Materials characterization techniques, ie, atomic and molecular identification and analysis, ate discussed ia articles the tides of which, for the most part, are descriptive of the analytical method. For example, both iaftared (it) and near iaftared analysis (nira) are described ia Infrared and raman SPECTROSCOPY. Nucleai magaetic resoaance (nmr) and electron spia resonance (esr) are discussed ia Magnetic spin resonance. Ultraviolet (uv) and visible (vis), absorption and emission, as well as Raman spectroscopy, circular dichroism (cd), etc are discussed ia Spectroscopy (see also Chemiluminescence Electho-analytical techniques It unoassay Mass specthot thy Microscopy Microwave technology Plasma technology and X-ray technology). 

During the past 20 y numerous other highly coloured halogen cations have been characterized by Raman spectroscopy. X-ray crystallography, and other techniques, as summarized in Table 17.18. Typical preparative routes involve direct oxidation of the halogen (a) in the absence of solvent, (b) in a solvent which is itself the oxidant (e.g. AsFs) or (c) in a non-reactive solvent (e.g. SO2). Some examples are listed below ... 

Nowadays there is a general consensus that the Ti(IV) atoms are incorporated as isolated centers into the framework and are substituting Si atoms in the tetrahedral positions forming [Ti04] units. The model of isomorphous substitution has been put forward on the basis of several independent characterization techniques, namely X-ray [21-23] or neutron [24-26] diffraction studies, IR (Raman) [52-57], UV-Vis [38,54,58], EXAFS, and XANES [52, 58-62] spectroscopies. 

In the last century, many microstructural characterization techniques have been developed, such as electron microscopy, atomic tunneling microscopy, photoelectron spectroscopy, Raman spectroscopy, etc. The structure of the OLED-based displays is such that many pixels are arranged orderly in the x-y plane. The size and number of pixels determine the resolution and size of the display. Along the z-axis, several layers are stacked on each other. These layers... 

Suitable characterization techniques for surface functional groups are temperature-programmed desorption (TPD), acid/base titration [29], infrared spectroscopy, or X-ray photoemission spectroscopy, whereas structural properties are typically monitored by nitrogen physisorption, electron microscopy, or Raman spectroscopy. The application of these methods in the field of nanocarbon research is reviewed elsewhere [5,32]. 

Many of the characterization techniques described in this chapter require ambient or vacuum conditions, which may or may not be translatable to operational conditions. In situ or in opemndo characterization avoids such issues and can provide insight and information under more realistic conditions. Such approaches are becoming more common in X-ray adsorption spectroscopy (XAS) methods ofXANES and EXAFS, in NMR and in transmission electron microscopy where environmental instruments and cells are becoming common. In situ MAS NMR has been used to characterize reaction intermediates, organic deposits, surface complexes and the nature of transition state and reaction pathways. The formation of alkoxy species on zeolites upon adsorption of olefins or alcohols have been observed by C in situ and ex situ NMR [253]. Sensitivity enhancement techniques play an important role in the progress of this area. In operando infrared and RAMAN is becoming more widely used. In situ RAMAN spectroscopy has been used to online monitor synthesis of zeolites in pressurized reactors [254]. Such techniques will become commonplace. 

Although several metal-containing heterocyclic compounds (such as porphyrins, phthalocyanines, naphthenates) are present in oil fractions most of the bench-scale research has been based on relatively rapid Ni, V, or Ni/V deposition procedures in which experimental FCC formulations have been artificially metal contaminated with solutions of Ni and/or V naphthenate dissolved in benzene (or toluene) (24). Metal levels in these novel FCC are usually above 0.5% that is well above the concentration that today exist on equilibrium FCC, see Figure 1. High metal concentration facilitate the study and characterization of Ni and V effects by modern characterization techniques such as X-ray photoelectron spectroscopy (XPS), Laser Raman spectroscopy (LRS), X-ray diffraction (XRD), electron microscopy, secondary ion mass spectrometry (SIMS), and 51V nuclear magnetic resonance (NMR). 

The aqueous preparation oT supported niobium oxide catalysts was developed by using niobium oxalate as a precursor. The molecular states oT aqueous niobium oxalate solutions were investigated by Raman spectroscopy as a -function o-f pH. The results show that two kinds o-f niobium ionic species exist in solution and their relative concentrations depend on the solution pH and the oxalic acid concentration. The supported niobium oxide catalysts were prepared by the incipient wetness impregnation technique and characterized by Raman, XRD, XPS, and FTIR as a -function o-f niobium oxide coverage and calcination temperature. The Raman studies reveal that two types o-f sur-face niobium oxide species exist on the alumina support and their relative concentrations depend on niobium oxide coverage. Raman, XRD, XPS, and FTIR results indicate that a monolayer oT sur-face niobium oxide corresponds to 19%... 

