Silk fibers mechanical properties

Biomechanical Machines. The mechanical properties of fibrous polypeptides could be put to use for the commercial production of fibers (qv) that are more elastic and resiUent than available synthetics (see Silk). The biochemical properties of proteins could also be harnessed for the conversion of mechanical energy to chemical energy (35). 

Table 3. Mechanical Properties of Silks and Other Fibers ...

Thermal Properties. Spider dragline silk was thermally stable to about 230°C based on thermal gravimetric analysis (tga) (33). Two thermal transitions were observed by dynamic mechanical analysis (dma), one at —75° C, presumed to represent localized mobiUty in the noncrystalline regions of the silk fiber, and the other at 210°C, indicative of a partial melt or a glass transition. Data from thermal studies on B. mori silkworm cocoon silk indicate a glass-transition temperature, T, of 175°C and stability to around 250°C (37). The T for wild silkworm cocoon silks were slightly higher, from 160 to 210°C. 

Raw silk was dissolved in hexafluoro-iso-propanol (HFIP) [17, 33]. A typical working concentration for spinning was 2.5% (w/v) silk fibroin in HFIP. The spinning solution was pressed through a small needle (0 80-250 pm) into a precipitation bath (methanol for Bombyx mori silk proteins and acetone for Nephila clavipes silk proteins) and the silk solution immediately precipitated as a fiber. The best performing fibers approached the maximum strength measured for native fibers of Bombyx mori, but did not achieve the mechanical properties of natural spider silk. 

Although the amino acid sequence as well as the secondary structure of fibroin differs from those of spidroin, the fibers spun from these proteins, that is, silkworm silk and spider silk have comparable mechanical properties. These may be attributed to the structural characteristics, both at the molecular and filament level. The superior mechanical properties of silk-based materials, such as films, coatings, scaffolds, and fibers produced using reconstituted or recombinant silk proteins, are determined by their condensed structures. 

The attractive properties of silk fibers as a natural, sustainable product have inspired researchers to look for options to fabricate such fibers without the use of worms or spiders. Furthermore, these natural polymers, silk proteins (both fibroin and spidroin), allow for adjustable mechanical properties, thermal resistance (Drummy et al., 2005 Motta et al., 2002), as well as biomedical compatibility (Vepari and Kaplan, 2007). 

As to fibers, it was reported that the inferior mechanical properties of silk from cocoons compared to spider silk result from the silkworm spinning process. If silkworm silk is processed at a constant pulling speed rather than constant force pulling, it possesses excellent properties, approaching the spider dragline silk (Shao and Vollrath, 2002). This suggests that the silkworm silk has the potential to produce better fibers, and the regenerated fibroin, which is easy to harvest, has the possibility to be fabricated into a reconstituted super-fiber. 

---