Biaxial-oriented polypropylene substrate

Patel et al. [70] in a recent publication have explored the adhesive action of the mbber-siUca hybrid nanocomposites on different substrates. The rubber-silica hybrid nanocomposites are synthesized through in situ silica formation from TEOS in strong acidic pH within acryhc copolymer (EA-BA) and terpolymer (EA-BA-AA) matrices. The transparent nanocomposites have been apphed in between the aluminum (Al), wood (W), and biaxially oriented polypropylene (PP) sheets separately and have been tested for peel strength, lap shear strength, and static holding power of the adhesive joints. 

Materials. Biaxially oriented polypropylene (PP) films of 50 um thickness were obtained from 3M and have been described (2). PMDA-ODA (PI) was Kapton H polyimide from Dupont. Copper-plated PTFE films were obtained from Spire Corporation (Bedford, MA). They were prepared using the Ion Beam Enhanced Deposition (IBED) process in which a 100 nm thick Cu film was vapor-deposited onto a PTFE substrate in the presence of a beam of 400 eV Ar+ ions of 25 uA/cm2 (IQ). Shortly before SIMS analysis, the Cu film was removed slowly by peeling at 90° in ambient conditions. Metal-coated PI films were prepared by sputtering 50 nm Cr and 1 um Cu onto a 50 um thick Kapton film on both sides. Thermal annealing was performed in a vacuum chamber at 2xl0 6 torr using a quartz lamp as the heating source. The samples were held for 15 min at the desired temperature and then cooled down to ambient temperature inside the chamber for about 2 hours. Just prior to SIMS analysis, the metal films were peeled slowly at 90° and then immediately introduced into the vacuum chamber of the instrument. 

---