Huang W, Kuhn IN, Tsung C-K, Zhang Y, Habas SE, Yang P, Somorjai GA (2008) Dendrimer templated synthesis of one nanometer Rh and Pt particles supported on mesoporous silica catalytic activity for ethylene and pyrrole hydrogenation. Nano Lett 8 2027... 

In particular, emphasis will be placed on the use of chemisorption to measure the metal dispersion, metal area, or particle size of catalytically active metals supported on nonreducible oxides such as the refractory oxides, silica, alumina, silica-alumina, and zeolites. In contrast to physical adsorption, there are no complete books devoted to this aspect of catalyst characterization however, there is a chapter in Anderson that discusses the subject. 

Raman spectroscopy has provided information on catalytically active transition metal oxide species (e. g. V, Nb, Cr, Mo, W, and Re) present on the surface of different oxide supports (e.g. alumina, titania, zirconia, niobia, and silica). The structures of the surface metal oxide species were reflected in the terminal M=0 and bridging M-O-M vibrations. The location of the surface metal oxide species on the oxide supports was determined by monitoring the specific surface hydroxyls of the support that were being titrated. The surface coverage of the metal oxide species on the oxide supports could be quantitatively obtained, because at monolayer coverage all the reactive surface hydroxyls were titrated and additional metal oxide resulted in the formation of crystalline metal oxide particles. The nature of surface Lewis and Bronsted acid sites in supported metal oxide catalysts has been determined by adsorbing probe mole-... 

The Zincke reaction has also been adapted for the solid phase. Dupas et al. prepared NADH-model precursors 58, immobilized on silica, by reaction of bound amino functions 57 with Zincke salt 8 (Scheme 8.4.19) for subsequent reduction to the 1,4-dihydropyridines with sodium dithionite. Earlier, Ise and co-workers utilized the Zincke reaction to prepare catalytic polyelectrolytes, starting from poly(4-vinylpyridine). Formation of Zincke salts at pyridine positions within the polymer was achieved by reaction with 2,4-dinitrochlorobenzene, and these sites were then functionalized with various amines. The resulting polymers showed catalytic activity in ester hydrolysis. ... 

Several aluminum- and titanium-based compounds have been supported on silica and alumina [53]. Although silica and alumina themselves catalyze cycloaddition reactions, their catalytic activity is greatly increased when they complex a Lewis acid. Some of these catalysts are among the most active described to date for heterogeneous catalysis of the Diels-Alder reactions of carbonyl-containing dienophiles. The Si02-Et2AlCl catalyst is the most efficient and can be... 

As described in the previous section, the silica-alumina catalyst covered with the silicalite membrane showed exceUent p-xylene selectivity in disproportionation of toluene [37] at the expense of activity, because the thickness of the sihcahte-1 membrane was large (40 pm), limiting the diffusion of the products. In addition, the catalytic activity of silica-alumina was not so high. To solve these problems, Miyamoto et al. [41 -43] have developed a novel composite zeohte catalyst consisting of a zeolite crystal with an inactive thin layer. In Miyamoto s study [41], a sihcahte-1 layer was grown on proton-exchanged ZSM-5 crystals (silicalite/H-ZSM-5) [42]. The silicalite/H-ZSM-5 catalysts showed excellent para-selectivity of >99.9%, compared to the 63.1% for the uncoated sample, and independent of the toluene conversion. 

This paper describes the catalytic activity of nickel phosphide supported on silica, alumina, and carbon-coated alumina in the hydrodesulfurization of 4,6-dimethyldibenzothiophene. The catalysts are made by the reduction of phosphate precursors. On the silica support the phosphate is reduced easily to form nickel phosphide with hi catalytic activity, but on the alumina support interactions between the phosphate and the alumina hinder the reduction. The addition of a carbon overlayer on alumina decreases the interactions and leads to the formation of an active phosphide phase. 

Stack and coworkers immobilized phenantrohne derivative 16 on micelle-templated silica SBA-15 (Scheme 8) [55,56]. The system showed more selective and efficient catalytic activity for olefin epoxidations with peracetic acid than the analogous homogeneous catalyst. 

Catalytic activities of the silica-supported vanadium oxides in either 3% methanol or in 5% O2 and 3% ethanol. Oxygen uptake was measured at 625 K. O2 and 3%... 

