Differential Scanning Calorimetry DSC Technique

Temperature-rising elution fractionation (tref) is a technique for obtaining fractions based on short-chain branch content versus molecular weight (96). On account of the more than four days of sample preparation required, stepwise isothermal segregation (97) and solvated thermal analysis fractionation (98) techniques using variations of differential scanning calorimetry (dsc) techniques have been developed. 

The gelatinization process can be observed by the differential scanning calorimetry (DSC) technique. Depending on the amount of water present in the system, several endotherm peaks can be detected (Figure 2.2). If the water volume fraction is significantly above 0.45 (conditions that can be referred to gelatinization) a single endotherm peak, pointed as G is observed [11]. 

Differential Scanning Calorimetry (DSC) Technique in which the difference in the amotmt of heat required to increase the temperature of a sample being analyzed and a reference sample, are measured as a function of temperature... 

The differential scanning calorimetry (DSC) technique is probably the most widely used thermal analysis technique in polymer science. It determines in a quantitative way the amount of heat absorbed or evolved by a sample as compared to a reference during a specific thermal transition (which could be a first-order or second-order transition). The changes experienced by the thermal properties of the samples can be determined isothermally as a function of time or at a constant heating or cooling rate as a function of temperature [1,2]. 

The process known as transimidization has been employed to functionalize polyimide oligomers, which were subsequentiy used to produce polyimide—titania hybrids (59). This technique resulted in the successhil synthesis of transparent hybrids composed of 18, 37, and 54% titania. The effect of metal alkoxide quantity, as well as the oligomer molecular weight and cure temperature, were evaluated using differential scanning calorimetry (dsc), thermogravimetric analysis (tga) and saxs. 

Most hydrocarbon resins are composed of a mixture of monomers and are rather difficult to hiUy characterize on a molecular level. The characteristics of resins are typically defined by physical properties such as softening point, color, molecular weight, melt viscosity, and solubiHty parameter. These properties predict performance characteristics and are essential in designing resins for specific appHcations. Actual characterization techniques used to define the broad molecular properties of hydrocarbon resins are Fourier transform infrared spectroscopy (ftir), nuclear magnetic resonance spectroscopy (nmr), and differential scanning calorimetry (dsc). 

Thermal analysis iavolves techniques ia which a physical property of a material is measured agaiast temperature at the same time the material is exposed to a coatroUed temperature program. A wide range of thermal analysis techniques have been developed siace the commercial development of automated thermal equipment as Hsted ia Table 1. Of these the best known and most often used for polymers are thermogravimetry (tg), differential thermal analysis (dta), differential scanning calorimetry (dsc), and dynamic mechanical analysis (dma). 

Transitions such as T and are rapidly and conveniently studied using differential scanning calorimetry (dsc). This technique monitors changes in... 

Difl erential thermal analysis (DTA) and differential scanning calorimetry (DSC) are the other mainline thermal techniques. These are methods to identify temperatures at which specific heat changes suddenly or a latent heat is evolved or absorbed by the specimen. DTA is an early technique, invented by Le Chatelier in France in 1887 and improved at the turn of the century by Roberts-Austen (Section 4.2.2). A... 

In general, X-ray data are used in conjunction with other techniques to obtain as full a picture as possible. For liquid-crystalline materials, differential scanning calorimetry (DSC) and polarizing optical microscopy (POM) are conventionally used. 

The techniques referred to above (Sects. 1—3) may be operated for a sample heated in a constant temperature environment or under conditions of programmed temperature change. Very similar equipment can often be used differences normally reside in the temperature control of the reactant cell. Non-isothermal measurements of mass loss are termed thermogravimetry (TG), absorption or evolution of heat is differential scanning calorimetry (DSC), and measurement of the temperature difference between the sample and an inert reference substance is termed differential thermal analysis (DTA). These techniques can be used singly [33,76,174] or in combination and may include provision for EGA. Applications of non-isothermal measurements have ranged from the rapid qualitative estimation of reaction temperature to the quantitative determination of kinetic parameters [175—177]. The evaluation of kinetic parameters from non-isothermal data is dealt with in detail in Chap. 3.6. 

A number of analytical techniques such as FTIR spectroscopy,65-66 13C NMR,67,68 solid-state 13 C NMR,69 GPC or size exclusion chromatography (SEC),67-72 HPLC,73 mass spectrometric analysis,74 differential scanning calorimetry (DSC),67 75 76 and dynamic mechanical analysis (DMA)77 78 have been utilized to characterize resole syntheses and crosslinking reactions. Packed-column supercritical fluid chromatography with a negative-ion atmospheric pressure chemical ionization mass spectrometric detector has also been used to separate and characterize resoles resins.79 This section provides some examples of how these techniques are used in practical applications. 

ADMET polymers are easily characterized using common analysis techniques, including nuclear magnetic resonance ( H and 13C NMR), infrared (IR) spectra, elemental analysis, gel permeation chromatography (GPC), vapor pressure osmometry (VPO), membrane osmometry (MO), thermal gravimetric analysis (TGA), and differential scanning calorimetry (DSC). The preparation of poly(l-octenylene) (10) via the metathesis of 1,9-decadiene (9) is an excellent model polymerization to study ADMET, since the monomer is readily available and the polymer is well known.21 The NMR characterization data (Fig. 8.9) for the hydrogenated versions of poly(l-octenylene) illustrate the clean and selective nature of ADMET. 

Thermoanalytical techniques such as differential scanning calorimetry (DSC) and thermogravi-metric analysis (TGA) have also been widely used to study rubber oxidation [24—27]. The oxidative stability of mbbers and the effectiveness of various antioxidants can be evaluated with DSC based on the heat change (oxidation exotherm) during oxidation, the activation energy of oxidation, the isothermal induction time, the onset temperamre of oxidation, and the oxidation peak temperature. 

The progress of polymer degradation may be followed by a wide variety of techniques, some of them being mentioned at the right column in the Bolland-Gee scheme (Scheme 2). There are techniques that directly monitor some of the elementary reaction steps such as, for example, oxygen absorption (reaction 2), differential scanning calorimetry (DSC) (reaction 3), chemiluminescence (reaction 11) analytical and/or spectral methods of determination of hydroperoxides, etc. 

Another important technique is the thermal analysis technique of differential scanning calorimetry (DSC). Current high-speed DSC equipment (sometimes also referred to as hyper-DSC) allows for rapid heating (up to 500°C/min) and cooling of (small) samples and therefore an increased rate of analysis per sample... 

---