Colloidal dispersions preparation

Fig. 9.2.11 TEM images of monodisperse colloidal dispersions prepared by heterogeneous nucleation with Pt as nucleating agent (A) Co15Ni6, dm = 50 nm, cr = 0.10dm. (B) Co8oNi2o, dm = 7 nm, Fig. 9.2.11 TEM images of monodisperse colloidal dispersions prepared by heterogeneous nucleation with Pt as nucleating agent (A) Co15Ni6, dm = 50 nm, cr = 0.10dm. (B) Co8oNi2o, dm = 7 nm, <r = 0.26dm. (a from Ref. 34.)...
ZINC SULFIDE COLLOIDAL DISPERSIONS PREPARED VIA INTERPHASE SYNTHESIS AND THEIR OPTICAL PROPERTIES... [Pg.320]

Thus, the feasible reason of the distinctions observed in UV-vis spectrum of the Ag-Au colloidal dispersions prepared by different techniques is the interaction of nanoparticles and functional groups of poly-N-(epoxypropyl)-carbazole. [Pg.339]

In Sec. 3 our presentation is focused on the most important results obtained by different authors in the framework of the rephca Ornstein-Zernike (ROZ) integral equations and by simulations of simple fluids in microporous matrices. For illustrative purposes, we discuss some original results obtained recently in our laboratory. Those allow us to show the application of the ROZ equations to the structure and thermodynamics of fluids adsorbed in disordered porous media. In particular, we present a solution of the ROZ equations for a hard sphere mixture that is highly asymmetric by size, adsorbed in a matrix of hard spheres. This example is relevant in describing the structure of colloidal dispersions in a disordered microporous medium. On the other hand, we present some of the results for the adsorption of a hard sphere fluid in a disordered medium of spherical permeable membranes. The theory developed for the description of this model agrees well with computer simulation data. Finally, in this section we demonstrate the applications of the ROZ theory and present simulation data for adsorption of a hard sphere fluid in a matrix of short chain molecules. This example serves to show the relevance of the theory of Wertheim to chemical association for a set of problems focused on adsorption of fluids and mixtures in disordered microporous matrices prepared by polymerization of species. [Pg.294]

We prepared ceria on Ni substrate by sol-gel coating method. Ceria sol solution was prepared with ceria sol solution (Alfa, 20% in H2O, colloidal dispersion) mixed with ethanol (99.9%, Hayman) with weight ratio (1 2) and stirred. Ceria was deposited on Ni substrate by dip coating method. The variation number of dipping was carried out to obtain different coating ratio. The anode was completely dipped into the ceria sol solution for several seconds and dried at a temperature of 50 C for 24 hours in air atmosphere followed by calcination at 700 C for 30 minutes in 5%H2-N2 atmosphere. [Pg.601]

Carotenoids are also present in animal products such as eggs, lobsters, greyflsh, and various types of hsh. In higher plants, they occur in photosynthetic tissues and choloroplasts where their color is masked by that of the more predominant green chlorophyll. The best known are P-carotene and lycopene but others are also used as food colorants a-carotene, y-carotene, bixin, norbixin, capsanthin, lycopene, and P-apo-8 -carotenal, the ethyl ester of P-apo-8-carotenic acid. These are Upid-soluble compounds, but the chemical industry manufactures water-dispersible preparations by formulating coUoid suspensions by emulsifying the carotenoids or by dispersing them in appropriate colloids. ... [Pg.52]

Herein we briefly mention historical aspects on preparation of monometallic or bimetallic nanoparticles as science. In 1857, Faraday prepared dispersion solution of Au colloids by chemical reduction of aqueous solution of Au(III) ions with phosphorous [6]. One hundred and thirty-one years later, in 1988, Thomas confirmed that the colloids were composed of Au nanoparticles with 3-30 nm in particle size by means of electron microscope [7]. In 1941, Rampino and Nord prepared colloidal dispersion of Pd by reduction with hydrogen, protected the colloids by addition of synthetic pol5mer like polyvinylalcohol, applied to the catalysts for the first time [8-10]. In 1951, Turkevich et al. [11] reported an important paper on preparation method of Au nanoparticles. They prepared aqueous dispersions of Au nanoparticles by reducing Au(III) with phosphorous or carbon monoxide (CO), and characterized the nanoparticles by electron microscopy. They also prepared Au nanoparticles with quite narrow... [Pg.49]

