Properties. One of the characteristic properties of the polyphosphazene backbone is high chain dexibility which allows mobility of the chains even at quite low temperatures. Glass-transition temperatures down to —105° C are known with some alkoxy substituents. Symmetrically substituted alkoxy and aryloxy polymers often exhibit melting transitions if the substituents allow packing of the chains, but mixed-substituent polymers are amorphous. Thus the mixed substitution pattern is deUberately used for the synthesis of various phosphazene elastomers. On the other hand, as with many other flexible-chain polymers, glass-transition temperatures above 100°C can be obtained with bulky substituents on the phosphazene backbone. [Pg.257]

Since successful commercialization of Kapton by Du Pont Company in the 1960s (10), numerous compositions of polyimide and various new methods of syntheses have been described in the Hterature (1—5). A successful result for each method depends on the nature of the chemical components involved in the system, including monomers, intermediates, solvents, and the polyimide products, as well as on physical conditions during the synthesis. Properties such as monomer reactivity and solubiHty, and the glass-transition temperature,T, crystallinity, T, and melt viscosity of the polyimide products ultimately determine the effectiveness of each process. Accordingly, proper selection of synthetic method is often critical for preparation of polyimides of a given chemical composition. [Pg.396]

Park et al. [20] reported on the synthesis of poly-(chloroprene-co-isobutyl methacrylate) and its compati-bilizing effect in immiscible polychloroprene-poly(iso-butyl methacrylate) blends. A copolymer of chloroprene rubber (CR) and isobutyl methacrylate (iBMA) poly[CP-Co-(BMA)] and a graft copolymer of iBMA and poly-chloroprene [poly(CR-g-iBMA)] were prepared for comparison. Blends of CR and PiBMA are prepared by the solution casting technique using THF as the solvent. The morphology and glass-transition temperature behavior indicated that the blend is an immiscible one. It was found that both the copolymers can improve the miscibility, but the efficiency is higher in poly(CR-Co-iBMA) than in poly(CR-g-iBMA),... [Pg.638]

Owing to multi-functionahty, physical properties such as solubihty and the glass transition temperature and chemical functionahty the hyperbranched (meth) acrylates can be controlled by the chemical modification of the functional groups. The modifications of the chain architecture and chemical structure by SCV(C)P of inimers and functional monomers, which may lead to a facile, one-pot synthesis of novel functionahzed hyperbranched polymers, is another attractive feature of the process. The procedure can be regarded as a convenient approach toward the preparation of the chemically sensitive interfaces. [Pg.33]

A simple algorithm [17] makes it possible to find the probability of any fragment of macromolecules of Gordonian polymers. Comparison of these probabilities with the data obtained by NMR spectroscopy provides the possibility to evaluate the adequacy of a chosen kinetic model of a synthesis process of a particular polymer specimen. The above-mentioned probabilities are also involved in the expressions for the glass transition temperature and some structure-additive properties of branched polymers [18,19]. [Pg.169]

V. Deimede, J.K. Kallitsis, and T. Pakula, Synthesis and properties of amorphous blue-light-emitting polymers with high glass-transition temperatures, J. Polym. Sci., Part A Polym. Chem., 39 3168-3179, 2001. [Pg.288]

Subsequently, Devia came to the U.S. to continue the research. A SIN type synthesis was selected because it offered two advantages ease in processing and a lower glass transition temperature, Tg, of the rubber product. As shall be seen from the following, the IPN and SIN synthesis yield quite different materials, even if the chemistry is nominally the same. However, since the earlier work has already been described, the following will emphasize the SIN synthesis (19-22). [Pg.408]

The key to a controlled molecular weight build-up, which leads to the control of product properties such as glass transition temperature and melt viscosity, is the use of a molar excess of diisopropanolamine as a chain stopper. Thus, as a first step in the synthesis process, the cyclic anhydride is dosed slowly to an excess of amine to accommodate the exothermic reaction and prevent unwanted side reactions such as double acylation of diisopropanolamine. HPLC analysis has shown that the reaction mixture after the exothermic reaction is quite complex. Although the main component is the expected acid-diol, unreacted amine and amine salts are still present and small oligomers already formed. In the absence of any catalyst, a further increase of reaction temperature to 140-180°C leads to a rapid polycondensation. The expected amount of water is distilled (under vacuum, if required) from the hot polymer melt in approximately 2-6 h depending on the anhydride used. At the end of the synthesis the concentration of carboxylic acid groups value reaches the desired low level. [Pg.48]

The inorganic poly(phosphazene) backbone has received attention as a PEM candidate. This is an attractive system for study due to its ease of synthesis and subsequent modification by many functional groups. However, these membranes generally show low glass transition temperatures and somewhat poor mechanical properties, and they require cross-linking to enhance their performance in hydrated environments. [Pg.370]

Much attention has been paid to the synthesis of fluorine-containing condensation polymers because of their unique properties (43) and different classes of polymers including polyethers, polyesters, polycarbonates, polyamides, polyurethanes, polyimides, polybenzimidazoles, and epoxy prepolymers containing pendent or backbone-incorporated bis-trifluoromethyl groups have been developed. These polymers exhibit promise as film formers, gas separation membranes, seals, soluble polymers, coatings, adhesives, and in other high temperature applications (103,104). Such polymers show increased solubility, glass-transition temperature, flame resistance, thermal stability, oxidation and environmental stability, decreased color, crystallinity, dielectric constant, and water absorption. [Pg.539]

Table 1 lists the glass transition temperatures for the pertinent siloxane oligomers as a function of TFP and DP contents. The percent of each comonomer is recorded with reference to the siloxane units as well as the entire oligomer. One notes the difference that this creates between the two nominally 100% TFP siloxanes of different molecular weight. Note also the higher Tg values for the DP series at equal weight percents, a factor which limits their ease of synthesis and may affect their mobility during cure. [Pg.89]


See other pages where Glass transition temperature synthesis is mentioned: [Pg.531]    [Pg.539]    [Pg.270]    [Pg.332]    [Pg.401]    [Pg.28]    [Pg.287]    [Pg.1215]    [Pg.533]    [Pg.535]    [Pg.276]    [Pg.308]    [Pg.40]    [Pg.60]    [Pg.63]    [Pg.106]    [Pg.224]    [Pg.17]    [Pg.310]    [Pg.480]    [Pg.64]    [Pg.163]    [Pg.108]    [Pg.168]    [Pg.178]    [Pg.458]    [Pg.459]    [Pg.462]    [Pg.463]    [Pg.464]    [Pg.18]    [Pg.78]    [Pg.306]    [Pg.46]    [Pg.110]    [Pg.311]    [Pg.71]    [Pg.65]    [Pg.531]   
See also in sourсe #XX -- [ Pg.89 , Pg.90 , Pg.91 , Pg.92 ]




SEARCH



Polymer synthesis glass transition temperatures

Transition synthesis

© 2024 chempedia.info