Cotton, J. B., Localised Corrosion 676 NACE International Corrosion Conference series NACE-3 (eds R. W. Stable, B. F. Brown, J. Kruger and A. Agrawal) (1974)... [Pg.889]

Frenier, Wayne E. (Hydrochem Industrial Services). 20 Years of Advances in Technology for Chemically Cleaning Industrial Equipment A Critical Review. Paper 338, presented at the NACE International Corrosion Conference, USA 1998. [Pg.765]

Reardon, P. A. Kelly, J. A. New Oxygen Scavengers and Their Chemistry Under Hydrothermal Conditions. Nalco/NACE International Corrosion Forum, 86. NACE International, USA, March 1986. [Pg.769]

L. Bertolini, P. Pedeferri, B. Bazzoni, L. Lazzari, Measurements of ohmic drop free potential in the presence of stray current , NACE International Corrosion 98 Conference, paper 98560, March 1998. [Pg.146]

G. Jones,]. Slater and R.W. Staehle (Eds.) High Temperature/ High Pressure Electrochemistry in Aqueous Solutions NACE, Intern. Corrosion Conference Series No.4. NACE, Houston, Tx, U.S.A., 1973. [Pg.33]

G. Rocchini NACE Intern. Corrosion Forum, Boston, 1985, paper No. 188. Published by NACE, Houston, Tx, U. S. A., 1985. [Pg.54]

National Association for PET Container Resources (NAPCOR) Facilitates the economical recovery of plastic containers, with an emphasis on PET, including U.S. recycling industry statistics and member company profiles, http //www.napcor.com National Association of Corrosion Engineers (NACE) International (corrosion) http //www. nace.org... [Pg.657]

Aberle, D., Agarwal, DC. 2008. High performance corrosion resistant stainless steels and nickel alloys for oil and gas applications. NACE—International Corrosion Conference Series, Corrosion 2008 New Orleans, LO March 16-20, 2008 Code 77054, pp. 080851-0808517. [Pg.451]

The UMIST Corrosion Discussion list (http / / www.cp.umist.ac.uk/corros-1/) and the NACE International Corrosion Network (http / /www.nacecorrosioimetwork. com/read/aIl forums/). [Pg.11]

Milde K, Sand W, Wolff W, Bock E (1983) Thiobacilli of the concrete walls of the Hamburg sewer system. J Gen Microbiol 129 1327-1333 Millard SG, Gowers KR, Bungey JH (1995) Galvanostatic pulse techniques a rapid method of assessing corrosion rates of steel in concrete structure. NACE International Corrosion, Houston Miller JDA (1970) Microbial aspects of metallurgy. Elsevier, New York, pp 61-105 Mills AL, Powelson DK (1996) Bacterial interactions with surfaces in soils. In Fletcher M (ed) Bacterial adhesion molecular and ecological diversity. Wiley-Liss, New York, pp 25-57... [Pg.337]

Farquhar, G.B. 1996. The Effect of Polycrylamide Polymers and Formaldehyde on Selected Strains of Oilfield Related Bacteria. Paper 96281 presented at the NACE International CORROSION 96 51 Annual Conference and Exposition, Denver, 24-29 March. [Pg.378]

S. Al-Sulaiman, A.W. Al-Mithin, G. Murray, A.J. Biedermann, M. Islam 2008. Advantages and limitations of using Field Test Kits for determining hacterial proliferation in oil field waters, NACE - International Corrosion Cortfererux Series, 086551—0865518. [Pg.523]

H. Amaya, M. Ueda, M. Sagara, K. Noda 2007. Effect of variation of local PH on stress corrosion cracking of stainless steels in high concentration brines. NACE - International Corrosion Conference Series, 070961-0709615. [Pg.523]

J. McKennis, N. Bae, M. Kimura, K. Shimamoto, H. Sato 2008. A new chemical mechanistic pos-mlate regarding annular environmentally assisted cracking (ABAC) - Importance of cations and key contaminants in packer fluids in cracking of martensitic stainless steel. NACE - International Corrosion Conference Series, 084831—0848316. [Pg.529]

D. Fyfe and co-workers. International Corrosion Forum Corrosion 75, Paper No. 63, Toronto, National Association of Corrosion Engineers (NACE), Houston, Texas, 1975. [Pg.195]

To obtain the corrosion current from Rp, values for the anodic and cathodic slopes must be known or estimated. ASTM G59 provides an experimental procedure for measuring Rp. A discussion or the factors which may lead to errors in the values for Rp, and cases where Rp technique cannot be used, are covered by Mansfeld in Polarization Resistance Measurements—Today s Status, Electrochemical Techniques for Corrosion Engineers (NACE International, 1992). [Pg.2441]

