive tin oxide films (112). The silver salt has also been used in the preparation of ceramic superconductors (113). Neodecanoate salts of barium, copper, yttrium, and europium have been used to prepare superconducting films and patterned thin-fHm superconductors. To prepare these materials, the metal salts are deposited on a substrate, then decomposed by heat to give the thin film (114—116) or by a focused beam (electron, ion, or laser) to give the patterned thin film (117,118). The resulting films exhibit superconductivity above Hquid nitrogen temperatures. 

Salts of neodecanoic acid have been used in the preparation of supported catalysts, such as silver neodecanoate for the preparation of ethylene oxide catalysts (119), and the nickel soap in the preparation of a hydrogenation catalyst (120). Metal neodecanoates, such as magnesium, lead, calcium, and zinc, are used to improve the adherence of plasticized poly(vinyl butyral) sheet to safety glass in car windshields (121). Platinum complexes using neodecanoic acid have been studied for antitumor activity (122). Neodecanoic acid and its esters are used in cosmetics as emoUients, emulsifiers, and solubilizers (77,123,124). Zinc or copper salts of neoacids are used as preservatives for wood (125). 

In this method, a metal oxide or hydroxide is slurried in an organic solvent, neodecanoic acid is slowly added, and the mixture is refluxed to remove the water. Salts that are basic can be prepared by using less than stoichiometric amounts of acid. This method has been used in the preparation of metal salts of silver (80) and vanadium (81). The third method of preparation is similar to the fusion process, the difference is the use of finely divided metal as the starting material instead of the metal oxide or hydroxide. This method has been appHed to the preparation of cobalt neodecanoate (82). Salts of tin (83) and antimony (84) have been prepared by the fusion method, starting with lower carboxyHc acids, then replacing these acids with neodecanoic acid. 

The metal salts of neodecanoic acid have found wide usage as driers for paints and inks (95,96). Metal neodecanoates that are used include silver (80), cobalt (82), and zirconium (79), along with lead, copper, manganese, and 2inc (see Driers and metallic soaps). 

---