Plate cracking

The majority of cracks associated with welds joining the plates cracks are perpendicular to the weld and run through the weldment. Repair-welded areas cracked again. [Pg.530]

Alloy 7079-T651 2.5 cm thick plate Crack orientation TL Temperature 23 °C Open circuit... [Pg.421]

ALLOY 7178 - T651 + OVERAGED AT 160°C 2.5 cm THICK PLATE CRACK ORIENTATION TL SATURATED AQUEOUS NaCI SOLUTION OPEN CIRCUIT TEMPERATURE 23°C... [Pg.331]

For an infinite plate, crack propagation by da in positive xi direction can also be considered as a shift of the integration region A in negative Xi direction, resulting in... [Pg.160]

PTH attributes including size, annular ring, plating thickness, plating voids and nodules, plating cracks, resin smear, etchback, wicking, innerlayer (post) separation, and solder thickness... [Pg.1195]

Cl 15 Steam generator internals damage and plate cracking... [Pg.6]

General Electric Company SIL 588, Top Guide and Core Plate Cracking, February 17, 1995. [Pg.69]

NRC Information Notice 95-17 Reactor Vessel Top Guide and Core Plate Cracking Provides information to alert licensees that significant cracking has been observed in the weld regions of the reactor vessel top gnide and core plate in an overseas BWR. [6.12]... [Pg.73]

GE SIL 588R1 (05/18/95) Top Guide and Core Plate Cracking Inspections of the core shroud in a non-GE BWR located outside the United States have revealed significant cracking. The core shroud material was 347 SS, which is a niobium stabilized austenitic stainless steel. This SIL revision provides an update and clarification of SIL No. 588, which is now void. This revision is based on feedback from BWR owners who inqrlemented the original recormnendations found in SIL No 588. This SIL is not applicable to BWR/6s. [6.241... [Pg.74]

The current wheel monitoring practices are described in section 20.2, but gaps exist in automatic detection and/or measuring of the following cracked/broken flange, thermal flange crack, cracked/broken/shattered/spread rim, cracked/broken plate, thermal plate crack, hole in plate, loose wheel, wheel gouge, subsurface defect, etc. [Pg.332]

Hard chrome plate (crack-free form is best)... [Pg.201]