Romero, Matilde F. Pdrez, Orlando Navarro, Alfredo. Phosphate Attack as Caustic Corrosion in High-Pressure Boiler Tubes. Material Performance . NACE International, USA, March 1999. [Pg.769]

Shimura, Y. Uchida, K. Sato, T. Taya, S. The Performance of New Volatile Oxygen Scavenger and Its Field Application in Boiler Systems. Kurita/NACE Corrosion 2000. NACE International, USA, April 2000. [Pg.769]

Figure 6. Bipolar precipitates consisting of an inner anion-selective layer and an outer cation-selective layer.19 When the electrode is polarized to the more noble side, protons and chloride ions are kept from permeating through the film, so that anodic dissolution of the substrate metal is blocked. (Reproduced from N. Sato, Corrosion, 45 354, 1989, Fig. 24 with permission of NACE International.)... Figure 6. Bipolar precipitates consisting of an inner anion-selective layer and an outer cation-selective layer.19 When the electrode is polarized to the more noble side, protons and chloride ions are kept from permeating through the film, so that anodic dissolution of the substrate metal is blocked. (Reproduced from N. Sato, Corrosion, 45 354, 1989, Fig. 24 with permission of NACE International.)...
Figure 7. Current-potential curve of a bipolar membrane of hydrous ironflll) oxide in chloride solution. FeCl3(aq)/Fe(HI)(oxideyNaCl(aq)-Na2Mo04(aq).l The system is kept at room temperature. C, cation A, anion. (Reproduced bom M. Sakashita and N. Sato, Corrosion 35,351,1979, Fig. 4 with permission from NACE International.)... Figure 7. Current-potential curve of a bipolar membrane of hydrous ironflll) oxide in chloride solution. FeCl3(aq)/Fe(HI)(oxideyNaCl(aq)-Na2Mo04(aq).l The system is kept at room temperature. C, cation A, anion. (Reproduced bom M. Sakashita and N. Sato, Corrosion 35,351,1979, Fig. 4 with permission from NACE International.)...
Figure 8. Schematic potential distribution across a bipolar membrane under increased anodic polarization. 15 At the neutral layer, dehydration proceeds in accordance with anodic polarization. and A are the inner potential and membrane potential, respectively. (Reproduced from N. Sato, Corrosion 45,354,1989, Fig. 27 with permission from NACE International.)... Figure 8. Schematic potential distribution across a bipolar membrane under increased anodic polarization. 15 At the neutral layer, dehydration proceeds in accordance with anodic polarization. and A are the inner potential and membrane potential, respectively. (Reproduced from N. Sato, Corrosion 45,354,1989, Fig. 27 with permission from NACE International.)...
Figure 2. Cumulative corrosion loss Y. INT for mild steel sensors embedded in concrete and exposed to a sewer bypass (a) control sample, (b) flushed sample. (Reprinted from Ref 6 with permission from NACE International.)... Figure 2. Cumulative corrosion loss Y. INT for mild steel sensors embedded in concrete and exposed to a sewer bypass (a) control sample, (b) flushed sample. (Reprinted from Ref 6 with permission from NACE International.)...
A. Legat, in I2th International Corrosion Congress, NACE International, Houston, TX, 1993. [Pg.245]

R. G. Buchheit, T. E. Hinkebein, R F. Hlava, and D. G. Melton. The effects of latex additions on centrifugally cast concrete for internal pipeline protection. In Proceedings Volume, volume 4, pages 2854-2864.12th SPE/NACE Int Corrosion Congr (Houston, TX, 9/19-9/24), 1993. [Pg.365]

NACE International Standard RP0472-95, Methods and Controls to Prevent In-Service Environmental Cracking of Carbon Steel Weldments in Corrosive Petroleum Refining Environments. [Pg.31]

Ziomek-Moroz M, Cramer SD, Holcomb GR, Covino, Jr BS, Bullard SJ, and Singh P. In Corrosion 2005, paper No. 10, NACE International, Houston, TX. [Pg.210]

S. Bemhardsson, R. Melstrom and B. Brox, in Corrosion/80-NACE, NACE International, Houston, Texas. (1980) p. 85. [Pg.314]


See other pages where NACE International Corrosion is mentioned: [Pg.26]    [Pg.26]    [Pg.26]    [Pg.52]    [Pg.451]    [Pg.93]    [Pg.528]    [Pg.26]    [Pg.26]    [Pg.26]    [Pg.52]    [Pg.451]    [Pg.93]    [Pg.528]    [Pg.245]    [Pg.245]    [Pg.245]    [Pg.245]    [Pg.245]    [Pg.245]    [Pg.245]    [Pg.246]    [Pg.246]    [Pg.246]    [Pg.3]   