Machine strand

Tensile and flexural properties were studied with an Instron 4204 testing machine. Tensile tests were performed on the drawn strands at a test speed of 3 mm/ min, while three-point-bending tests (ISO 178) at a speed of 5 mm/min were applied to the injection molded specimens. Charpy impact strength was measured of the unnotched samples with a Zwick 5102 pendulum-type testing machine using a span of 70 mm. The specimens (4 X 10 X 112 mm) used for three-point-bending tests were also used for the impact tests. It should be noted that neither the tensile tests for the strands nor the impact tests were standard tests. The samples were conditioned for 88 h at 23°C (50% r.h,) before testing. 

Incorporation of a flavin electron donor and a thymine dimer acceptor into DNA double strands was achieved as depicted in Scheme 5 using a complex phosphoramidite/H-phosphonate/phosphoramidite DNA synthesis protocol. For the preparation of a flavin-base, which fits well into a DNA double strand structure, riboflavin was reacted with benzaldehyde-dimethylacetale to rigidify the ribityl-chain as a part of a 1,3-dioxane substructure [49]. The benzacetal-protected flavin was finally converted into the 5 -dimethoxytri-tyl-protected-3 -H-phosphonate ready for the incorporation into DNA using machine assisted DNA synthesis (Scheme 5a). For the cyclobutane pyrimidine dimer acceptor, a formacetal-linked thymine dimer phosphoramidite was prepared, which was found to be accessible in large quantities [50]. Both the flavin base and the formacetal-linked thymidine dimer, were finally incorporated into DNA strands like 7-12 (Scheme 5c). As depicted in... 

Polymerase chain reaction (PCR) is one of the most important techniques for rapid bacterial identification. It consists of repeated cycles of enzymatic reactions in a thermal cycler (PCR machine) that copies DNA strands many times. The DNA amplified in one PCR cycle is used as a template for the next cycle. This results in an exponential increase of the desired target... 

To make cut pile carpets, two strands of BCF yarns are twisted together and heat-set with steam using a Superba heat setting machine at 135-145 °C or at 175-195 °C when heat-set with super-heated steam in a Suessen. An experimental design experiment [94] showed the higher the heat set temperature, then the lower is the bulk of the final carpet, but there is an increase in the tip definition and walk performance. The tufted carpets are then dyed with disperse dyes at atmospheric boil [95] in a continuous or a batch process. PTT carpets showed excellent resiliency in walk test experiments, equivalent to a nylon and much better than both PET and polypropylene, had lower static charge of <3.5 kV, and were resistant to coffee, mustard, betadine, red acid dyes and other stains [96],... 

The polymer was extruded at 240 C to produce 28-strand multifilament yarn. The yam was hot-stretched and fiber tensile strengths in the range 3-6 g/den (1-2 dpf) could be obtained. The yam was placed on braider bobbins on a 12-carrier machine with 7-ply core. The braid was made with 51 picks per inch and hot-stretched 25% at215 F. 

One way to characterise thermoplastic melts is by using a Rheotens machine (31) which subjects an extruded strand of melt to tensile elongation at a fixed velocity while measuring the tensile force. The typical response (melt tensile force versus draw velocity) for branched PP extends to twice as high a draw velocity, with six times the force, than that for linear PP. Alternatively a... 

As is well known, the first stage in synthesizing proteins is transcription of genetic code from DNA to messenger RNA (mRNA), a process that depends on RNA polymerase (transcriptase). A strand of nucleotides in RNA mirrors the order of nucleotides in DNA, thus containing information in a certain sequence in which amino acids must be bound to form the corresponding protein. Protein synthesis takes place on ribosomes, which can be represented as certain machines in which proteins and various amino acids are assembled. 

Second-strand synthesis Execute the following program on a PCR machine ... 

Oriented strand board (OSB) is obtained from wood chips. The orientation is designed to simulate the characteristics of a wood panel, with limited swelling and higher resistance in the fibre direction. Chips are orientated by air with a blowing machine. These panels are commonly used on building sites, and they often make part of the walls in houses, especially in the United States. If no orientation is given, the panel is called waferboard. 

The effect of sample size and number must be taken into account, if, for example, the mixing quality is investigated in the laboratory on a small machine, and the results are then scaled up to production levels. The number of individual samples and the volume of the individual samples in relation to the total volume should be the same in the laboratory as on the production machine. If in production, for instance, the melt forms 50 strands after extrusion, then 50 partial flows must also be produced by the laboratory-scale machine. This is not always possible or practical with the usually small volumetric flows in model experiments. For this reason, laboratory work often relies on model systems and alternative methods of evaluation. 

---