Thermal reduction at 623 K by means of CO is a common method of producing reduced and catalytically active chromium centers. In this case the induction period in the successive ethylene polymerization is replaced by a very short delay consistent with initial adsorption of ethylene on reduce chromium centers and formation of active precursors. In the CO-reduced catalyst, CO2 in the gas phase is the only product and chromium is found to have an average oxidation number just above 2 [4,7,44,65,66], comprised of mainly Cr(II) and very small amount of Cr(III) species (presumably as Q -Cr203 [66]). Fubini et al. [47] reported that reduction in CO at 623 K of a diluted Cr(VI)/Si02 sample (1 wt. % Cr) yields 98% of the silica-supported chromium in the +2 oxidation state, as determined from oxygen uptake measurements. The remaining 2 wt. % of the metal was proposed to be clustered in a-chromia-like particles. As the oxidation product (CO2) is not adsorbed on the surface and CO is fully desorbed from Cr(II) at 623 K (reduction temperature), the resulting catalyst acquires a model character in fact, the siliceous part of the surface is the same of pure silica treated at the same temperature and the anchored chromium is all in the divalent state. 

Zeolites have ordered micropores smaller than 2nm in diameter and are widely used as catalysts and supports in many practical reactions. Some zeolites have solid acidity and show shape-selectivity, which gives crucial effects in the processes of oil refining and petrochemistry. Metal nanoclusters and complexes can be synthesized in zeolites by the ship-in-a-bottle technique (Figure 1) [1,2], and the composite materials have also been applied to catalytic reactions. However, the decline of catalytic activity was often observed due to the diffusion-limitation of substrates or products in the micropores of zeolites. To overcome this drawback, newly developed mesoporous silicas such as FSM-16 [3,4], MCM-41 [5], and SBA-15 [6] have been used as catalyst supports, because they have large pores (2-10 nm) and high surface area (500-1000 m g ) [7,8]. The internal surface of the channels accounts for more than 90% of the surface area of mesoporous silicas. With the help of the new incredible materials, template synthesis of metal nanoclusters inside mesoporous channels is achieved and the nanoclusters give stupendous performances in various applications [9]. In this chapter, nanoclusters include nanoparticles and nanowires, and we focus on the synthesis and catalytic application of noble-metal nanoclusters in mesoporous silicas. 

X-Ray irradiation of quartz or silica particles induces an electron-trap lattice defect accompanied by a parallel increase in cytotoxicity (Davies, 1968). Aluminosilicate zeolites and clays (Laszlo, 1987) have been shown by electron spin resonance (e.s.r.) studies to involve free-radical intermediates in their catalytic activity. Generation of free radicals in solids may also occur by physical scission of chemical bonds and the consequent formation of dangling bonds , as exemplified by the freshly fractured theory of silicosis (Wright, 1950 Fubini et al., 1991). The entrapment of long-lived metastable free radicals has been shown to occur in the tar of cigarette smoke (Pryor, 1987). 

Fe/Ir catalysts In situ Fe and Ir Mossbauer spectroscopy of silica-supported Fe/Ir catalysts with different iron to iridium ratios following pretreatment in hydrogen show that the reduction of the Fe component is enhanced by the presence of Ir metal. The presence of Ir was found to increase the catalytic activity in hydrogenation of carbon monoxide and also to influence selectivity... 

Apart from a few reports" on solid acid catalyzed esterification of model compounds, to our knowledge utilization of solid catalysts for biodiesel production from low quality real feedstocks have been explored only recently. 12-Tungstophosphoric acid (TPA) impregnated on hydrous zirconia was evaluated as a solid acid catalyst for biodiesel production from canola oil containing up to 20 wt % free fatty acids and was found to give ester yield of 90% at 200°C. Propylsulfonic acid-functionalized mesoporous silica catalyst for esterification of FFA in flotation beef tallow showed a superior initial catalytic activity (90% yield) relative to a... 

Zinc chloride was used as a catalyst in the Friedel Crafts benzylation of benzenes in the presence of polar solvents, such as primary alcohols, ketones, and water.639 Friedel-Crafts catalysis has also been carried out using a supported zinc chloride reagent. Mesoporous silicas with zinc chloride incorporated have been synthesized with a high level of available catalyst. Variation in reaction conditions and relation of catalytic activity to pore size and volume were studied.640 Other supported catalytic systems include a zinc bromide catalyst that is fast, efficient, selective, and reusable in the /wa-bromination of aromatic substrates.641... 

---