Mechanical property measurement torsion test

Mechanical Properties. Dynamic mechanical properties were determined both in torsion and tension. For torsional modulus measurements, a rectangular sample with dimensions of 45 by 12.5 mm was cut from the extruded sheet. Then the sample was mounted on the Rheometrics Mechanical Spectrometer (RMS 800) using the solid fixtures. The frequency of oscillation was 10 rad/sec and the strain was 0.1% for most samples. The auto tension mode was used to keep a small amount of tension on the sample during heating. In the temperature sweep experiments the temperature was raised at a rate of 5°C to 8°C per minute until the modulus of a given sample dropped remarkably. The elastic component of the torsional modulus, G, of the samples was measured as a function of temperature. For the dynamic tensile modulus measurements a Rheometrics Solid Analyzer (RSA II) was used. The frequency used was 10 Hz and the strain was 0.5 % for all tests. 

D5279-95 Standard Test Method for Measuring the Dynamic Mechanical Properties of Plastics in Torsion D5592-94 Standard Guide for Material Properties Needed in Engineering Design Using Plastics... 

Mechanical Properties. The measurement of mechanical properties is concerned with load-deformation or stress-strain relationships. Forces may be applied as tension, shear, torsion, and compression and bending. Stress is the force divided by the cross-sectional area of the sample. Strain is the change in a physical dimension of the sample divided by the original dimension. The ratio of the stress to strain is referred to the modulus. Stress maybe applied continuously or periodically at varying rates for dilferent tests. The characteristic stress-strain curve, stress relaxation, or impact behavior is very important in determining the applications and limitations of a polsrmer. 

This second group of tests is designed to measure the mechanical response of a substance to applied vibrational loads or strains. Both temperature and frequency can be varied, and thus contribute to the information that these tests can provide. There are a number of such tests, of which the major ones are probably the torsion pendulum and dynamic mechanical thermal analysis (DMTA). The underlying principles of these dynamic tests have been covered earlier. Such tests are used as relatively rapid methods of characterisation and evaluation of viscoelastic polymers, including the measurement of T, the study of the curing characteristics of thermosets, and the study of polymer blends and their compatibility. They can be used in essentially non-destructive modes and, unlike the majority of measurements made in non-dynamic tests, they yield data on continuous properties of polymeric materials, rather than discontinuous ones, as are any of the types of strength which are measured routinely. 

Dynamic Mechanical Testing - Film properties such as impact resistance and the cure response of thermosetting resins are conveniently investigated by dynamic measurements in which an oscillatory or torsional strain is applied to the sample with the stress and phase difference between the applied strain and measured stress being determined. In the present study, a Rheovibron Viscoelastometer was used which employed a sinusoidal strain at a... 

---