ESA should be determined - most often this is done using Hxjpd charge. However, several different approaches can be used to obtain reliable estimate of ESA, especially if one deals with alloy catalysts. In case of single-crystal electrodes ESA is usually close to geometrical surface area, that is Rf is close to 1 (ideally equal to), hr the case of poly-oriented electrodes Rf can be of the order of 10. ... 

Mixtures of polymers at surfaces provide the interesting possibility of exploring polymer miscibility in two dimensions. Baglioni and co-workers [17] have shown that polymers having the same orientation at the interface are compatible while those having different orientations are not. Some polymers have their hydrophobic portions parallel to the surface, while others have a perpendicular disposition. The surface orientation effect is also present in mixtures of poly(methyl methacrylate), PMMA, and fatty acids. 

There have been many studies of the orientation of nitration in di- and poly-substituted derivatives of benzene, but in very few cases have... 

Polyimide. Polyimide is a biaxiaHy oriented high performance film that is tough, flexible, and temperature- and combustion-resistant. Its room temperature properties compare to poly(ethylene terephthalate), but it retains these good characteristics at temperatures above 400°C. Its electrical resistance is good and it is dimensionally stable. The principal detriment is fairly high moisture absorbance. The main uses are for electrical insulation, particularly where high temperatures are prevalent or ionizing radiation is a problem. The films may be coated to reduce water absorption and enhance... 

In conventional tenter orientation, the sequence of steps is as described above (MD—TD). In some cases it is advantageous to reverse the draw order (TD—MD) or to use multiple draw steps, eg, MD—TD—MD. These other techniques are used to produce "tensilized" films, where the MD tensile properties are enhanced by further stretching. The films are generally unbalanced in properties and in extreme cases may be fibrillated to give fiber-like elements for special textile appHcations. Tensilized poly(ethylene terephthalate) is a common substrate for audio and video magnetic tape and thermal transfer tape. 

BiaxiaHy oriented films have excellent tensile strength properties and good tear and impact properties. They are especially well regarded for their brilliance and clarity. Essentially all poly(ethylene terephthalate) film is biaxiaHy oriented, and more than 80% of polypropylene film is biaxiaHy oriented. Polystyrene film is oriented, and a lesser amount of polyethylene, polyamide, poly(vinyl chloride), and other polymers are so processed. Some of the specialty films, like polyimides (qv), are also oriented. 

Poly(vinyl fluoride) is available from Du Pont both as a resia and as transparent and pigmented films under the trademark Tedlar PVF film. Films are available ia nonoriented and oriented grade ia several tensile modifications and thicknesses, with either adherable or nonadherable release-grade surfaces. The 1992 prices ranged from 30 to 70/kg, vs 24 to 62/kg ia 1988. Prices for specially tailored films were significantly higher. 

Poly(vinylidene chloride). Poly(viayHdene chloride) [9002-85-1] (PVDC), most of which is produced by Dow Chemical, is best known in its saran or PVC-copolymerized form (see Vinylidene chloride and poly(VINYLIDENE chloride)). As solvent or emulsion coating, PVDC imparts high oxygen, fat, aroma, and water-vapor resistance to substrates such as ceUophane, oriented polypropylene, polyester, and nylon. 

In 1975, the synthesis of the first main-chain thermotropic polymers, three polyesters of 4,4 -dihydroxy-a,a -dimethylbenzalazine with 6, 8, and 10 methylene groups in the aHphatic chain, was reported (2). Shortly thereafter, at the Tennessee Eastman Co. thermotropic polyesters were synthesized by the acidolysis of poly(ethylene terephthalate) by/ -acetoxybenzoic acid (3). Copolymer compositions that contained 40—70 mol % of the oxybenzoyl unit formed anisotropic, turbid melts which were easily oriented. 

Soft-drink bottles made from poly(ethylene terephthalate) (PET) are usuady made by stretch-blow mol ding in a two-step process. Eirst, a test-tube-shaped preform is molded, which is then reheated to just above its glass-transition temperature, stretched, and blown. Stretching the PET produces biaxial orientation, which improves transparency, strength, and toughness of the botde (54,56). A one-step process is used for many custom containers that are injection stretch-blow molded. 

Thermoplasticity. High molecular weight poly(ethylene oxide) can be molded, extmded, or calendered by means of conventional thermoplastic processing equipment (13). Films of poly(ethylene oxide) can be produced by the blown-film extmsion process and, in addition to complete water solubiUty, have the typical physical properties shown in Table 3. Films of poly(ethylene oxide) tend to orient under stress, resulting in high strength in the draw direction. The physical properties, melting behavior, and crystallinity of drawn films have been studied by several researchers (14—17). 

With appropriately substituted oxetanes, aluminum-based initiators (321) impose a degree of microstmctural control on the substituted polyoxetane stmcture that is not obtainable with a pure cationic system. A polymer having largely the stmcture of poly(3-hydroxyoxetane) has been obtained from an anionic rearrangement polymerisation of glycidol or its trimethylsilyl ether, both oxirane monomers (322). Polymerisation-induced epitaxy can produce ultrathin films of highly oriented POX molecules on, for instance, graphite (323). Theoretical studies on the cationic polymerisation mechanism of oxetanes have been made (324—326). 

Poly(phenylene ether). The only commercially available thermoplastic poly(phenylene oxide) PPO is the polyether poly(2,6-dimethylphenol-l,4-phenylene ether) [24938-67-8]. PPO is prepared by the oxidative coupling of 2,6-dimethylphenol with a copper amine catalyst (25). Usually PPO is blended with other polymers such as polystyrene (see PoLYETPiERS, Aromatic). However, thermoplastic composites containing randomly oriented glass fibers are available. 

Biaxial orientation effects are of importance in the manufacture of films and sheet. Biaxially stretched poly(ethylene terephthalate) (e.g. Melinex),... 

Much of the success of the poly(ethylene terephthalate) bottle has arisen from the control of the biaxial orientation that occurs during manufacture to give a product both strong and of low gas permeability. 

In the case of polymer molecules where the dipoles are not directly attached to the main chain, segmental movement of the chain is not essential for dipole polarisation and dipole movement is possible at temperatures below the glass transition temperature. Such materials are less effective as electrical insulators at temperatures in the glassy range. With many of these polymers, e.g., poly(methyl methacrylate), there are two or more maxima in the power factor-temperature curve for a given frequency. The presence of two such maxima is due to the different orientation times of the dipoles with and without associated segmental motion of the main chain. 

---