Deuterated polymer blend films

Using FRES and others techniques, Wang and Composto investigated wetting and phase separation in polymer blend films composed of deuterated poly(methyl methacrylate) (d-PMMA) and poly(styrene-raw-acrylonitrile) (h-SAN) at the critical concentration [176-180]. This blend is characterized by a lower critical solution temperature (LCST) behavior with Tlcst 160 °C and 0d-PMMA 0.5 [180]. In this... 

Surface-directed spinodal decomposition was first observed in an isotopic polymer blend (Jones et al. 1991) thin films of a mixture of poly(ethylene-propylene) and its deuterated analogue were annealed below the upper critical solution temperature and the depth profiles measured using forward recoil spectrometry, to reveal oscillatory profiles similar to those sketched in figure 5.30. Similar results have now been obtained for a number of other polymer blends, including polystyrene with partially brominated polyst)u-ene (Bruder and Brenn 1992), polystyrene with poly(a-methyl styrene) (Geoghegan et al. 1995) and polystyrene with tetramethylbisphenol-A polycarbonate (Kim et al. 1994), suggesting that the phenomenon is rather general. 

Bruder and Brenn (1992) studied the spinodal decomposition in thin films of a blend of deuterated polystyrene (dPS) and poly(styrene-co-4-bromostyrene) (PBrxS) by TOF-ERDA. They examined the effect of different substrates on the decomposition process. In one series of experiments, a solution of the polymers in toluene was spread on a silicon wafer to form a film of thickness 550 nm which was then heated in vacuum at 180°C for various times. 

Zink et al. used a blend of polystyrene (hPS) and its deuterated counterpart (dPS), both of molecular weight 1.95 x 106 (abbreviated 1.95 M). The average volume fraction (4>dPS) of deuterated polystyrene was 30%. The polymers were dissolved in toluene and spin cast on thin silicon wafers (about 10 x 10 mm), the resulting film thickness being about 300 nm. The samples were annealed at 245°C for 8 days, and the measurement of the resulting depth profiles was conducted by NRA using a monoenergetic 700 keV 3He beam. The nuclear reaction employed can be written ... 

The bilayer morphology of thin asymmetric films of may be unstable. A regularly corrugated surface structure of the films was ascribed to spinodal transition into a laterally phase separated structure, where the surface morphology depended on the polymer incompatibility and the interfacial interactions [347, 348]. Recently, the phase separation and dewetting of thin films of a weakly incompatible blend of deuterated PS and poly(p-methylstyrene) have been monitored by SFM [349, 350]. Starting from a bilayer structure, after 454 h at T= 154 °C the film came to the final dewetting state where mesoscopic drops of... 

The use of Small-Angle Neutron Scattering (SANS) has been exponentially increasing for the study of polymers, largely of elastomers and nanopolymers, for the last 40 years [198]. Matsuba et al. [199] worked on an isotropic blend of deuterated PE and hydrogenated polyethylene (HPE 3 wt%) during uniaxial drawing at 125°C to understand the formation mechanism of the shish kebab from the isotropic film. In the early... 

---