Glass Transition and Other Transitions

Differential scanning calorimetry, thermomechanical analysis, dynamic mechanical analysis, differential thermal analysis, dielectric thermal analysis, infrared and NMR spectroscopy, are some of the instrumental techniques that have been applied to the determination of glass transition and other transition temperatures in polymers (Chapter 13). 

In the following section several types of instrumentation used to measure the glass transition and other transitions are discussed. 

The glass transition and other transitions in polymers can be observed experimentally by measuring any one of several basic thermodynamic, physical, mechanical, or electrical properties as a function of temperature. Recall that in first-order transitions such as melting and boiling, there is a discontinuity in the volume-temperature plot. For second-order transitions such as the glass transition, a change in slope occurs, as illustrated in Figure 8.5 (9). 

Figure 4.3b is a schematic representation of the behavior of S and V in the vicinity of T . Although both the crystal and liquid phases have the same value of G at T , this is not the case for S and V (or for the enthalpy H). Since these latter variables can be written as first derivatives of G and show discontinuities at the transition point, the fusion process is called a first-order transition. Vaporization and other familiar phase transitions are also first-order transitions. The behavior of V at Tg in Fig. 4.1 shows that the glass transition is not a first-order transition. One of the objectives of this chapter is to gain a better understanding of what else it might be. We shall return to this in Sec. 4.8. 

In other work, the impact of thermal processing on linewidth variation was examined and interpreted in terms of how the resist s varying viscoelastic properties influence acid diffusion (105). The authors observed two distinct behaviors, above and below the resist film s glass transition. For example, a plot of the rate of deprotection as a function of post-exposure processing temperature show a change in slope very close to the T of the resist. Process latitude was improved and linewidth variation was naininiized when the temperature of post-exposure processing was below the film s T. 

The glass-transition temperature, T, of dry polyester is approximately 70°C and is slightly reduced ia water. The glass-transitioa temperatures of copolyesters are affected by both the amouat and chemical nature of the comonomer (32,47). Other thermal properties, including heat capacity and thermal conductivity, depend on the state of the polymer and are summarized ia Table 2. 

Properties. One of the characteristic properties of the polyphosphazene backbone is high chain dexibility which allows mobility of the chains even at quite low temperatures. Glass-transition temperatures down to —105° C are known with some alkoxy substituents. Symmetrically substituted alkoxy and aryloxy polymers often exhibit melting transitions if the substituents allow packing of the chains, but mixed-substituent polymers are amorphous. Thus the mixed substitution pattern is deUberately used for the synthesis of various phosphazene elastomers. On the other hand, as with many other flexible-chain polymers, glass-transition temperatures above 100°C can be obtained with bulky substituents on the phosphazene backbone. 

A plasticizer is a substance the addition of which to another material makes that material softer and more flexible. This broad definition encompasses the use of water to plasticize clay for the production of pottery, and oils to plasticize pitch for caulking boats. A more precise definition of plasticizers is that they are materials which, when added to a polymer, cause an increase in the flexibiUty and workabiUty, brought about by a decrease in the glass-transition temperature, T, of the polymer. The most widely plasticized polymer is poly(vinyl chloride) (PVC) due to its excellent plasticizer compatibility characteristics, and the development of plasticizers closely follows the development of this commodity polymer. However, plasticizers have also been used and remain in use with other polymer types. 

The iatroduction of a plasticizer, which is a molecule of lower molecular weight than the resia, has the abiUty to impart a greater free volume per volume of material because there is an iucrease iu the proportion of end groups and the plasticizer has a glass-transition temperature, T, lower than that of the resia itself A detailed mathematical treatment (2) of this phenomenon can be carried out to explain the success of some plasticizers and the failure of others. Clearly, the use of a given plasticizer iu a certain appHcation is a compromise between the above ideas and physical properties such as volatiUty, compatibihty, high and low temperature performance, viscosity, etc. This choice is appHcation dependent, ie, there is no ideal plasticizer for every appHcation. 

Polycarbonates are an unusual and extremely useful class of polymers. The vast majority of polycarbonates are based on bisphenol A [80-05-7] (BPA) and sold under the trade names Lexan (GE), Makrolon (Bayer), CaUbre (Dow), and Panlite (Idemitsu). BPA polycarbonates [25037-45-0] having glass-transition temperatures in the range of 145—155°C, are widely regarded for optical clarity and exceptional impact resistance and ductiUty at room temperature and below. Other properties, such as modulus, dielectric strength, or tensile strength are comparable to other amorphous thermoplastics at similar temperatures below their respective glass-transition temperatures, T. Whereas below their Ts most amorphous polymers are stiff and britde, polycarbonates retain their ductiUty. 

Polycarbonate—polyester blends were introduced in 1980, and have steadily increased sales to a volume of about 70,000 t. This blend, which is used on exterior parts for the automotive industry, accounting for 85% of the volume, combines the toughness and impact strength of polycarbonate with the crystallinity and inherent solvent resistance of PBT, PET, and other polyesters. Although not quite miscible, polycarbonate and PBT form a fine-grained blend, which upon analysis shows the glass-transition temperature of the polycarbonate and the melting point of the polyester. 

Other Properties. The glass-transition temperature for PPO is 190 K and varies htde with molecular weight (182). The temperature dependence of the diffusion coefficient of PPO in the undiluted state has been measured (182). 

---