Noble metal coatings hardness

Under severe conditions and at high temperatures, noble metal films may fail by oxidation of the substrate base metal through pores in the film. Improved life may be achieved by first imposing a harder noble metal film, eg, rhodium or platinum—iridium, on the substrate metal. For maximum adhesion, the metal of the intermediate film should ahoy both with the substrate metal and the soft noble-metal lubricating film. This sometimes requires more than one intermediate layer. For example, silver does not ahoy to steel and tends to lack adhesion. A flash of hard nickel bonds weh to the steel but the nickel tends to oxidize and should be coated with rhodium before applying shver of 1—5 p.m thickness. This triplex film then provides better adhesion and gready increased corrosion protection. 

Cladding may be less expensive than selective electro deposition when coatings greater than 1 p.m of a noble metal are required, but may be more expensive than electro deposition for thinner coatings. Selective techniques are most easily used for sheet metal substrates that are to be machine stamped and formed into contacts. Clad noble metals are considerably more ductile (and less hard) than comparable electro deposits and, therefore, are better suited to forming operations. Contacts that are made into separate parts from rod by screw machining are usually coated on all exposed surfaces by barrel electroplating. 

---