A brief review has appeared covering the use of metal-free initiators in living anionic polymerizations of acrylates and a comparison with Du Font s group-transfer polymerization method (149). Tetrabutylammonium thiolates mn room temperature polymerizations to quantitative conversions yielding polymers of narrow molecular weight distributions in dipolar aprotic solvents. Block copolymers are accessible through sequential monomer additions (149—151) and interfacial polymerizations (152,153). 

The earliest SIS block copolymers used in PSAs were nominally 15 wt% styrene, with an overall molecular weight on the order of 200,000 Da. The preparation by living anionic polymerization starts with the formation of polystyryl lithium, followed by isoprene addition to form the diblock anion, which is then coupled with a difunctional agent, such as 1,2-dibromoethane to form the triblock (Fig. 5a, path i). Some diblock material is inherently present in the final polymer due to inefficient coupling. The diblock is compatible with the triblock and acts... 

A polymer-bound hindered amine light stabilizer [P-HALS] has been synthesized by terminating the living anionic polymerization of isoprene with 4(2,3-epoxy pro-poxy)-1,2,2,6,6-pentamethylpiperidine followed by hydrogenation of the resulting polymer to E-P copolymer using Zeigler type catalyst [40] ... 

Many block and graft copolymer syntheses involving transformation reactions have been described. These involve preparation of polymeric species by a mechanism that leaves a terminal functionality that allows polymerization to be continued by another mechanism. Such processes are discussed in Section 7.6.2 for cases where one of the steps involves conventional radical polymerization. In this section, we consider cases where at least one of the steps involves living radical polymerization. Numerous examples of converting a preformed end-functional polymer to a macroinitiator for NMP or ATRP or a macro-RAFT agent have been reported.554 The overall process, when it involves RAFT polymerization, is shown in Scheme 9.60. 

Vinyl copolymers contain mers from two or more vinyl monomers. Most common are random copolymers that are formed when the monomers polymerize simultaneously. They can be made by most polymerization mechanisms. Block copolymers are formed by reacting one monomer to completion and then replacing it with a different monomer that continues to add to the same polymer chain. The polymerization of a diblock copolymer stops at this point. Triblock and multiblock polymers continue the polymerization with additional monomer depletion and replenishment steps. The polymer chain must retain its ability to grow throughout the process. This is possible for a few polymerization mechanisms that give living polymers. 

In a batch reactor, the relative monomer concentrations will change with time because the two monomers react at different rates. For polymerizations with a short chain life, the change in monomer concentration results in a copolymer composition distribution where polymer molecules formed early in the batch will have a different composition from molecules formed late in the batch. For living polymers, the drift in monomer composition causes a corresponding change down the growing chain. This phenomenon can be used advantageously to produce tapered block copolymers. 

A porphinatoaluminum alkoxide is reported to be a superior initiator of c-caprolactone polymerization (44,45). A living polymer with a narrow molecular weight distribution (M /Mjj = 1.08) is ob-tmned under conditions of high conversion, in part because steric hindrance at the catalyst site reduces intra- and intermolecular transesterification. Treatment with alcohols does not quench the catalytic activity although methanol serves as a coinitiator in the presence of the aluminum species. The immortal nature of the system has been demonstrated by preparation of an AB block copolymer with ethylene oxide. The order of reactivity is e-lactone > p-lactone. 

In both anionic and cationic polymerization it is possible to create living polymers . In this process, we starve the reacting species of monomer. Once the monomer is exhausted, the terminal groups of the chains are still activated. If we add more monomer to the reaction vessel, chain groivth will restart. This technique provides us with a uniquely controllable system in which we can add different monomers to living chains to create block copolymers. 

A radical initiator based on the oxidation adduct of an alkyl-9-BBN (47) has been utilized to produce poly(methylmethacrylate) (48) (Fig. 31) from methylmethacrylate monomer by a living anionic polymerization route that does not require the mediation of a metal catalyst. The relatively broad molecular weight distribution (PDI = (MJM ) 2.5) compared with those in living anionic polymerization cases was attributed to the slow initiation of the polymerization.69 A similar radical polymerization route aided by 47 was utilized in the synthesis of functionalized syndiotactic polystyrene (PS) polymers by the copolymerization of styrene.70 The borane groups in the functionalized syndiotactic polystyrenes were transformed into free-radical initiators for the in situ free-radical graft polymerization to prepare s-PS-g-PMMA graft copolymers. 

Polymer Synthesis and Characterization. This topic has been extensively discussed in preceeding papers.(2,23,24) However, we will briefly outline the preparative route. The block copolymers were synthesized via the sequential addition method. "Living" anionic polymerization of butadiene, followed by isoprene and more butadiene, was conducted using sec-butyl lithium as the initiator in hydrocarbon solvents under high vacuum. Under these conditions, the mode of addition of butadiene is predominantly 1,4, with between 5-8 mole percent of 1,2 structure.(18) Exhaustive hydrogenation of polymers were carried out in the presence of p-toluenesulfonylhydrazide (19,25) in refluxing xylene. The relative block composition of the polymers were determined via NMR. 

Further work related to the synthesis of copolymers with either P2VP or P4VP blocks has been reported in the literature. Triblock terpolymers PS-fc-P2VP-fo-PEO were synthesized in THF at - 78 °C by sequential polymerization of styrene and 2VP, initiated by s-BuLi in the presence of IiCl [25]. The living polymer was terminated with EO. The end-hydroxyl group was... 

Hyperbranched polymers have also been prepared via living anionic polymerization. The reaction of poly(4-methylstyrene)-fo-polystyrene lithium with a small amount of divinylbenzene, afforded a star-block copolymer with 4-methylstyrene units in the periphery [200]. The methyl groups were subsequently metalated with s-butyllithium/tetramethylethylenediamine. The produced anions initiated the polymerization of a-methylstyrene (Scheme 109). From the radius of gyration to hydrodynamic radius ratio (0.96-1.1) it was concluded that the second generation polymers behaved like soft spheres. 

The production of olefin block copolymers has been an aspiration of academic researchers and polymer manufacturers alike. Tremendous progress toward this end has been achieved in recent years with the discovery of several designer catalysts capable of living olefin polymerization. However, the stoichiometric nature of the living process, coupled with related process limitations of low polymerization temperatures and slow batch processes, have precluded these approaches from widespread application. 

---