Poly . glass transition temperature

T is the glass-transition temperature at infinite molecular weight and is the number average molecular weight. The value of k for poly(methyl methacrylate) is about 2 x 10 the value for acrylate polymers is approximately the same (9). A detailed discussion on the effect of molecular weight on the properties of a polymer may be found in Reference 17. 

A plasticizer is a substance the addition of which to another material makes that material softer and more flexible. This broad definition encompasses the use of water to plasticize clay for the production of pottery, and oils to plasticize pitch for caulking boats. A more precise definition of plasticizers is that they are materials which, when added to a polymer, cause an increase in the flexibiUty and workabiUty, brought about by a decrease in the glass-transition temperature, T, of the polymer. The most widely plasticized polymer is poly(vinyl chloride) (PVC) due to its excellent plasticizer compatibility characteristics, and the development of plasticizers closely follows the development of this commodity polymer. However, plasticizers have also been used and remain in use with other polymer types. 

Soft-drink bottles made from poly(ethylene terephthalate) (PET) are usuady made by stretch-blow mol ding in a two-step process. Eirst, a test-tube-shaped preform is molded, which is then reheated to just above its glass-transition temperature, stretched, and blown. Stretching the PET produces biaxial orientation, which improves transparency, strength, and toughness of the botde (54,56). A one-step process is used for many custom containers that are injection stretch-blow molded. 

Fig. 2. Glass-transition temperature—molecular weight relationship for poly(ethylene oxide) (-) represents classical T —mol wt relationship Q, data from...

Fig. 2. Glass-transition temperature, T, for two commercially available, miscible blend systems (a) poly(phenylene oxide) (PPO) and polystyrene (PS) (42) ...

Carbon Cha.in Backbone Polymers. These polymers may be represented by (4) and considered derivatives of polyethylene, where n is the degree of polymeriza tion and R is (an alkyl group or) a functional group hydrogen (polyethylene), methyl (polypropylene), carboxyl (poly(acryhc acid)), chlorine (poly(vinyl chloride)), phenyl (polystyrene) hydroxyl (poly(vinyl alcohol)), ester (poly(vinyl acetate)), nitrile (polyacrylonitrile), vinyl (polybutadiene), etc. The functional groups and the molecular weight of the polymers, control thek properties which vary in hydrophobicity, solubiUty characteristics, glass-transition temperature, and crystallinity. 

The thermal glass-transition temperatures of poly(vinyl acetal)s can be determined by dynamic mechanical analysis, differential scanning calorimetry, and nmr techniques (31). The thermal glass-transition temperature of poly(vinyl acetal) resins prepared from aliphatic aldehydes can be estimated from empirical relationships such as equation 1 where OH and OAc are the weight percent of vinyl alcohol and vinyl acetate units and C is the number of carbons in the chain derived from the aldehyde. The symbols with subscripts are the corresponding values for a standard (s) resin with known parameters (32). The formula accurately predicts that resin T increases as vinyl alcohol content increases, and decreases as vinyl acetate content and aldehyde carbon chain length increases. 

As shown in Table 3, the glass-transition temperatures of the amorphous straight-chain alkyl vinyl ether homopolymers decrease with increasing length of the side chain. Also, the melting points of the semicrystalline poly(alkyl vinyl ether)s increase with increasing side-chain branching. 

Table 3. Glass-Transition Temperature of Amorphous Poly(Vinyl Ether)s and Melting Points of Crystalline Poly(Vinyl Ether)s ...

Stereoregular poly-/n7 j -l,4-chloroprene (57) and poly-i7j -l,4-chloroprene (58) have been synthesized. The cis stmcture has a higher glass-transition temperature, and despite the large number of inverted units, a relatively high melting point. 

Other Polyimides. In 1979, Rohm Haas introduced Kamax resin, which was thought to be an /V-methylamine imidization product of poly(methyl methacrylate) (118). The product was then withdrawn, but was reintroduced in the late 1980s. The partly imidized resins are similar to poly(methyl methacrylate) but have a higher glass-transition temperature. 

When dipoles are directly attached to the chain their movement will obviously depend on the ability of chain segments to move. Thus the dipole polarisation effect will be much less below the glass transition temperature, than above it Figure 6.4). For this reason unplasticised PVC, poly(ethylene terephthalate) and the bis-phenol A polycarbonates are better high-frequency insulators at room temperature, which is below the glass temperature of each of these polymers, than would be expected in polymers of similar polarity but with the polar groups in the side chains. 

In the case of polymer molecules where the dipoles are not directly attached to the main chain, segmental movement of the chain is not essential for dipole polarisation and dipole movement is possible at temperatures below the glass transition temperature. Such materials are less effective as electrical insulators at temperatures in the glassy range. With many of these polymers, e.g., poly(methyl methacrylate), there are two or more maxima in the power factor-temperature curve for a given frequency. The presence of two such maxima is due to the different orientation times of the dipoles with and without associated segmental motion of the main chain. 

Poly(vinyl acetate) is too soft and shows excessive cold flow for use in moulded plastics. This is no doubt associated with the fact that the glass transition temperature of 28°C is little above the usual ambient temperatures and in fact in many places at various times the glass temperature may be the lower. It has a density of 1.19 g/cm and a refractive index of 1.47. Commercial polymers are atactic and, since they do not crystallise, transparent (if free from emulsifier). They are successfully used in emulsion paints, as adhesives for textiles, paper and wood, as a sizing material and as a permanent starch . A number of grades are supplied by manufacturers which differ in molecular weight and in the nature of comonomers (e.g. vinyl maleate) which are commonly used (see Section 14.4.4)... 

Whilst the Tg of poly(dimethylsiloxane) rubbers is reported to be as low as -123°C they do become stiff at about -60 to -80°C due to some crystallisation. Copolymerisation of the dimethyl intermediate with a small amount of a dichlorodiphenylsilane or, preferably, phenylmethyldichlorosilane, leads to an irregular structure and hence amorphous polymer which thus remains a rubber down to its Tg. Although this is higher than the Tg of the dimethylsiloxane it is lower than the so that the polymer remains rubbery down to a lower temperature (in some cases down to -100°C). The Tg does, however, increase steadily with the fraction of phenylsiloxane and eventually rises above that of the of the dimethylsilicone rubber. In practice the use of about 10% of phenyldichlorosilane is sufficient to inhibit crystallisation without causing an excess rise in the glass transition temperature. As with the polydimethylsilox-anes, most methylphenyl silicone rubbers also contain a small amount of vinyl groups. 

Plasticizers are substances (usually low molecular weight diluents) that are incorporated into polymeric materials to improve their workability and increase flexibility. Polymeric plasticizers are low glass transition temperature (Tg) poly-... 

---