Phenol formaldehyde dispersion resole

The in situ process is simpler because it requires less material handling (35) however, this process has been used only for resole resins. When phenol is used, the reaction system is initially one-phase alkylated phenols and bisphenol A present special problems. As the reaction with formaldehyde progresses at 80—100°C, the resin becomes water-insoluble and phase separation takes place. Catalysts such as hexa produce an early phase separation, whereas NaOH-based resins retain water solubiUty to a higher molecular weight. If the reaction medium contains a protective coUoid at phase separation, a resin-in-water dispersion forms. Alternatively, the protective coUoid can be added later in the reaction sequence, in which case the reaction mass may temporarily be a water-in-resin dispersion. The protective coUoid serves to assist particle formation and stabUizes the final particles against coalescence. Some examples of protective coUoids are poly(vinyl alcohol), gum arabic, and hydroxyethjlceUulose. 

Water-based dispersions or emulsions such as polyvinyl acetate, acrylics, polyvinyl chloride and polyvinyl alcohol with plasticizers and tackifiers. In addition, this range can include urea formaldehyde and phenolic adhesives, resins, natural adhesives produced from starch, dextrin, casein, animal glues (see Polyvinyl alcohol in adhesives, Phenolic adhesives single-stage resoles. Phenolic adhesives two-stage novolacs. Animal glues and technical gelatins) and rubber latex (see Emulsion and dispersion adhesives). Solvent-free 100% solids such as polyurethane. Hot melt adhesives include Ethylene-vinyl acetate copolymers, polyolefins, polyamides, polyesters with tackifiers and waxes. More recent additions include cross-linkable systems. 

Addition of p-cresol formaldehyde (PCF) into phenolic/NBR blends resulted in rednction in the domain size of the dispersed phase and improvement in mechanical properties [244]. PCF resin has an intermediate polarity compared with NBR and resole and can react faster with NBR. Therefore, PCF molecules are likely to be concentrated at the phenolic/NBR interface and act as an external compatibilising agents [245]. Thus compatibility and chemical bonding between NBR and phenolic resin is improved, leading to the enhancement in properties. The other materials used as toughening agents of phenolic resin include elastomers such as natural rubber and nitrile rubber [246, 247], reactive liquid polymers [248] and thermoplastics such as polysulfone, polyamide, polyethylene oxide [249, 250]. 

---