Enantiomers monomers

In 1962, Inoue et al [140, 141], first succeeded in carrying out an asymmetric selective polymerization of /-propylene oxide (J,/-PO) using dialkylzinc-optically active (+)-borneol or (-)-menthol catalysts with a conversion of 30% (Scheme LVIII) the polymer was found to be optically active, levorotatory in benzene solution and dextrorotatory in chloroform, like the polymer obtained by Price [92] from the purified /-enantiomer monomer. There were no absorption bands corresponding to the original alcohol detected in the IR spectrum and the optical activity of the polymer must, therefore, be attributed to the prevalence of one of the two enantiomeric units. 

Oligomer (Section 14 15) A molecule composed of too few monomer units for it to be classified as a polymer but more than in a dimer trimer tetramer etc Oligonucleotide (Section 28 6) A polynucleotide containing a relatively small number of bases Oligosaccharide (Section 25 1) A carbohydrate that gives three to ten monosacchandes on hydrolysis Optical activity (Section 7 4) Ability of a substance to rotate the plane of polanzed light To be optically active a sub stance must be chiral and one enantiomer must be present in excess of the other... 

Figure 1.3 Molecular models showing the two enantiomers resulting from the loss of mirror plane symmet7 on adsorption with the molecular plane parallel to the substrate. The separation of enantiomers observed by STM is identified by the relative displacement of adjacent monomers within the double chain. (Reprinted with permission from Ref. [6]. Copyright 2001, American Physical Society.)...

The chiral sites which are able to rationalize the isospecific polymerization of 1-alkenes are also able, in the framework of the mechanism of the chiral orientation of the growing polymer chain, to account for the stereoselective behavior observed for chiral alkenes in the presence of isospecific heterogeneous catalysts.104 In particular, the model proved able to explain the experimental results relative to the first insertion of a chiral alkene into an initial Ti-methyl bond,105 that is, the absence of discrimination between si and re monomer enantiofaces and the presence of diastereoselectivity [preference for S(R) enantiomer upon si (re) insertion]. Upon si (re) coordination of the two enantiomers of 3-methyl-l-pentene to the octahedral model site, it was calculated that low-energy minima only occur when the conformation relative to the single C-C bond adjacent to the double bond, referred to the hydrogen atom bonded to the tertiary carbon atom, is nearly anticlinal minus, A- (anticlinal plus, A+). Thus one can postulate the reactivity only of the A- conformations upon si coordination and of the A+ conformations upon re coordination (Figure 1.16). In other words, upon si coordination, only the synperiplanar methyl conformation would be accessible to the S enantiomer and only the (less populated) synperiplanar ethyl conformation to the R enantiomer this would favor the si attack of the S enantiomer with respect to the same attack of the R enantiomer, independent of the chirality of the catalytic site. This result is in agreement with a previous hypothesis of Zambelli and co-workers based only on the experimental reactivity ratios of the different faces of C-3-branched 1-alkenes.105... 

Fig. 21. Molecular imprinting of (R)-propranolol using methacrylic acid (MAA) as the functional monomer and trimethylolpropane trimethacrylate (TRIM) as the crosslinking monomer. (Reprinted with permission from [126], Copyright 1998 Elsevier). The enantiose-lectivity of a given polymer is predetermined by the configuration of the ligand, R-propranolol present during its preparation. Since the imprinted enantiomer possesses a higher affinity for the polymer, the separation is obtained with a predictable elution order of the enantiomers...

Their studies involved the partial polymerization of NCAs of mixtures of specific amino adds having known e.e.s, followed by determination of the e.e.s of the amino adds in both the resulting polypeptides and in the residual unreacted NCA monomers. [94] In a typical experiment it was found that when an optically impure leucine NCA monomer having an l > d e.e. of 31.2% was polymerized to the extent of 52 % to the helical polyleucine peptide, the e.e. of the polymer was enhanced to 45.4 %, an increase of 14.2 %. In the same experiment the e.e. of the unreacted leucine NCA monomer was depleted to a similar extent. Analogous experiments with valine NCAs of known e.e.s, however, led to a reverse effect, namely, the preferential incorporation of the racemate rather than one enantiomer into the growing polyvaline peptide. This finding was interpreted to be the result of the fact that polyvaline consists of (3-sheets rather than a-helices, emphasizing that the Wald mechanism applies only to a-helix polymers. At about the same time Brach and Spach [95] showed that, under proper conditions, (3-sheet polymers could also be implicated in the amplification of amino add e.e.s. 

Vlhen the chiral methylation is carried out with 30% aqueous NaOH the indanone is deprotonated at the interface but does not precipitate as the sodium enolate (Figure 11). In this system there are 3 to 4 molecules of H2O per molecule of catalyst available while in the 50% NaOH reactions the toluene is very dry with only 1 molecule of H2O available per catalyst molecule thus forcing the formation of tight ion pairs. Solvation of the ion pairs in the toluene/30% NaOH system should decrease the ee which we indeed observe with an optimum 78% versus 94% in the 50% NaOH reaction. In the 30% NaOH reactions the ee decreases from 78% to 55% as the catalyst concentration increases from 1 mM to 16 mM (80 mM 5, 560 mM CH3CI, 20 C). Based on these ee s rates of formation of (-h)-enantiomer and racemic product can be calculated. When the log of these rates are plotted versus the log of catalyst concentrations (Figure 13) we find an order of about 0.5 in the catalyst for the chiral process similar to that found using 50% NaOH consistent with a dimer-monomer pre-equilibrium. The order in catalyst for the... 

Molecular imprinted polymers MIPs exhibit predetermined enan-tioselectivity for a specific chiral molecnle, which is nsed as the chiral template dnring the imprinting process. Most MIPs are obtained by copolymerization from a mixture consisting of a fnnctional mono-nnsatn-rated (vinylic, acrylic, methacrylic) monomer, a di- or tri-nnsatnrated cross-linker (vinylic, acrylic, methacrylic), a chiral template (print molecnle) and a porogenic solvent to create a three-dimensional network. When removing the print molecnle, chiral cavities are released within the polymer network. The MIP will memorize the steric and functional binding featnres of the template molecnle. Therefore, inclusion of the enantiomers into the asymmetric cavities of this network can be assumed as... 

---