Corrosion/cracking

FlOiei Evaluation of techniques for assessing corrosion cracking In dissimilar metal welds Dr D.R. Tice AEA Technology... 

The Institute has many-year experience of investigations and developments in the field of NDT. These are, mainly, developments which allowed creation of a series of eddy current flaw detectors for various applications. The Institute has traditionally studied the physico-mechanical properties of materials, their stressed-strained state, fracture mechanics and developed on this basis the procedures and instruments which measure the properties and predict the behaviour of materials. Quite important are also developments of technologies and equipment for control of thickness and adhesion of thin protective coatings on various bases, corrosion control of underground pipelines by indirect method, acoustic emission control of hydrogen and corrosion cracking in structural materials, etc. 

A process involving combined corrosion and straining of the metal due to residual or applied stresses. The occurrence of stress corrosion cracking is highly specific only particular metal/environment systems will crack. 

The appearance of stress corrosion cracking may be either intergranular or transgranular in nature. 

Stainless steel alloys show exceUent corrosion resistance to HCl gas up to a temperature of 400°C. However, these are normally not recommended for process equipment owing to stress corrosion cracking during periods of cooling and shut down. The corrosion rate of Monel is similar to that of mild steel. Pure (99.6%) nickel and high nickel alloys such as Inconel 600 can be used for operation at temperatures up to 525°C where the corrosion rate is reported to be about 0.08 cm/yr (see Nickel and nickel alloys). 

Duplex stainless steels (ca 4% nickel, 23% chrome) have been identified as having potential appHcation to nitric acid service (75). Because they have a lower nickel and higher chromium content than typical austenitic steels, they provide the ductabdity of austenitic SS and the stress—corrosion cracking resistance of ferritic SS. The higher strength and corrosion resistance of duplex steel offer potential cost advantages as a material of constmction for absorption columns (see CORROSION AND CORROSION CONTROL). 

Titanium is resistant to nitric acid from 65 to 90 wt % and ddute acid below 10 wt %. It is subject to stress—corrosion cracking for concentrations above 90 wt % and, because of the potential for a pyrophoric reaction, is not used in red filming acid service. Tantalum exhibits good corrosion resistance to nitric acid over a wide range of concentrations and temperatures. It is expensive and typically not used in conditions where other materials provide acceptable service. Tantalum is most commonly used in appHcations where the nitric acid is close to or above its normal boiling point. 

Stress corrosion cracking, prevalent where boiling occurs, concentrates corrosion products and impurity chemicals, namely in the deep tubesheet crevices on the hot side of the steam generator and under deposits above the tubesheet. The cracking growth rates increase rapidly at both high and low pH. Either of these environments can exist depending on the type of chemical species present. 

Many instances of intergranular stress corrosion cracking (IGSCC) of stainless steel and nickel-based alloys have occurred in the reactor water systems of BWRs. IGSCC, first observed in the recirculation piping systems (21) and later in reactor vessel internal components, has been observed primarily in the weld heat-affected zone of Type 304 stainless steel. 

Stress Corrosion Cracking of Ahoy 600," Report NP-2114-SR, Electric Power Research Institute, Palo Alto, Calif., Nov. 1981. 

Final Purification. Oxygen containing compounds (CO, CO2, H2O) poison the ammonia synthesis catalyst and must be effectively removed or converted to inert species before entering the synthesis loop. Additionally, the presence of carbon dioxide in the synthesis gas can lead to the formation of ammonium carbamate, which can cause fouHng and stress-corrosion cracking in the compressor. Most plants use methanation to convert carbon oxides to methane. Cryogenic processes that are suitable for purification of synthesis gas have also been developed. 

R. J. I In dinger and R. M. Curran, Experience with Stress Corrosion Cracking in Earge Steam Turbines, Corrosion 81, National Association of Corrosion Engineers, Toronto, Ontario, Canada, 1981. 

A. Ptakash,D. K. Kim, and R. M. Shemeashi, International Conference on Fatigue, Corrosion Cracking Fracture Mechanical andFailure Analysis, ASM... 

Stress Corrosion Crocking. Stress corrosion cracking occurs from the combined action of corrosion and stress. The corrosion may be initiated by improper chemical cleaning, high dissolved oxygen levels, pH excursions in the boiler water, the presence of free hydroxide, and high levels of chlorides. Stresses are either residual in the metal or caused by thermal excursions. Rapid startup or shutdown can cause or further aggravate stresses. Tube failures occur near stressed areas such as welds, supports, or cold worked areas. 

Localized corrosion, which occurs when the anodic sites remain stationary, is a more serious industrial problem. Forms of localized corrosion include pitting, selective leaching (eg, dezincification), galvanic corrosion, crevice or underdeposit corrosion, intergranular corrosion, stress corrosion cracking, and microbiologicaHy influenced corrosion. Another form of corrosion, which caimot be accurately categorized as either uniform or localized, is erosion corrosion. 

Corrosion control requires a change in either the metal or the environment. The first approach, changing the metal, is expensive. Also, highly alloyed materials, which are resistant to general corrosion, are more prone to failure by localized corrosion mechanisms such as stress corrosion cracking. 

Zirconium resists attack by nitric acid at concentrations up to 70 wt % and up to 250°C. Above concentrations of 70 wt %, zirconium is susceptible to stress-corrosion cracking in welds and points of high sustained tensile stress (29). Otherwise, zirconium is resistant to nitric acid concentrations of 70—98 wt % up to the boiling point. 

Materials of Construction. GeneraHy, carbon steel is satisfactory as a material of construction when handling propylene, chlorine, HCl, and chlorinated hydrocarbons at low temperatures (below 100°C) in the absence of water. Nickel-based aHoys are chiefly used in the reaction area where resistance to chlorine and HCl at elevated temperatures is required (39). Elastomer-lined equipment, usuaHy PTFE or Kynar, is typicaHy used when water and HCl or chlorine are present together, such as adsorption of HCl in water, since corrosion of most metals is excessive. Stainless steels are to be avoided in locations exposed to inorganic chlorides, as stainless steels can be subject to chloride stress-corrosion cracking. Contact with aluminum should be avoided under aH circumstances because of potential undesirable reactivity problems. 

Drilling Muds in the Petroleum and Natural Gas Industry. Since 1941, chromium chemicals have been used in the drilling of wells to combat fatigue corrosion cracking of drill strings, with about one metric ton of sodium chromate being used aimuaHy for an average West Texas well. Other early uses were in gas-condensate wells in Louisiana and East Texas. 

---