Living polymers copolymers

Block copolymers are closer to blends of homopolymers in properties, but without the latter s tendency to undergo phase separation. As a matter of fact, diblock copolymers can be used as surfactants to bind immiscible homopolymer blends together and thus improve their mechanical properties. Block copolymers are generally prepared by sequential addition of monomers to living polymers, rather than by depending on the improbable rjr2 > 1 criterion in monomers. 

When the initial monomer supply is exhausted, the anionic chain ends retain their activity. Thus, these anionic chains have been termed living polymers. If more monomer is added, they resume propagation. If it is a second monomer, the result is a block copolymer. 

In the absence of impurities there is frequently no termination step in anionic polymerisations. Hence the monomer will continue to grow until all the monomer is consumed. Under certain conditions addition of further monomer, even after an interval of several weeks, will eause the dormant polymerisation process to proceed. The process is known as living polymerisation and the products as living polymers. Of particular interest is the fact that the follow-up monomer may be of a different species and this enables block copolymers to be produced. This technique is important with certain types of thermoplastic elastomer and some rather specialised styrene-based plastics. 

Ion coupling of anionic and cationic living polymers is an interesting procedure for the synthesis of a well-defined block copolymer. Attempted coupling of the polystyrene anion with the poly-THF cation initiated by triethyloxonium tetrafluoro-borate yielded a block copolymer mixed with homopolymers394. The block ef-... 

Vinyl copolymers contain mers from two or more vinyl monomers. Most common are random copolymers that are formed when the monomers polymerize simultaneously. They can be made by most polymerization mechanisms. Block copolymers are formed by reacting one monomer to completion and then replacing it with a different monomer that continues to add to the same polymer chain. The polymerization of a diblock copolymer stops at this point. Triblock and multiblock polymers continue the polymerization with additional monomer depletion and replenishment steps. The polymer chain must retain its ability to grow throughout the process. This is possible for a few polymerization mechanisms that give living polymers. 

In a batch reactor, the relative monomer concentrations will change with time because the two monomers react at different rates. For polymerizations with a short chain life, the change in monomer concentration results in a copolymer composition distribution where polymer molecules formed early in the batch will have a different composition from molecules formed late in the batch. For living polymers, the drift in monomer composition causes a corresponding change down the growing chain. This phenomenon can be used advantageously to produce tapered block copolymers. 

A porphinatoaluminum alkoxide is reported to be a superior initiator of c-caprolactone polymerization (44,45). A living polymer with a narrow molecular weight distribution (M /Mjj = 1.08) is ob-tmned under conditions of high conversion, in part because steric hindrance at the catalyst site reduces intra- and intermolecular transesterification. Treatment with alcohols does not quench the catalytic activity although methanol serves as a coinitiator in the presence of the aluminum species. The immortal nature of the system has been demonstrated by preparation of an AB block copolymer with ethylene oxide. The order of reactivity is e-lactone > p-lactone. 

In both anionic and cationic polymerization it is possible to create living polymers . In this process, we starve the reacting species of monomer. Once the monomer is exhausted, the terminal groups of the chains are still activated. If we add more monomer to the reaction vessel, chain groivth will restart. This technique provides us with a uniquely controllable system in which we can add different monomers to living chains to create block copolymers. 

What is a living polymer What sort of copolymer can be made from it ... 

Further work related to the synthesis of copolymers with either P2VP or P4VP blocks has been reported in the literature. Triblock terpolymers PS-fc-P2VP-fo-PEO were synthesized in THF at - 78 °C by sequential polymerization of styrene and 2VP, initiated by s-BuLi in the presence of IiCl [25]. The living polymer was terminated with EO. The end-hydroxyl group was... 

Another type of copolymer is a block copolymer. Here a low molecular weight polymer may be extended by reaction with a new monomer. Recall that we talked about living polymers in this Chapter, Section 2.3. If, for example, we polymerized styrene alone first, then added some butadiene and polymerized it further, we would have a number of styrene units bundled together and a number of butadienes also together. 

No formal termination is given in structure 5.42 because in the absence of contaminants the product is a stable macroanion. Szwarz named such stable active species living polymers. These macroanions or macrocarbanions have been used to produce block copolymers such as Kraton. Kraton is an ABA block copolymer of styrene (A) and butadiene (B) (structure 5.43). Termination is brought about by addition of water, ethanol, carbon dioxide, or oxygen. 

The stability of polystyryl carbanions is greatly decreased in polar solvents such as ethers. In addition to hydride elimination, termination in ether solvents proceeds by nucleophilic displacement at the C—O bond of the ether. The decomposition rate of polystyryllithium in THF at 20°C is a few percent per minute, but stability is significantly enhanced by using temperatures below 0°C [Quirk, 2002], Keep in mind that the stability of polymeric carbanions in the presence of monomers is usually sufficient to synthesize block copolymers because propagation rates are high. The living polymers of 1,3-butadiene and isoprene decay faster than do polystyryl carbanions. 

Difunctional initiators such as sodium naphthalene are useful for producing ABA, BABAB, CAB AC, and other symmetric block copolymers more efficiently by using fewer cycles of monomer additions. Difunctional initiators can also be prepared by reacting a diene such as /n-diisoprope ny I benzene or l,3-bis(l-phenylethenyl)benzene with 2 equiv of butyl-lithium. Monomer B is polymerized by a difunctional initiator followed by monomer A. A polymerizes at both ends of the B block to form an ABA triblock. BABAB or CABAC block copolymers are syntehsized by the addition of monomer B or C to the ABA living polymer. The use of a difunctional initiator is the only way to synthesize a MMA-styrene-MMA triblock polymer since MMA carbanion does not initiate styrene polymerization (except by using a coupling reaction—Sec. 5-4c). 

The polydispersity of polymers prepared in this way is usually very low for example, a value MJM of 1.05 was found for a sample of poly(a-methylsty-rene). Living polymers can also be used for the preparation of block copolymers after the consumption of the first monomer, a second anionically polymerizable monomer is added which then grows onto both ends of the initially formed block. By termination of the living polymer with electrophilic compounds the polymer chains can be provided with specific end groups for example, living polystyrene reacts with carbon dioxide to give polystyrene with carboxylic end groups. 

Polyethers are prepared by the ring opening polymerization of three, four, five, seven, and higher member cyclic ethers. Polyalkylene oxides from ethylene or propylene oxide and from epichlorohydrin are the most common commercial materials. They seem to be the most reactive alkylene oxides and can be polymerized by cationic, anionic, and coordinated nucleophilic mechanisms. For example, ethylene oxide is polymerized by an alkaline catalyst to generate a living polymer in Figure 1.1. Upon addition of a second alkylene oxide monomer, it is possible to produce a block copolymer (Fig. 1.2). 

Living polymers have been extensively investigated by Szwarc and coworkers [3], who have shown that the formed polymer can spontaneously resume its growth on addition of the same or different fresh monomer. Block copolymers are easily synthesized by this technique. The lack of self-termination is overcome by the addition of proton donators, carbon dioxide, or ethylene oxide. 

---