Modified polyphenylene oxide mechanical

Modified-polyphenylene oxide (or ether) is a blend of high impact polystyrene (PS) and polyphenylene oxide (PPO), plus thermal stabilizers and a triarylphosphate flame retardant. Studies of the mechanism of the flame retardant in modified-polyphenylene oxide have shown some evidence for both solid phase and vapor phase inhibition (4). Indeed, one is always interested to know whether flame retardant action is on the solid or vapor phase. 

TABLE 3-83. PHYSICAL AND MECHANICAL PROPERTIES OF MODIFIED POLYPHENYLENE OXIDE... 

Polyphenylene oxide (PPO) or Polyphenylene ether (PPE) is an amorphous polymer with a softening temperature of about 210 °C. To improve its processability it is mostly blended with PS (modified PPE, e.g. Noryl ), which is at the cost of its heat distortion temperature. The properties are excellent the applications are mainly in fine-mechanical construction, in automotive parts, in household equipment etc. 

Wei Wei, G. X., Sue, H.-J. Fracture mechanisms in preformed polyphenylene oxide particle-modified bismaleimide resins. J. Appl. Polym. Sci. 74 (1999) 2539-2545. 

A modified epoxy matrix for Kevlar FRP composites was produced from ep>oxy/polyphenylene oxide (PPO) blends cured with multifunctional cyanate ester resin [94]. The effects of the PPO content on the cme behavior in the cyanate ester-cmed epoxy were investigated with FTIR. The cme reaction in the ep>oxy/PPO blends was faster than that of the neat epoxy system. FTIR analysis revealed that the cyanate fimctional group reactions were accelerated by adding PPO and that several co-reactions had occurred. Thermal mechanical analysis showed that the thermal stability of the epoxy/PPO matrix is improved by adding PPO. In the respective compursites, the ISS values between Kevlar fiber and the epoxy/PPO blends are almost the same as those between Kevlar fiber and neat epoxy. The ILSS in the respective laminates increases with the PPO content, which was attributed to an increase in the composites ductility. 

Property data for GRTP s are presented in two major breakouts. In the first breakout, the basic resins—styrene acrylonitrile (SAN), polycarbonate, polysulfone, polyacetal, polypropylene, polyphenylene oxide (PPG), nylon, modified PPG, and polyvinyl chloride—are treated as the independent variables and the physical, mechanical, electrical, thermal, chemical, and weathering characteristics are treated as the dependent variables. In the second breakout, the functional relationships are reversed, te., the properties are the independent variable and the resins are the dependent variable. ASTM test methods by which the physical values were determined are listed. The. physical data versus resins are presented in both tabular and graphic form. 

---