Tensile test results

Figure 4. Slow strain rate tensile test results at closed-loop controlled potentials with respect to a reference electrode (a) Reduction in area (RA) and (b) RA ratio (to H Free in Ni(g)).

CNT buckypaper/epoxy composites was conducted. The tensile test results are shown in the Figure 14.19, and tensile properties were summarized in Figure 14.20. 

Figure 14.20. Tensile test results of the NBP composites (a) Histogram graph of the Young s modulus, (b) Histogram graph of the tensile strength (11).

Tensile testing results in an elonption of the specimens. This deformation is retained at low tenqieratures, but retraction of the sample occurs as the Tg is apprcrached. If the retraction is uniestrained, this results in more material being drawn into the active zone of the ESR cavity. An apparent increase in radical con-... 

Splitting Tensile Test. Results of the splitting tensile tests for various S-A-S mix designs are shown in Table VI. These are compared with the conventional asphaltic concrete mix design shown in Table V. 

The work of Bussu and Irving on 6.35 mm (0.25 in.) thick 2024-T351 Al sheet is illustrative of hardness variations following FSW in 2024-T351 Al (Ref 12). In their work (Fig. 5.3), hardness is illustrated both as a function of distance from the joint interface and depth from the top surface. As shown, a typical W -shaped hardness curve is created. Due to the close relationship between hardness profiles and tensile test results, this composite of hardness results has implications for resultant mechanical properties. The studies in this work show four distinct hardness zones ... 

Fig. 5.37 Tensile test results for longitudinal microspecimens in friction stir welded 7349-T6. HAZ, heat-affected zone TMAZ, thermomechanically affected zone WN, weld nugget Source Ref 83...

Table 7.6 Tensile test results for friction stir welds (FSWs) of Ti-6AI-4V...

FIGURE 6-1 Tensile test results of Nicalon fiber-reinforced SiC matrix composites prepared by CVI. Source ... 

FIGURE 6-4 Tensile test results of Ui-Nicalon fiber-reinforced SiC-Si matrix composites prepared by melt infiltration. Results are for 4 2 and 4 4 fiber layup indicative of the number of plies in 0° and 90° directions, respectively. Source Corman et al., 1996. 

FIGURE 6-5 Tensile test results for hot pressed Niealon SiC fiberreinforced glass-eeramie matrix eomposites with... 

The tensile test results of PP/PPy nanocomposites show that incorporation of PPy nanoparticles in PP improves the strength and the stiffness while limiting the elongation of PP. In order to investigate the potential improvement in dispersion of PPy nanoparticles in PP, identical tensile tests were employed to nanocomposites prepared with dispersant. Due... 

The tensile tests results of various compounds of PP/nano-CaC03 are indicated in Table 6 and Figures 5 and 6. 

Figure 13.11 shows the tensile test results of (a) the disassembled and reconstituted original HIPS with the wide particle-size distribution having a craze-flow stress of = 19.0 MPa as a standard for comparison (b) the special blend containing only the large particles with a flow stress (Tco = 18.17 MPa (c) the special blend containing only the small particles with a flow stress of around CTco = 20.46 MPa, but a substantial upper yield stress of 24.0 MPa. Clearly, the two special blends with narrow particle-size distributions have substantially different behaviors and bracket the behavior of the reassembled original HIPS. 

Tensile test results (Fig. 6) show retention of toe room temperature UTS of260 MPa up to 1200°C in air, which is in agreement with the four point flexural strength data (Table n). 

FIGURE 6. Tensile test results of Nextel 610/monazite/alumina composites versus control samples (Nextel 610/alumina) tested at high temperature. Samples sintered for five hours at 1100-1200°C sintering temperature = test temperature (10 min. soak test temperature.)... 

Figure 5.14 Tensile test results of the various fibers (adapted from Reference [20])...

Figure 7.15 Tensile test results of SMPFs with various pre-tensions. Source [21] Reproduced with permission from Elsevier...

TABLE 11.1. Tensile Test Results on LCP Film Made with TRD. 

To estimate the effect of the fillers, composite/matrix ratios are calculated from tensile tests results. In Fig. 17.6 are shown, with the last five graphs, different... 

Table 4.14 Tensile test results for first and second loading/unloading cycles to nominal strain e = 3. Test temperature = 23 1°C, relative humidity = 41 7% RH, and nominal strain-rate = 0.03 s [135]...

Fig. 1.4 Schematic shape of the plate-like specimen used in tensile testing resulting in uniform and reproducible values...

I 73 Polystyrene-Montmorillonite Nanocomposites by In-situ Polymerization and Their Properties Table 13.4 Tensile test results for PS-MMT nanocomposites. 

---