Hoppers flow instabilities

The key to solving these problems is to design the vessel for a mass flow pattern. This involves consideration of both the hopper angle and surface finish, the effect of inserts used to introduce gas and control the solids flow pattern, and sizing the outlet valve to avoid arching and discharge rate limitations. In addition, the gas or liquid must be injected such that the solid particles are uniformly exposed to it, and flow instabilities such as fluidization in localized regions are avoided. 

In Sections 4.4 and 4.5, we dealt briefly with particulate flow instabilities in hoppers and the nonhomogeneous stress distributions created under uniaxial loading of a particulate assembly. In this section, we will expand on the discrete nature of such assemblies, and refer the reader to the computational and experimental tools that have been developed, and are rapidly advancing, to study such phenomena. 

In polymer processing practice, we need to ensure that the particulate gravitational mass flow rate of the hopper exceeds, over the complete operating range, the extruder open discharge rate (i.e., the rate without any die restriction). That is, hoppers must not be the production-rate limiting factor. Second, and more importantly, it is necessary for stable extrusion operations and extruded product quality that the flow be steady and free of instabilities of the particulate flow emerging from the hoppers. Finally, as we will see in Chapter 9, we need to know the pressure under the hopper in order to determine the pressure profile in a SSE. 

For uniform and stable extrusion it is important to check periodically the drive system, the take-up device, and other equipment, and compare it to its original performance. If variations are excessive, all kinds of problems will develop in the extruded product. An elaborate process-control system can help, but it is best to improve stability in all facets of the extrusion line. Some examples of instabilities and problem areas include 1) non-uniform plastics flow in the hopper 2) troublesome bridging, with excessive barrel heat that melts the solidified plastic in the hopper and feed section and stops the plastic flow 3) variations in barrel heat, screw heat, screw speed, the screw power drive, die heat, die head pressure, and the take-up device 4) insufficient melting or mixing capacity 5) insufficient pressure-generating capacity 6) wear or damage of the screw or barrel 7) melt fracture/sharkskin (see Chapter 2), and so on. 

---