Recent studies of supported vanadium oxide catalysts have revealed that the vanadium oxide component is present as a two-dimensional metal oxide overlayer on oxide supports (1). These surface vanadium oxide species are more selective than bulk, crystalline V2O5 for the partial oxidation of hydrocarbons (2). The molecular structures of the surface vanadium oxide species, however, have not been resolved (1,3,4). A characterization technique that has provided important information and insight into the molecular structures of surface metal oxide species is Raman spectroscopy (2,5). The molecular structures of metal oxides can be determined from Raman spectroscopy through the use of group theory, polarization data, and comparison of the... 

A number of crystalline VOPO4 phases were detected in the VPO catalysts by different research groups [11,12] that displayed vastly different catalytic behavior during on-stream conditioning (Figure 2). Poorly crystalline and amorphous VOPO4 phases present in the catalysts are often undetected by XRD. The presence of such disordered phases may be confirmed by other characterization techniques, such as Raman spectroscopy and P spin echo NMR. The incomplete phase analysis of VPO catalysts is one of the major reasons responsible for several alternative definitions of the equilibrated state and the nature of the active VPO phase [10-12]. In many cases, only short-term VPO conditioning... 

Raman spectroscopy, which is also used to measure the crystal size of nano-structured solids through the phonon confinement model (PCM), provides only semi-quantitative results for size measurements in ND powders due to insufficient understanding of the Raman spectra of ND and a lack of agreement between theoretical predictions of the model and experimental Raman data. However, taking into account the broad size distribution of ND powders and the contributions of lattice defects, a significant improvement in the predictions of the model was achieved. However, a correct interpretation of Raman data and quantitative size measurements still requires additional information on sample structure and composition. Therefore, a combined use of various characterization techniques such as XRD, HRTEM, and Raman spectroscopy can be recommended for a reliable determination of the average size of ND crystals and their distribution. 

Previous work on KxCm showed the need for a variety of characterization techniques for these highly air sensitive materials. These included in situ conductivity, Raman spectroscopy, microwave absorption, and dc susceptibility. In this study, as well, all doping reactions and measurements were carried out using sealed tubes. C60 was purified by chromatography of fullerite on oc-tadecylsilanised silica with toluene-isopropanol eluent, and dried at 160°C under vacuum. 

The susceptibility of solid surfaces to contamination often results in a requirement for an ultrahigh vacuum (UHV) chamber for preparation and observation of particular samples. For many materials, including metals such as platinum and nickel, adsorption of hydrocarbons and chemisorption of oxygen are quite fast at atmospheric pressure, and the surface must be isolated in UHV to prevent rapid degradation. In addition, a sample in UHV may be subjected to surface analytical techniques such as X-ray photoelectron and Auger spectroscopy to verify or corroborate Raman results. As a result, much of the early and well-characterized surface Raman experiments were carried out in UHV chambers operating below 10 torr (12). 

Zeolites. The weak Raman signals arising from the aluminosilicate zeolite framework allow for the detection of vibrational bands of adsorbates, especially below 1200 cm which are not readily accessible to infrared absorption techniques. Raman spectroscopy is an extremely effective characterization method when two or more colored species coexist on the surface, since the spectrum of one of the species may be enhanced selectively by a careful choice of the exciting line. A wide range of adsorbate/zeolite systems have been examined by Raman spectroscopy and include SO2, NO2, acety-lene/polyacetylene, dimethylacetylene, benzene, pyridine, pyrazine, cyclopropane, and halogens. Extensive discussions of these absorbate/zeolite studies are found in a review article by Bartlett and Cooney. ... 

VIBRATIONAL SPECTROSCOPY Infrared and Raman spectroscopies have proven to be useful techniques for studying the interactions of ions with surfaces. Direct evidence for inner-sphere surface complex formation of metal and metalloid anions has come from vibrational spectroscopic characterization. Both Raman and Fourier transform infrared (FTIR) spectroscopies are capable of examining ion adsorption in wet systems. Chromate (Hsia et al., 1993) and arsenate (Hsia et al., 1994) were found to adsorb specifically on hydrous iron oxide using FTIR spectroscopy. Raman and FTIR spectroscopic studies of arsenic adsorption indicated inner-sphere surface complexes for arsenate and arsenite on amorphous iron oxide, inner-sphere and outer-sphere surface complexes for arsenite on amorphous iron oxide, and outer-sphere surface complexes for arsenite on amorphous aluminum oxide (Goldberg and Johnston, 2001). These surface configurations were used to constrain the surface complexes in application of the constant capacitance and triple layer models (Goldberg and Johnston, 2001). 

---