Reduction of two different precious metal ions by refluxing in ethanol/water in the presence of PVP gave a colloidal dispersion of core/shell structured bimetallic nanoparticles. In the case of Pd and Au ions, e.g., the colloidal dispersions of bimetallic nanoparticles with a Au core/Pd shell structure are produced. In contrast, it is difficult to prepare bimetallic nanoparticles with the inverted core/shell (in this case, Pd-core/Au-shell) structure. The sacrificial hydrogen strategy was used to construct the inverted core/shell structure, where the colloidal dispersions of Pd-cores are treated with hydrogen and then the solution of the second element, Au ions, is slowly added to the dispersions. This novel method, developed by us, gave the inverted core/shell structured bimetallic nanoparticles. The Pd-core/Au-shell structure was confirmed by FT-IR spectra of adsorbed CO [144]. [Pg.56]

Principally purification and characterization methods of monometallic nanoparticles are directly applied to those of bimetallic nanoparticles. Purification of metal nanoparticles dispersed in solution is not so easy. So, in classical colloid chemistry, contamination is carefully avoided. For example, people used pure water, distilled three times, and glass vessels, cleaned by steam, for preparation of colloidal dispersions. In addition, the reagents which could not byproduce contaminates were used for the preparation. Recently, however, various kinds of reagents were used for the reaction and protection. Thus, the special purification is often required especially when the nanoparticles are prepared by chemical methods. [Pg.58]

After our success in preparation of the colloidal dispersions of Pt-core/Pd-shell bimetallic nanoparticles by simultaneous reduction of PdCl2 and H2PtCl6 in refluxing ethanol/water in the presence of poly(V-vinyl-2-pyrroli-done) [15,16] several reports have appeared on the formation of the core/shell-structured bimetallic nanoparticles by simultaneous reactions [5,52,68,183]. [Pg.65]

Monitoring the pH value during the preparation of gold sol, which leads to the below reported results, it has been observed that pH moves from ca. 3.2, before NaBH4 addition, to ca. 6.9, after NaBH4 addition. In this section a discussion of the influence of the initial pH value on the properties of the colloidal dispersion stabilized by a large amount (PVA/Au = 0.67) or a low amount (PVA/ Au = 0.05) of stabilizer is presented. Proper amounts of HCl or NaOH were used to produce the reported pH values. [Pg.256]

Partially hydrolyzed polyacrylamides, carboxymethylcellulose, polysaccharides, and acrylamido methylpropane sulfonate have been screened to investigate the performance of aluminum citrate as a chelate-type crosslinker. An overview of the performance of 18 different polymers has been presented in the literature [1646]. The performance of the colloidal dispersion gels depends strongly on the type and the quality of the polymer used. The gels were mixed with the polymers at two polymer concentrations, at three polymer-to-aluminum ratios, and in different concentrations of potassium chloride. The gels were quantitatively tested 1,7, 14, and 28 days after preparation. [Pg.116]

The structures of four of the synthetic carotenoids (beta-carotene, canthaxanthin, beta-apo-8 -carotenol, beta-apo-8 -carotenoic acid) are shown in Fig. 8.2. By virtue of their conjugated double bond structure, they are susceptible to oxidation but formulations with antioxidants were developed to minimize oxidation. Carotenoids are classified as oil soluble but most foods require water soluble colorants thus three approaches were used to provide water dispersible preparations. These included formulation of colloidal suspensions, emulsification of oily solutions, and dispersion in suitable colloids. The Hoffman-LaRoche firm pioneered the development of synthetic carotenoid colorants and they obviously chose candidates with better technological properties. For example, the red canthaxanthin is similar in color to lycopene but much more stable. Carotenoid colorants are appropriate for a wide variety of foods.10 Regulations differ in other countries but the only synthetic carotenoids allowed in foods in the US are beta-carotene, canthaxanthin, and beta-8-carotenol. [Pg.186]

