Cobalt-based alloys, localized corrosion potentiodynamic polarization

G61-86, Conducting cyclic potentiodynamic polarization measurements for localized corrosion susceptibility of iron-, nickel-, or cobalt-based alloys, Annual Book of ASTM Standards, ASTM International, Philadelphia, Pa., 2000, p. 240, Vol. 3.02. [Pg.721]

ASTM G 61-86, Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements for Localized Corrosion Susceptibility of Iron-, Nickel-, or Cobalt-Based Alloys, ASTM International, West Conshohocken, PA, 2003. [Pg.321]

Nickel-base alloys respond well to most electrochemical test techniques and show active-passive behavior in many environments. Due to their rapid repassivation, however, the results obtained with potentiod3mamic techniques can sometimes be affected by scan rate and immersion time prior to starting the test [5,6], Electrochemical techniques are useful for investigating localized corrosion resistance, ASTM G 61, Test Method for Conducting Cyclic Potentio-dynamic Polarization Measurements for Localized Corrosion Susceptibility of Iron-, Nickel-, or Cobalt-Based Alloys, and general corrosion resistance, ASTM G 59, Practice for Conducting Potentiodynamic Polarization Resistance Measurements of nickel alloys. Electrochemical impedance measurement techniques have not been extensively applied to nickel alloys. [Pg.584]

Electrochemical tests provide a means to understand the corrosion process, simulate service conditions, or accelerate evaluation of a material [27]. ASTM G 3, Practice for Conventions Applicable to Electrochemical Measurements in Corrosion Testing ASTM G 5, Standard Reference Test Method for Making Potentiostatic and Potentiodynamic Polarization Measurements and ASTM G 61, Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements for Localized Corrosion Susceptibility of Iron-, Nickel-, or Cobalt-Based Alloys provide background in some of these techniques. [Pg.776]

Cyclic potentiodynamic polarization for localized corrosion susceptibility of iron-, nickel-, or cobalt-base alloys G61... [Pg.253]