An essential work of fracture (EWF) analysis of PPG was performed using PPGs of various Mn [21]. It was found that, independent of the Mn, load versus displacement curves are similar and can thus be compared. A significant amount of plastic... 

Wang XL, Li RKY, Cao YX, Meng YZ (2005) Essential work of fracture analysis of poly (propylene carbonate) with varying molecular weight Polym Test 24 699-703... 

When fracture occurs out of the linear domain (fracture with yielding), e.g., for highly toughened thermosets or at high temperatures, it is still possible to apply fracture mechanics, with the energetic theory. For instance, the J-integral may be used for bulk materials (Williams, 1984) or Essential Work for Fracture for thin films (Mai and Powell, 1991 Liu and Nairn, 1998). 

Toughness, modifier, polyethylene terephthalate, core-shell, essential work of fracture... 

This technique were used because of its simplicity and its ability to qualitatively decompose the energy at rupture into its two intrinsic components energy for creating new surfaces (essential work of fracture. We) and "plastic" work, or more seemingly dissipated energy due to the deformation of the bulk. 

Fig. 7. Essential work of fracture. Comparison between semi-crystalline (a) and amorphous PET (b). ( ) Non blended PET ( ) PET with 21 % of NR (A)PET with 21 % of R.

Table 2. Essential work of fracture Values for the parameters...

Essential work of fracture measurements clearly show that this efficiency always corresponds to a significant increase in the apparent plastic work, whereas essential work of rupture remains low. This observation suggests that toughening results from an additional process induced by the particles. 

ESSENTIAL WORK OF FRACTURE OF INJECTION MOULDED SAMPLES OF PET AND PET/PC BLENDS... 

PET, PET/PC Blends, Essential Work of Fracture (EWF), Injection Mould, Orientation... 

Essential Work of Fracture of Injection Moulded Samples of PET and PET/PC Blends 79... 

Fig. 8. Essential components (Wc and We") from the partitioning as a function of global essential work of fracture (we) for PET/PC blends. Solid and dashed lines represent the trends followed.

RATE AND TEMPERATURE EFFECTS ON THE PLANE STRESS ESSENTIAL WORK OF FRACTURE IN SEMICRYSTALLINE PET... 

It can be seen from Fig. 5 that as the temperature rises the specific essential work of fracture term (Wg) slightly decreases from 41.6 kJ/m at 0°C to 35.6 kJ/m at 70°C. On the other hand, the specific non-essential parameter ( 3wp) steadily increases with temperature from 4.7 MJ/m ... 

From the data reported in Fig. 6, it can be seen that the specific essential work of fracture term is practically insensitive to displacement rate up to 500 mm/min (being its value slightly oscillating around 40 kJ/m ) and that a marked increase (up to 63.7 kJ/m ) occurs only under impact conditions. The specific non-essential parameter gradually increases with loading rate from 5.2 MJ/m to 18.5 MJ/m. Again, this behaviour is consistent with previous literature data obtained by Arkhireyeva and Hashemi [18] for a similar material over a much narrow displacement rate interval (from 2 to 50 mm/min). 

Fig. 8. Effect of displacement rate on the yielding (Wg y) and the necking/tearing (Wg related parts of the specific essential work of fracture at various temperatures.

---