Impact strength Charpy

The cast zinc—aluminum—copper slush alloy, after aging for ten years indoors, shows a tensile strength of 238 MPa (34,500 psi) with Charpy impact strengths of 1.4—4.1 J (1—3 ft4bf) (87). [Pg.413]

Samples S/B mole. b ratios Elongation at break, % Light transmittance, % Charpy impact strength, J /m Heat distortion temperature, °C... [Pg.184]

Tensile and flexural properties were studied with an Instron 4204 testing machine. Tensile tests were performed on the drawn strands at a test speed of 3 mm/ min, while three-point-bending tests (ISO 178) at a speed of 5 mm/min were applied to the injection molded specimens. Charpy impact strength was measured of the unnotched samples with a Zwick 5102 pendulum-type testing machine using a span of 70 mm. The specimens (4 X 10 X 112 mm) used for three-point-bending tests were also used for the impact tests. It should be noted that neither the tensile tests for the strands nor the impact tests were standard tests. The samples were conditioned for 88 h at 23°C (50% r.h,) before testing. [Pg.625]

Figure 6 Effect of ABS weight percent on Charpy impact strength. Figure 6 Effect of ABS weight percent on Charpy impact strength.
Charpy impact strength (kJ/m ) Izod notched impact (J/m) 20-110 3-7 2-5 24-57... [Pg.860]

Figure 2. Influence of atactic (aPM) and isotactic (iPM) PP-g-MA blend compatibilizers on the morphological and mechanical properties of PP—PA6 (70/30) PA6 domain size (a), Youngs modulus (b), yield stress (c), and notched Charpy impact strength (d). Figure 2. Influence of atactic (aPM) and isotactic (iPM) PP-g-MA blend compatibilizers on the morphological and mechanical properties of PP—PA6 (70/30) PA6 domain size (a), Youngs modulus (b), yield stress (c), and notched Charpy impact strength (d).
Standard test methods for the determination of Charpy impact strength are listed in Table 12.11. For example, BS 2782 (method 351 A) uses a... [Pg.877]

Table 12.11. Standard test methods for the determination of Charpy impact strength... Table 12.11. Standard test methods for the determination of Charpy impact strength...
Figure 11.16 Falling weight Charpy impact strength of the a-PP and (3-PP specimens impacted at different speeds. (From Reference 18 with permission from Elsevier.)... Figure 11.16 Falling weight Charpy impact strength of the a-PP and (3-PP specimens impacted at different speeds. (From Reference 18 with permission from Elsevier.)...
Figure 18.8 Temperature dependences of Charpy impact strength (specimens with sharp notches) for PA6 and its blends with g-PE (a) and (g-PE/g-EPDM) (b) g-PO concentration, 30 wt%. Figure 18.8 Temperature dependences of Charpy impact strength (specimens with sharp notches) for PA6 and its blends with g-PE (a) and (g-PE/g-EPDM) (b) g-PO concentration, 30 wt%.
Conditional growth rate of adhesional strength Charpy impact strength for sharply notched specimens Swell of extrudate... [Pg.551]

B4 Charpy impact strength (unnotched) 50% of the value obtained on unprestrained. unexposed test pieces... [Pg.361]

Figure I 3.22 Young s modulus vs. charpy impact strength at 23 °C (redrawn from Juan, P. et o/., SAE paper 980067). Figure I 3.22 Young s modulus vs. charpy impact strength at 23 °C (redrawn from Juan, P. et o/., SAE paper 980067).
Experimental standard and apparatus Impact strength is an important indicator to measure toughness property of rigid polyurethane material, which is in according to Plastics-Determination of charpy impact strength of rigid materials (GB/T 1043-93). [Pg.295]


See other pages where Impact strength Charpy is mentioned: [Pg.21]    [Pg.96]    [Pg.414]    [Pg.193]    [Pg.289]    [Pg.630]    [Pg.643]    [Pg.299]    [Pg.799]    [Pg.799]    [Pg.115]    [Pg.80]    [Pg.117]    [Pg.37]    [Pg.351]    [Pg.414]    [Pg.193]    [Pg.299]    [Pg.302]    [Pg.861]    [Pg.323]    [Pg.327]    [Pg.647]    [Pg.355]    [Pg.368]    [Pg.368]    [Pg.425]    [Pg.544]    [Pg.283]    [Pg.378]    [Pg.500]    [Pg.247]    [Pg.427]    [Pg.104]   
See also in sourсe #XX -- [ Pg.227 ]

See also in sourсe #XX -- [ Pg.36 , Pg.37 , Pg.403 ]

See also in sourсe #XX -- [ Pg.478 ]

See also in sourсe #XX -- [ Pg.358 , Pg.359 ]

See also in sourсe #XX -- [ Pg.478 ]




SEARCH



Charpy

© 2024 chempedia.info