Characteristic microstructural properties of TiOj membranes produced in this way are given in Table 2.5. Mean pore diameters of 4-5 nm were obtained after heat treatment at T < 500°C. The pore size distribution was narrow in this case and the particle size in the membrane layer was about 5 nm. Anderson et al. (1988) discuss sol/gel chemistry and the formation of nonsupported titania membranes using the colloidal suspension synthesis of the type mentioned above. The particle size in the colloidal dispersion increased with the H/Ti ratio from 80 nm (H /Ti = 0.4, minimum gelling volume) to 140 nm (H /Ti " — 1.0). The membranes, thus prepared, had microstructural characteristics similar to those reported in Table 2.5 and are composed mainly of 20 nm anatase particles. Considerable problems were encountered in membrane synthesis with the polymeric gel route. Anderson et al. (1988) report that clear polymeric sols without precipitates could be produced using initial water concentrations up to 16 mole per mole Ti. Transparent gels could be obtained only when the molar ratio of H2O to Ti is < 4. Gels with up to 12 wt.% T1O2 could be produced provided a low pH is used (H /Ti + < 0.025). [Pg.36]

Trigonal crystalline solid or amorphous powder mineral millerite has a yellow metallic luster color varies from yellow to brownish black density 5.30 to 6.65 g/cm3 exhibits three allotropic modifications (1) the acid-soluble amorphous alpha form obtained from nickel salt solution by precipitation with ammonium sulfide, (2) the alpha form rapidly transforms to a crystalline beta form as a brown colloidal dispersion upon exposure to air, and (3) a rhombo-hedral gamma modification found native as mineral millerite, which also can be prepared artificially under certain conditions. [Pg.624]

When preparing lipid nano- and microparticles from solid, crystalline raw materials, it is usually expected that the lipid matrix of the particles is or will become solid after the dispersion step. It has, however, turned out that some matrix materials do not crystallize easily in the colloidally dispersed state after processing in the heat ) 2005 by CRC Press LLC... [Pg.7]

Colloidal dispersions of fine metal particles can usually be prepared by reduction of metal ions. The first scientific report to synthesize colloidal dispersion of metals was presented by Faraday, who prepared metal colloids without stabilizers (5). In his case counteranions may have played the role of the stabilizer. In most recent cases, however, stabilizers are usually added to the system to stabilize the colloidal dispersions. [Pg.430]

Faraday prepared a colloidal dispersion of gold fine particles by reduction of gold(lll) ions with white phosphorus. Recently, Turkevich prepared the gold sol by reduction... [Pg.430]


See other pages where Colloidal dispersions preparation is mentioned: [Pg.431]    [Pg.1275]    [Pg.54]    [Pg.55]    [Pg.57]    [Pg.59]    [Pg.61]    [Pg.279]    [Pg.431]    [Pg.1275]    [Pg.54]    [Pg.55]    [Pg.57]    [Pg.59]    [Pg.61]    [Pg.279]    [Pg.150]    [Pg.52]    [Pg.49]    [Pg.243]    [Pg.258]    [Pg.296]    [Pg.11]    [Pg.51]    [Pg.259]    [Pg.278]    [Pg.154]    [Pg.247]    [Pg.928]    [Pg.141]    [Pg.6]    [Pg.444]    [Pg.254]    [Pg.49]    [Pg.15]    [Pg.253]   
See also in sourсe #XX -- [ Pg.10 , Pg.11 , Pg.12 , Pg.13 , Pg.16 , Pg.17 , Pg.18 , Pg.19 ]