Nickel-base alloys stress-corrosion cracking

Many instances of intergranular stress corrosion cracking (IGSCC) of stainless steel and nickel-based alloys have occurred in the reactor water systems of BWRs. IGSCC, first observed in the recirculation piping systems (21) and later in reactor vessel internal components, has been observed primarily in the weld heat-affected zone of Type 304 stainless steel. [Pg.195]

Flange face areas experience stagnant conditions. Additionally, some gasket materials, such as asbestos fiber, contain leachable chloride ions. This creates crevice and stress corrosion cracking problems on sealing surfaces. Where necessary, flange faces that are at risk can be overlaid with nickel-based alloys. Alternatively, compressed asbestos fiber gaskets shrouded in PTFE may be used. [Pg.904]

With regard to stress-corrosion cracking in the Ni-Cr-Fe system, including both nickel-base alloys and stainless steels, a vast number of papers has been published. A detailed review of work published before 1969 is available and the authors have since published additional data . [Pg.794]

Replacing some of the nickel with iron produces a family of alltws with intermediate corrosion resistance between stainless steels and the Ni-Cr-Mo alloys. Alloys such as Incoloy 825 and Hastelloy G-3 and G-30 are in this family. Incoloy 825 has 40 percent Ni, 21 percent Cr, 3 percent Mo, and 2.25 percent Cu. Hastelloy G-3 contains 44 percent Ni, 22 percent Cr, 6.5 percent Mo, and 0.05 percent C maximum. These alloys have extensive applications in sulfuric acid systems. Because of their increased nickel and molybdenum contents they are more tolerant of chloride-ion contamination than are standard stainless steels. The nickel content decreases the risk of stress-corrosion cracking molybdenum improves resistance to crevice corrosion and pitting. Many of the nickel-based alloys are proprietary and are coverecf by the following specifications ... [Pg.33]

One material that has wide application in the systems of DOE facilities is stainless steel. There are nearly 40 standard types of stainless steel and many other specialized types under various trade names. Through the modification of the kinds and quantities of alloying elements, the steel can be adapted to specific applications. Stainless steels are classified as austenitic or ferritic based on their lattice structure. Austenitic stainless steels, including 304 and 316, have a face-centered cubic structure of iron atoms with the carbon in interstitial solid solution. Ferritic stainless steels, including type 405, have a body-centered cubic iron lattice and contain no nickel. Ferritic steels are easier to weld and fabricate and are less susceptible to stress corrosion cracking than austenitic stainless steels. They have only moderate resistance to other types of chemical attack. [Pg.34]

An example of a nickel-based alloy that is resistant to stress-corrosion cracking is inconel. Inconel is composed of 72% nickel, 14-17% chromium, 6-10% iron, and small amounts of manganese, carbon, and copper. [Pg.86]

Nickel and nickel-based alloys play a major role in the chemical process industry because of their excellent corrosion resistance and their low susceptibihty to stress corrosion cracking. [Pg.86]

Schmitt [52] reviewed the effect of elemental sulfur on corrosion of construction materials (carbon steels, ferric steels, austenitic steels, ferritic-austenitic steels (duplex steels), nickel and cobalt-based alloys and titanium. Wet elemental sulfur in contact with iron is aggressive and can result in the formation of iron sulfides or in stress corrosion cracking. Iron sulfides containing elemental sulfur initiate corrosion only when the elemental sulfur is in direct contact with the sulfide-covered metal. Iron sulfides are highly electron conductive and serve to transport electrons from the metal to the elemental sulfur. The coexistence of hydrogen sulfide and elemental sulfur in aqueous systems, that is, sour gases and oils, causes crevice corrosion rates of... [Pg.673]

D. E, Jordan, Stress-Corrosion Cracking of Nickel-Base Alloy Weldments, International Institute of Welding Annual Assembly, Montreal (1990). [Pg.1010]

Kane, R. D., Greer, J. B., Hanson, J. R., et tJ., Stress Corrosion Cracking of Nickel Base Alloys in Chloride Containing Environment, Paper 174, CORROSION/79, NACE, Atlanta, GA, April 1979. [Pg.301]


See other pages where Nickel-base alloys stress-corrosion cracking is mentioned: [Pg.1155]    [Pg.1188]    [Pg.124]    [Pg.136]    [Pg.2417]    [Pg.905]    [Pg.144]    [Pg.1308]    [Pg.1102]    [Pg.3]    [Pg.136]    [Pg.65]    [Pg.2172]    [Pg.2679]    [Pg.592]    [Pg.632]    [Pg.366]    [Pg.120]    [Pg.2656]    [Pg.2421]    [Pg.76]    [Pg.83]    [Pg.403]    [Pg.410]    [Pg.570]    [Pg.647]    [Pg.378]    [Pg.1131]    [Pg.172]    [Pg.187]    [Pg.378]    [Pg.1781]    [Pg.120]    [Pg.190]    [Pg.191]    [Pg.143]    [Pg.593]   


SEARCH



Alloying nickel

Alloying nickel-based alloys

Alloys based

Corrosion alloying

Corrosion nickel-based alloys

Corrosive stress

Cracking alloy

Nickel alloys cracking

Nickel corrosion

Nickel-base alloys

Nickel-base alloys corrosion

Nickel-based alloys

Stress crack

Stress crack corrosion

Stress nickel-based alloys

Stress-corrosion cracking

© 2024 chempedia.info