Template metal oxides

According to Ref. [12], template for synthesis of nanomaterials is defined as a central structure within which a network forms in such a way that removal of this template creates a filled cavity with morphological or stereochemical features related to those of the template. The template synthesis was applied for preparation of various nanostructures inside different three-dimensional nanoporous structures. Chemically, these materials are presented by polymers, metals, oxides, carbides and other substances. Synthetic methods include electrochemical deposition, electroless deposition, chemical polymerization, sol-gel deposition and chemical vapor deposition. These works were reviewed in Refs. [12,20]. An essential feature of this... 

Porous aluminum oxide can be used as a template for the production of nanowires and nanotubes. For example, metals can be deposited on the pore walls by the following procedures deposition from the gas phase, precipitation from solution by electrochemical reduction or with chemical reducing agents, or by pyrolysis of substances that have previously been introduced into the pores. Wires are obtained when the pore diameters are 25 nm, and tubes from larger pores the walls of the tubes can be as thin as 3 nm. For example, nanowires and nanotubes of nickel, cobalt, copper or silver can be made by electrochemical deposition. Finally, the aluminum oxide template can be removed by dissolution with a base. 

Sadakane, M., Asanuma, T., Kubo, J. et al. (2005) Facile procedure to prepare three-dimensionally ordered macroporous (3DOM) perovskite-type mixed metal oxides by colloidal crystal templating method, Chem. Mater. 17, 3546. 

Yang, P. D. Zhao, D. Y. Margolese, D. I. Chmelka, B. F. Stucky, G. D. 1999. Block copolymer templating syntheses of mesoporous metal oxides with large ordering lengths and semicrystalline framework. Chem. Mater. 11 2813-2826. 

In 1990, Choudary [139] reported that titanium-pillared montmorillonites modified with tartrates are very selective solid catalysts for the Sharpless epoxidation, as well as for the oxidation of aromatic sulfides [140], Unfortunately, this research has not been reproduced by other authors. Therefore, a more classical strategy to modify different metal oxides with histidine was used by Moriguchi et al. [141], The catalyst showed a modest e.s. for the solvolysis of activated amino acid esters. Starting from these discoveries, Morihara et al. [142] created in 1993 the so-called molecular footprints on the surface of an Al-doped silica gel using an amino acid derivative as chiral template molecule. After removal of the template, the catalyst showed low but significant e.s. for the hydrolysis of a structurally related anhydride. On the same fines, Cativiela and coworkers [143] treated silica or alumina with diethylaluminum chloride and menthol. The resulting modified material catalyzed Diels-Alder reaction between cyclopentadiene and methacrolein with modest e.s. (30% e.e.). As mentioned in the Introduction, all these catalysts are not yet practically important but rather they demonstrate that amorphous metal oxides can be modified successfully. 

It is important to note that in addition to microporous solids, other chemical systems have been used to template the growth of nanomaterials. For example, emulsions have been used to pattern both the pores in titania [14] and the packing of latex particles [46]. Reversed micelles have also been used as patterning agents. Examples include the syntheses of super-paramagnetic ferrite nanoparticles [15] and BaC03 nanowires [47]. Finally, carbon nanotubules have also been used as templates [16,48,49]. A variety of nanomaterials including metal oxides [16,48,49] and GaN have been synthesized inside such tubules [50]. 

Since this initial work there has been a plethora of literature on mesoporous molecular sieves. In addition to the silica and aluminosilicate frameworks similar mesoporous structures of metal oxides now include the oxides of Fe, Ti, V, Sb, Zr, Mn, W and others. Templates have been expanded to include nonionic, neutral surfactants and block copolymers. Pore sizes have broadened to the macroscopic size, in excess of 40 nm in diameter. A recent detailed review of the mesoporous molecular sieves is given in ref [73]. Vartuli and Degnan have reported a Mobil M41S mesoporous-based catalyst in commercial use, but to date the application has not been publicly identified.[74]. 

In the following section, we restrict our discussion to templated mesoporous solids that are of potential interest as battery electrodes, including many transition-metal oxides and carbon. This slice of the literature still points the interested reader to many articles on the synthesis and physical characterization of relevant mesoporous materials. A much smaller number of electrochemical studies with templated mesoporous electrodes have been published, and these studies in particular will be noted. 

There are, however, two limitations associated with preparation and application of zeolite based catalysts. First, hydrothermal syntheses Umit the extent to which zeolites can be tailored with respect to intended appUcation. Many recipes involving metals that are interesting in terms of catalysis lead to disruption of the balance needed for template-directed pore formation rather than phase separation that produces macroscopic domains of zeoUte and metal oxide without incorporating the metal into the zeohte. When this happens, the benefits of catalysis in confined chambers are lost. Second, hydrothermal synthesis of zeoHtic, silicate based soHds is also currently Hmited to microporous materials. While the wonderfully useful molecular sieving abihty is derived precisely from this property, it also Hmits the sizes of substrates that can access catalyst sites as weU as mass transfer rates of substrates and products to and from internal active sites. 

---