Polyimides property examples

Self-lubricating grades Graphite Graphite + M0S2 + Graphite + 

General chemical properties are subject to the compatibility of the fillers and reinforcements with the ambient conditions. If the fillers are well adapted, the chemical properties are the same as the polyimide matrix. 

Weak acids Strong acids Bases Solvents 

Limited behaviour, preliminary tests necessary Limited behaviour with hot acids 

Limited to poor behaviour even at ambient temperature 

---

Bis-maleimide resins composed of BMI and diamines have been reported in the early 1960s in the patent literature. Since that time, a number of patents have appeared describing improvements in their properties and uses [3]. Although many bis-maleimide resins are commercially developed, relatively few reports of their use as adhesives are to be found in scientific journals [4-10]. Improvements of maleimide resins are mirrored in the improvements of thermosetting polyimides. For example, the method of in situ polymerization of monomer reactants (PMR method) was developed [6]. 

The preparation of composites prepared by high temperature decomposition reactions have mainly concentrated on polyimides and reactive inorganic additives (e.g., simple salts and complexes). In many cases polymer-metal composites have been unintentionally produced by workers whose primary goal was the modification of polyimide properties by incorporation of metal ions. For example, approximately 30 years ago Angelo briefly reported in a patent the addition of metal ions to several types of polyimides for the purpose of forming particle-containing transparent polyimide shaped structures. Ten years... 

For reasons that are not fiiUy understood, PPSF exhibits generally improved compatibiUty characteristics over either PSF or PES in a number of systems. An example of this is blends of PPSF with polyaryletherketones (39,40). These blends form extremely finely dispersed systems with synergistic strength, impact, and environmental stress cracking resistance properties. Blends of PPSF with either PSF or PES are synergistic in the sense that they exhibit the super-toughness characteristic of PPSF at PSF or PES contents of up to 35 wt % (33,34). The miscibility of PPSF with a special class of polyimides has been discovered and documented (41). The miscibility profile of PPSF with high temperature (T > 230° C) polysulfones has been reported (42). 

Polyimide-clay nanocomposites constitute another example of the synthesis of nanocomposite from polymer solution [70-76]. Polyimide-clay nanocomposite films were produced via polymerization of 4,4 -diaminodiphenyl ether and pyromellitic dianhydride in dimethylacetamide (DMAC) solvent, followed by mixing of the poly(amic acid) solution with organoclay dispersed in DMAC. Synthetic mica and MMT produced primarily exfoliated nanocomposites, while saponite and hectorite led to only monolayer intercalation in the clay galleries [71]. Dramatic improvements in barrier properties, thermal stability, and modulus were observed for these nanocomposites. Polyimide-clay nanocomposites containing only a small fraction of clay exhibited a several-fold reduction in the... 

The polyimide-CNT composites have good biocompatibility and conductive properties, which can be used to fabricate the electrode arrays, and enhance their biocompatibility. For example, they can be used as the stimulator embedded in the blind eyes, and can be used for the electrode arrays transplanted in the human body without damaging human organs and tissues (Tulevski et al., 2007). 

Certain polyimides resist high-energy radiation well. For example, the properties of certain grades are still suitable after exposure to 10 and 10 Mrad. 

Metal ion modified polyimide films have been prepared to obtain materials having mechanical, electrical, optical, adhesive, and surface chemical properties different from nonmodified polyimide films. For example, the tensile modulus of metal ion modified polyimide films was increased (both at room temperature and 200 0 whereas elongation was reduced compared with the nonmodif ied polyimide (i). Although certain polyimides are )cnown to be excellent adhesives 2) lap shear strength (between titanium adherends) at elevated temperature (275 0 was increased by incorporation of tris(acetylacetonato)aluminum(III) (2). Highly conductive, reflective polyimide films containing a palladium metal surface were prepared and characterized ( ). The thermal stability of these films was reduced about 200 C, but they were useful as novel metal-filled electrodes ( ). 

Poly[2,2 -(m-phenylene-5,5 -benzimidazole)] (PBI) is a very high glass transition temperature (Tg 430°C), commercially available material. It possesses excellent mechanical properties, but is difficult to process into large parts and has high moisture regain and poor thermo-oxidative stability at temperatures above approximately 260 °C. Polyimides, especially the thermoplastic polyimides, offer attractive thermo-oxidative stability and processibility, but often lack the thermal and mechanical characteristics necessary to perform in applications such as the matrix for high use-temperature (over 300 °C) structural composites (for example, carbon fiber reinforced) for aerospace use. The attempt to mitigate... 

In most of the previous work with polyimide fibers, the fibers were spun from poly(amic acid) precursors, which were thermally imidized in the fiber form. However, high degrees of imidization were not achieved. Thus, tensile properties of these polymers were not as good as those of high-performance fibers. Work in our laboratories has shown that when the fibers are spun directly from preimidized polymers, it is possible to achieve tensile properties that are as good or even better than those of poly(p-phenyleneterephthalamide) (PPTA or Kevlar ) fibers. For example, fibers have been prepared from m-cresol solutions of BPDA-PFMB using a dry-jet wet-spinning method. The as-spun fibers were then extensively drawn and annealed above 400°C to achieve excellent mechanical properties. 

---