Small amounts of yttrium (0.1 to 0.2%) can be used to reduce the grain size in chromium, molybdenum, zirconium, and titanium, and to increase strength of aluminum and magnesium alloys. 

Common alloying elements include nickel to improve low temperature mechanical properties chromium, molybdenum, and vanadium to improve elevated-temperature properties and silicon to improve properties at ordinary temperatures. Low alloy steels ate not used where corrosion is a prime factor and are usually considered separately from stainless steels. 

Chromium is the most effective addition to improve the resistance of steels to corrosion and oxidation at elevated temperatures, and the chromium—molybdenum steels are an important class of alloys for use in steam (qv) power plants, petroleum (qv) refineries, and chemical-process equipment. The chromium content in these steels varies from 0.5 to 10%. As a group, the low carbon chromium—molybdenum steels have similar creep—mpture strengths, regardless of the chromium content, but corrosion and oxidation resistance increase progressively with chromium content. 

Carbon content is usually about 0.15% but may be higher in bolting steels and hot-work die steels. Molybdenum content is usually between 0.5 and 1.5% it increases creep—mpture strength and prevents temper embrittlement at the higher chromium contents. In the modified steels, siUcon is added to improve oxidation resistance, titanium and vanadium to stabilize the carbides to higher temperatures, and nickel to reduce notch sensitivity. Most of the chromium—molybdenum steels are used in the aimealed or in the normalized and tempered condition some of the modified grades have better properties in the quench and tempered condition. 

Another anomalous property of some nickel—iron aHoys, which are caHed constant-modulus aHoys, is a positive thermoelastic coefficient which occurs in aHoys having 27—43 wt % nickel. The elastic moduH in these aHoys increase with temperature. UsuaHy, and with additions of chromium, molybdenum, titanium, or aluminum, the constant-modulus aHoys are used in precision weighing machines, measuring devices, and osciHating mechanisms (see Weighing AND proportioning). 

Vitahium FHS ahoy is a cobalt—chromium—molybdenum ahoy having a high modulus of elasticity. This ahoy is also a preferred material. When combiaed with a properly designed stem, the properties of this ahoy provide protection for the cement mantle by decreasing proximal cement stress. This ahoy also exhibits high yields and tensile strength, is corrosion resistant, and biocompatible. Composites used ia orthopedics include carbon—carbon, carbon—epoxy, hydroxyapatite, ceramics, etc. 

Alloying elements such as nickel, chromium, molybdenum, and copper, which may be introduced with scrap, can increase the hardenability, although only slightly, because the concentrations are ordinarily low. However, the heat-treating characteristics may change, and for appHcations in which ductihty is important, as in low carbon steels for deep drawing, the increased hardness and lower ductiHty imparted by these elements may be harmful. 

Materials of Construction. Resistance of alloys to concentrated sulfuric acid corrosion iacreases with increasing chromium, molybdenum, copper, and siUcon content. The corrosiveness of sulfuric acid solutions is highly dependent on concentration, temperature, acid velocity, and acid impurities. An excellent summary is available (114). Good general discussions of materials of constmction used ia modem sulfuric acid plants may be found ia References 115 and 116. More detailed discussions are also available (117—121). For nickel-containing alloys Reference 122 is appropriate. An excellent compilation of the relatively scarce Hterature data on corrosion of alloys ia Hquid sulfur trioxide and oleum may be found ia Reference 122. 

The neutral complexes of chromium, molybdenum, tungsten, and vanadium are six-coordinate and the CO molecules are arranged about the metal in an octahedral configuration as shown in stmcture (3). Vanadium carbonyl possesses an unpaired electron and would be expected to form a metal—metal bond. Steric hindrance may prevent dimerization. The other hexacarbonyls are diamagnetic. 

C. L. RoUinson, The Chemistry of Chromium, Molybdenum, andTungsten, Vol. 21, Pergamon Press, Oxford, UK, 1975. 

Complexes (191) and (192) are formed from dimethyldiazirine with carbonyls of chromium, molybdenum and tungsten. They show no tendency towards N—N cleavage (80JOM(193)57). Complex (193) is made from a mixed complex by displacement of norbor-nadiene. 

For medium- to high-impact applications a wide range of low-alloy steels are produced containing some chromium, molybdenum, phosphorus, and silicon. Economy of manufacture is a benefit for selec tion of these steels. 

Above temperatures of 900°F, the austenitic stainless steel and other high alloy materials demonstrate inereas-ingly superior creep and stress-rupture properties over the chromium-molybdenum steels. For furnace hangers, tube supports, and other hardware exposed to firebox temperatures, cast alloys of 25 Cr-20 Ni and 25 Cr-12 Ni are frequently used. These materials are also generally needed because of their resistanee to oxidation and other high temperature corrodents. 

Furnace tubes, piping, and exchanger tubing with metal temperatures above 800°F now tend to be an austenitic stainless steel, e.g., Type 304, 321, and 347, although the chromium-molybdenum steels are still used extensively. The stainless steels are favored beeause not only are their creep and stress-rupture properties superior at temperatures over 900°F, but more importantly because of their vastly superior resistance to high-temperature sulfide corrosion and oxidation. Where corrosion is not a significant factor, e.g., steam generation, the low alloys, and in some applications, carbon steel may be used. 

Dimethylberyllium Chromium Molybdenum (IV) Trichloro(vinyl)silane... 

Low-carbon, low-alloy steels are in widespread use for fabrication-welded and forged-pressure vessels. The carbon content of these steels is usually below 0.2%, and the alloying elements that do not exceed 12% are nickel, chromium, molybdenum, vanadium, boron and copper. The principal applications of these steels are given in Table 3.8. 

Many metals are naturally brittle at room temperature, so must be machined when hot. However, particles of these metals, such as tungsten, chromium, molybdenum, etc., can be suspended in a ductile matrix. The resulting composite material is ductile, yet has the elevated-temperature properties of the brittle constituents. The actual process used to suspend the brittle particles is called liquid sintering and involves infiltration of the matrix material around the brittle particles. Fortunately, In the liquid sintering process, the brittle particles become rounded and therefore naturally more ductile. 

Table 23.2 Oxidation states and stereochemistries of compounds of chromium, molybdenum and tungsten...

---