Micropores conductivity

J.Y. Yang and D.C. Martin, Microporous conducting polymers on neural microelectrode arrays -1 - Electrochemical deposition. Sens. Actual. B Chem., 101(1-2), 133-142 (2004). 

Yang, J. Y. and Martin, D. C. (2004) Microporous conducting polymers on neural microelectrode arrays - i - electrochemical deposition. Sensors and Actuators B Chemical 101,133-42. 

The swelling of the adsorbent can be directly demonstrated as in the experiments of Fig. 4.27 where the solid was a compact made from coal powder and the adsorbate was n-butane. (Closely similar results were obtained with ethyl chloride.) Simultaneous measurements of linear expansion, amount adsorbed and electrical conductivity were made, and as is seen the three resultant isotherms are very similar the hysteresis in adsorption in Fig. 4.27(a), is associated with a corresponding hysteresis in swelling in (h) and in electrical conductivity in (c). The decrease in conductivity in (c) clearly points to an irreversible opening-up of interparticulate junctions this would produce narrow gaps which would function as constrictions in micropores and would thus lead to adsorption hysteresis (cf. Section 4.S). 

Capillary Suction Processes. The force needed to remove water from capillaries increases proportionately with a decrease in capillary radius, exceeding 1400 kPa (200 psi) in a 1-p.m-diameter capillary. Some attempts have been made to use this force as a way to dewater sludges and cakes by providing smaller dry capillaries to suck up the water (27). Sectors of a vacuum filter have been made of microporous ceramic, which conducts the moisture from the cake into the sector and removes the water on the inside by vacuum. Pore size is sufficiently small that the difference in pressure during vacuum is insufficient to displace water from the sector material, thus allowing a smaller vacuum pump to be effective (126). 

Numerical values for solid diffusivities D,j in adsorbents are sparse and disperse. Moreover, they may be strongly dependent on the adsorbed phase concentration of solute. Hence, locally conducted experiments and interpretation must be used to a great extent. Summaries of available data for surface diffusivities in activated carbon and other adsorbent materials and for micropore diffusivities in zeolites are given in Ruthven, Yang, Suzuki, and Karger and Ruthven (gen. refs.). 

Microporous insulation represents a good compromise its thermal conductivity reaches 4-8 mWrrf K-1 in a pressure range of only 0.1-1 mbar. Another advan-... 

Haute, S. and Stimming, U. 2001. Proton conducting membranes based on electrolyte filled microporous matrices. Journal of Membrane Science 185 95-103. 

The effective conductivity of the membrane depends on its random heterogeneous morphology—namely, the size distribution and connectivity of fhe proton-bearing aqueous pafhways. On fhe basis of the cluster network model, a random network model of microporous PEMs was developed in Eikerling ef al. If included effecfs of varying connectivity of the pore network and of swelling of pores upon water uptake. The model was applied to exploring the dependence of membrane conductivity on water content and... 

A rigid microporous morphology, which does not reorganize upon water uptake, corresponds to a simple linear relation x w) = yw. In this limiting case, the model resembles the archetypal problem of percolation in bicontin-uous random media. Due to deviations of swelling from fhis law, universal percolation exponents in relations between conductivity and water content are not warranted. 

Apparently, the formation of the microporous structure within the PVdF—HFP copolymer was of critical importance to the success of Bellcore technology, and the ion conductivity was proportional to the uptake of the liquid electrolyte. To achieve the desired porosity of PVdF film, Bellcore researchers prepared the initial polymer blend of PVdF with a plasticizer dibutylphthalate (DBP), which was then extracted by low boiling solvents after film formation. Thus, a pore-memory would be left by the voids that were previously occupied by DBP. However, due to the incomplete dissolution of such high-melting DBP during the extraction process, the pore-memory could never be restored at 100% efficiency. Beside the total volume of pores thus created by the plasticizer. 

These types of separators consist of a solid matrix and a liquid phase, which is retained in the microporous structure by capillary forces. To be effective for batteries, the liquid in the microporous separator, which generally contains an organic phase, must be insoluble in the electrolyte, chemically stable, and still provide adequate ionic conductivity. Several types of polymers, such as polypropylene, polysulfone, poly(tetrafluoroethylene), and cellulose acetate, have been used for porous substrates for supported-liquid membranes. The PVdF coated polyolefin-based microporous membranes used in gel—polymer lithium-ion battery fall into this category. Gel polymer... 

A novel microporous separator using polyolefins has been developed and used extensively in lithium-ion batteries since it is difficult for conventional separator materials to satisfy the characteristics required in lithium-ion batteries. In lithium-ion batteries two layers of separators are sandwiched between positive and negative electrodes and then spirally wound together in cylindrical and prismatic configurations. The pores of the separator are filled with ionically conductive liquid electrolyte. 

Asahi Chemical Industry carried out an exploratory investigation to determine the requirements for cellulose based separators for lithium-ion batteries. In an attempt to obtain an acceptable balance of lithium-ion conductivity, mechanical strength, and resistance to pinhole formation, they fabricated a composite separator (39—85 /cellulosic fibers (diameter 0.5—5.0 /pore diameter 10—200 nm) film. The fibers can reduce the possibility of separator meltdown under exposure to heat generated by overcharging or internal short-circuiting. The resistance of these films was equal to or lower than the conventional polyolefin-based microporous separators. The long-term cycling performance was also very comparable. 

Abraham et al. were the first ones to propose saturating commercially available microporous polyolefin separators (e.g., Celgard) with a solution of lithium salt in a photopolymerizable monomer and a nonvolatile electrolyte solvent. The resulting batteries exhibited a low discharge rate capability due to the significant occlusion of the pores with the polymer binder and the low ionic conductivity of this plasticized electrolyte system. Dasgupta and Ja-cobs patented several variants of the process for the fabrication of bonded-electrode lithium-ion batteries, in which a microporous separator and electrode were coated with a liquid electrolyte solution, such as ethylene—propylenediene (EPDM) copolymer, and then bonded under elevated temperature and pressure conditions. This method required that the whole cell assembling process be carried out under scrupulously anhydrous conditions, which made it very difficult and expensive. 

---